Concrete slump retaining agent to which methylcellulose is added and preparation method thereof

A technology of methyl cellulose and concrete, which is applied in the field of concrete slump-retaining agent added with methyl cellulose and its preparation, which can solve the problems of excessive slump loss of high-efficiency water-reducing agent, etc., and achieve obvious slump-retaining effect 、To overcome the effect of too large and too fast slump loss

Inactive Publication Date: 2015-12-09
徐明
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a concrete slump-retaining agent added with methyl cellulose and its preparation method. Adding the slump-retaining agent in the process of concrete construction can overcome the shor...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A concrete slump-retaining agent added with methyl cellulose, the components and the mass parts of each component are as follows: 1 part of methyl cellulose, 6 parts of polyacrylamide, 2 parts of calcium formate, 1.0 part of sucrose, itaconic acid 4 parts, 0.5 parts of methallyl polyoxyethylene ether, 8 parts of monoethanolamine, 3 parts of formic acid, 0.5 parts of phosphoric acid, 5 parts of sodium methacrylate, 3 parts of sodium styrene sulfonate, 0.1 parts of p-toluenesulfonic acid 4.7 parts of methacrylic acid, 1.0 parts of sodium gluconate, 5 parts of sodium hydroxide, and 15 parts of water.

[0020] The preparation method comprises the steps of:

[0021] 1) Mix monoethanolamine with formic acid and phosphoric acid and add itaconic acid into the reaction kettle. Under the protection of nitrogen, heat up to 70°C at a heating rate of 0.5°C / min. Add methyl cellulose and continue to heat up to 100°C. The rate is 0.5°C / min, the constant temperature reaction is 1h, and...

Embodiment 2

[0026] A concrete slump-retaining agent added with methyl cellulose, the components and the mass parts of each component are as follows: 6 parts of methyl cellulose, 10 parts of polyacrylamide, 6 parts of calcium formate, 3.2 parts of sucrose, itaconic acid 8 parts, 1.5 parts of methallyl polyoxyethylene ether, 20 parts of monoethanolamine, 7 parts of formic acid, 1.5 parts of phosphoric acid, 12 parts of sodium methacrylate, 8 parts of sodium styrene sulfonate, 0.5 parts of p-toluenesulfonic acid 9.5 parts of methacrylic acid, 2.2 parts of sodium gluconate, 15 parts of sodium hydroxide, and 20 parts of water.

[0027] The preparation method comprises the steps of:

[0028] 1) Mix monoethanolamine with formic acid and phosphoric acid and add itaconic acid into the reaction kettle. Under the protection of nitrogen, heat up to 90°C with a heating rate of 2°C / min. Add methyl cellulose and continue to heat up to 120°C. The rate was 2°C / min, the constant temperature was reacted fo...

Embodiment 3

[0033] A concrete slump-retaining agent added with methyl cellulose, the components and the mass parts of each component are as follows: 4.2 parts of methyl cellulose, 8.3 parts of polyacrylamide, 4.3 parts of calcium formate, 2.3 parts of sucrose, and itaconic acid 6.5 parts, 1.1 parts of methallyl polyoxyethylene ether, 14 parts of monoethanolamine, 4.7 parts of formic acid, 1.1 parts of phosphoric acid, 8.1 parts of sodium methacrylate, 5.2 parts of sodium styrene sulfonate, 0.3 parts of p-toluenesulfonic acid 7.1 parts of methacrylic acid, 1.6 parts of sodium gluconate, 10 parts of sodium hydroxide, and 17 parts of water.

[0034] The preparation method comprises the steps of:

[0035] 1) Mix monoethanolamine with formic acid and phosphoric acid and add itaconic acid into the reaction kettle. Under the protection of nitrogen, heat up to 80°C with a heating rate of 1°C / min. Add methyl cellulose and continue to heat up to 110°C. The rate was 1°C / min, the constant temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a concrete slump retaining agent to which methylcellulose is added and a preparation method thereof. The concrete slump retaining agent is prepared from, by mass, 1-6 parts of methylcellulose, 6-10 parts of polyacrylamide, 2-6 parts of calcium formate, 1.0-3.2 parts of saccharose, 4-8 parts of itaconic acid, 0.5-1.5 parts of methyl allyl polyethenoxy ether, 8-20 parts of monoethanolamine, 3-7 parts of formic acid, 0.5-1.5 parts of phosphoric acid, 5-12 parts of sodium methallyl sulfonate, 3-8 parts of sodium p-styrenesulfonate, 0.1-0.5 part of p-toluenesulfonic acid, 4.7-9.5 parts of methacrylic acid, 1.0-2.2 parts of gluconic acid sodium salt, 5-15 parts of sodium hydroxide and 15-20 parts of water.

Description

technical field [0001] The invention belongs to the technical field of concrete admixtures, and in particular relates to a concrete slump-retaining agent added with methyl cellulose and a preparation method thereof. Background technique [0002] With the vigorous development of the commercial concrete industry for construction, concrete admixtures in my country have been widely used in recent years, among which the Cai series sulfonate formaldehyde condensate type high-efficiency water reducer, melamine sulfonate formaldehyde condensate type high-efficiency water reducer Water agent, lignosulfonate water reducer, sugar calcium water reducer, etc. are used in large amounts. These superplasticizers endow fresh concrete with good fluidity and strength, which can basically meet the construction needs for on-site mixing. But for commercial concrete, there is a common problem of excessive slump loss. At present, there are many ways to solve the slump loss of concrete, and the fol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/38
Inventor 徐明
Owner 徐明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap