In-glaze relief base material, in-glaze decal paper made with it and its manufacturing process

An in-glaze color and relief technology, which is applied in the crafts and decorative arts for producing decorative surface effects, can solve the problems of low resistance to mechanical wear and corrosion, can not achieve energy saving and consumption reduction, and is not suitable for other glazes. , to improve the mechanical wear resistance and corrosion resistance of enamel, good three-dimensional effect, and simplify the printing process.

Active Publication Date: 2019-03-29
福建省德化铭丰金花纸有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the in-glaze ceramics made by this method are exquisite and clear, have a strong sense of space and high collection value, this process is not suitable for other glazes, and the firing temperature and color range of in-glaze relief products are limited, and they are resistant to mechanical wear. And low corrosion resistance, and the process is complicated, it needs to be fired many times, the firing time is long, and the effect of energy saving and consumption reduction cannot be achieved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • In-glaze relief base material, in-glaze decal paper made with it and its manufacturing process
  • In-glaze relief base material, in-glaze decal paper made with it and its manufacturing process
  • In-glaze relief base material, in-glaze decal paper made with it and its manufacturing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The in-glaze relief base material includes the following components in parts by mass: 47 parts of bone soil, 1 part of alumina, 15 parts of quartz powder, 8 parts of feldspar powder, and 17 parts of frit for high-temperature glaze; The high-temperature glaze frit is a transparent frit produced by Johnson Matthey, which is characterized by high transparency and good leveling.

[0031] The method for making in-glaze colored flower paper with the in-glaze relief base material comprises the following steps:

[0032] Step 1: Preparation of in-glaze relief base material:

[0033] a. Calcination: according to the mass ratio, mix the components of the in-glaze relief bottom material evenly, put them in a high-temperature resistant container made of quartz sand, and put them in a kiln for calcination at 1100°C. The calcination time After 12 hours, after natural cooling, the mixture was obtained;

[0034] b. ball milling: after mixing the mixture described in step 1a and dehydr...

Embodiment 2

[0048] The in-glaze relief base material includes the following components in parts by mass: 50 parts of bone soil, 3 parts of alumina, 17 parts of quartz powder, 10 parts of feldspar powder, and 20 parts of frit for high-temperature glaze; The frit for high-temperature glaze is a transparent frit produced by Johnson Matthey in the United Kingdom. It is characterized by high transparency and good leveling, and is usually suitable for raw materials for medium-temperature and bone china glazes.

[0049] The method for making in-glaze colored flower paper with the in-glaze relief base material comprises the following steps:

[0050] Step 1: Preparation of in-glaze relief base material:

[0051] a. Calcination: According to the mass ratio, mix the components of the in-glaze relief bottom material evenly, put them in a high-temperature resistant container made of quartz sand, and put them in a kiln for calcination at 1125°C. The calcination time After 13 hours, after natural cooli...

Embodiment 3

[0066] The in-glaze relief base material includes the following components in parts by mass: 52 parts of bone soil, 5 parts of alumina, 19 parts of quartz powder, 11 parts of feldspar powder, and 25 parts of frit for high-temperature glaze; The frit for high-temperature glaze is a transparent frit produced by Johnson Matthey in the United Kingdom. It is characterized by high transparency and good leveling, and is usually suitable for raw materials for medium-temperature and bone china glazes.

[0067] The method for making in-glaze colored flower paper with the in-glaze relief base material comprises the following steps:

[0068] Step 1: Preparation of in-glaze relief base material:

[0069] a. Calcination: according to the mass ratio, mix the components of the in-glaze relief base material evenly and put them into a high-temperature resistant container made of quartz sand, put them in a kiln and calcinate at 1150°C, and the calcining time After 14 hours, after natural coolin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an in-glaze decoration embossment base material, in-glaze decoration stain paper manufactured through the in-glaze decoration embossment base material and a manufacturing technology of the in-glaze decoration embossment base material, and belongs to the technical field of in-glaze decoration stained paper. According to the in-glaze decoration embossment base material, the in-glaze decoration stained paper manufactured through the in-glaze decoration embossment base material and the manufacturing technology of the in-glaze decoration embossment base material, the in-glaze decoration embossment base material is manufactured through the four steps of calcination, ball-milling, drying and pulverizing. The method for manufacturing the in-glaze decoration stained paper through the in-glaze decoration embossment base material includes the four steps of ink grinding, printing, color printing and sealing compound. The method is suitable for different glaze and firing temperatures, the color modulation range of the in-glaze decoration embossment product is widened, the product corrosion resistance and abrasion resistance are improved, zero heavy metal dissolving is achieved, and pigment solubility is high. The three-dimensional effect is good, and brightness is high. The printing technological process is simplified, and the product is high in yield, flawless and more attractive; moreover, the lead and cadmium dissolving-out amount can reach the Europe and America national standard.

Description

technical field [0001] The invention belongs to the technical field of in-glaze relief printing technology, and in particular relates to a manufacturing process of in-glaze decal paper. Background technique [0002] With the improvement of people's quality of life and the transformation of consumption concepts, the requirements for the artistry and appreciation of ceramic products are getting higher and higher. In order to improve the artistry of ceramic products, it is often necessary to use a variety of surface decoration methods, such as in-glaze colored paper (also known as high-temperature fast-fired flower paper), another ceramic decorative printing process extended on the basis of over-glaze color decoration technology Technology, replacing the traditional handicraft painting technology. [0003] Since ceramic pigment manufacturers currently provide few types of relief materials, that is, transparent and milky white relief materials are not enough to meet the color r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00C04B41/86B44C1/165
Inventor 吕素妹沙轩林巧玲连志斌
Owner 福建省德化铭丰金花纸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap