Staining fluid for zirconia pre-burned false tooth

A technology of zirconia and dyeing liquid, which is applied in the field of dyeing liquid, can solve the problems of high cost, complex composition, and long dyeing time, and achieve the effect of low cost, uniform overall color, and short dyeing time

Active Publication Date: 2016-02-03
QINHUANGDAO ZEKENI CERAMIC TECH CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although there are many kinds of dyeing solutions for zirconia pre-fired dentures used in the market, the defects of long dyeing time, complex components and high cost are common, and the existing Vita16 color dyeing solutions cannot meet the daily requirements. In view of the demand for production, it is necessary to invent a dyeing solution for all-ceramic dentures with short dyeing time, low cost and good dyeing effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of dyeing solution for zirconia calcined denture, it is made up of the raw material of following weight part:

[0020] Deionized water 1000g;

[0021] Erbium nitrate colorant 16g;

[0022] Praseodymium nitrate colorant 3.2g;

[0023] Ferric chloride coloring agent 8.1g.

[0024] The deployment method is as follows:

[0025] Put the 500ml capacity glass beaker on the electronic balance, reset the electronic balance, add the above-mentioned colorants in turn according to the formula, use a measuring cylinder to measure 500ml of distilled water into the beaker, and then fully stir until all the colorants are completely melted. .

[0026] Soak the zirconia pre-fired denture in the above-mentioned A1 staining solution for 10 seconds, dry the denture with an infrared lamp for 10 minutes, and sinter it at 1480°C-1530°C for 5 hours to obtain a colored dental restoration. The zirconia shows the color of A1 .

Embodiment 2

[0028] A kind of dyeing solution for zirconia calcined denture, it is made up of the raw material of following weight part:

[0029] Deionized water 1000g;

[0030] Erbium nitrate colorant 23.1g;

[0031] Praseodymium nitrate colorant 4.9g;

[0032] Ferric chloride coloring agent 10.7g.

[0033] The deployment method is as follows:

[0034] Put the 500ml capacity glass beaker on the electronic balance, reset the electronic balance, add the above-mentioned colorants in turn according to the formula, use a measuring cylinder to measure 500ml of distilled water into the beaker, and then fully stir until all the colorants are completely melted. .

[0035] Soak the zirconia pre-fired denture in the above-mentioned A2 staining solution for 10 seconds, dry it, and sinter it at 1480-1530° C. for 5 hours to obtain a colored dental restoration. The zirconia shows the A2 color.

Embodiment 3

[0037] A kind of dyeing solution for zirconia calcined denture, it is made up of the raw material of following weight part:

[0038] Deionized water 1000g;

[0039] Erbium nitrate coloring agent 2.7g;

[0040] Praseodymium nitrate colorant 22.8g;

[0041] Ferric chloride coloring agent 16.5g.

[0042] The deployment method is as follows:

[0043] Put the 500ml capacity glass beaker on the electronic balance, reset the electronic balance, add the above-mentioned colorants in turn according to the formula, use a measuring cylinder to measure 500ml of distilled water into the beaker, and then fully stir until all the colorants are completely melted. .

[0044] Soak the zirconia pre-fired denture in the above staining solution for 10 seconds, dry it, and sinter it at 1500° C. for 5 hours to obtain a colored dental restoration. The zirconia shows an A3 color.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to staining fluid for a zirconia pre-burned false tooth. The staining fluid consists of the following raw materials in parts by weight: 1000 parts of deionized water, 9.6 to 57 parts of iron chloride, 4.2 to 46.2 parts of erbium nitrate and 0.6 to 24 parts of praseodymium nitrate. The staining fluid has excellent permeation rate, the staining fluid can permeate for 0.8mm in 5 seconds in a single direction, for 1.2mm in 10 seconds in a single direction and for 1.5mm in 20 seconds in a single direction, the permeation speed is high, the stained pre-burned false tooth is integrally uniform in color; moreover, the light transmittance is similar to that of a natural color. Besides, the satisfaction on the requirement of vita 16 colors, four effect colors of A5, B5, C5 and G1 (gingival porcelain color) can also be achieved by the staining color, the production demand of a technician is satisfied, and the blank of the effect color in the industry can be filled. The staining fluid has the characteristics of short time, good staining effect and low cost, and is capable of completing the staining in ten seconds and suitable for the production of false tooth companies.

Description

technical field [0001] The invention relates to a dyeing solution, in particular to a dyeing solution for all-ceramic dentures, especially zirconia pre-fired dentures. Background technique [0002] Currently, in prosthodontics, color and light transmission are an important indicator affecting the objectivity of restorations and teeth. The use of dental CAD / CAM technology to make all-ceramic restorations has opened up a new way for the automatic processing of restorations and the production of high-strength all-ceramic crowns and bridges. The color of uncolored zirconia pre-fired dentures is mostly white to ivory. Although it can simulate the color of natural teeth to a certain extent, it cannot meet the clinical requirements for the color of restorations. Only by coloring zirconia and adjusting the color and light transmittance of zirconia to be close to the color and light transmittance of the tooth to be restored can the needs of customers be met. At present, the colorin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/85
Inventor 陈志杰
Owner QINHUANGDAO ZEKENI CERAMIC TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com