Rare earth ion doped GdI3 glass ceramic and preparation method thereof
A technology of glass-ceramics and rare earth ions, which is applied in the field of rare-earth ion-doped GdI3 glass-ceramics and its preparation, can solve the problems of poor chemical stability and mechanical strength, low phonon energy, and easy water absorption of crystals, and achieve mechanical Good performance, low phonon energy, and high up-conversion efficiency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0019] Example 1
[0020] Er 3+ , Yb 3+ Doped GdI 3 The mole percentage composition of glass-ceramics is: SiO 2 75mol%, GdI 3 20mol%, ErI 3 0.5mol%, YbI 3 4.5mol%, the process for preparing glass ceramics with the above composition is as follows:
[0021] (1) Weigh gadolinium acetate, erbium acetate and ytterbium acetate, and the weights are respectively based on the GdI in the above molar percentage composition 3 , ErI 3 , YbI 3 Weigh the molar percentage of acetic acid, dissolve the above-mentioned acetate in deionized water to form an acetate solution, add triiodoacetic acid to the acetate solution to obtain a transparent mixed solution, wherein the triiodoacetic acid and the acetate solution The molar ratio of the total metal ions is 3:1;
[0022] (2) According to the same mole percentage as step (1), SiO 2 Weigh the ethyl orthosilicate and dissolve it in ethanol to obtain the ethyl orthosilicate solution, then mix the mixed solution prepared in step (1) with the ethyl orthosilic...
Example Embodiment
[0026] Example 2
[0027] Tm 3+ , Yb 3+ Doped GdI 3 The mole percentage composition of glass-ceramics is: SiO 2 80.5mol%, GdI 3 15mol%, TmI 3 0.5mol%, YbI 3 4mol%, after the same preparation and heat treatment process as in Example 1, a transparent rare earth ion Tm is obtained 3+ , Yb 3+ Doped GdI 3 Glass-ceramic. The glass-ceramics were measured with a TRIAX550 fluorescence spectrometer, and under the excitation condition of a 970nm laser, strong blue upconversion luminescence was observed.
Example Embodiment
[0028] Example 3
[0029] Er 3+ , Tm 3+ , Yb 3+ Doped GdI 3 The mole percentage composition of glass-ceramics is: SiO 2 81mol%, GdI 3 14mol%, ErI 3 0.4mol%, TmI 3 0.2mol%, YbI 3 4.4mol%, after the same preparation and heat treatment process as in Example 1, a transparent rare earth ion Er 3+ , Tm 3+ , Yb 3+ Doped GdI 3 Glass-ceramic. The glass-ceramics were measured with a TRIAX550 fluorescence spectrometer, and under the excitation condition of a 970nm laser, strong blue, green and red upconversion luminescence was observed.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap