Synthesis method for zeolite-coated precious metal particles and application of zelite-coated precious metal particles in light paraffin isomerization

A precious metal and coating technology, used in molecular sieve catalysts, petroleum industry, refined hydrocarbon oil, etc., can solve the problems of inability to enter molecular sieve pores, bulk hydroxides, etc., to improve hydrogenation-dehydrogenation performance and improve metal dispersion. degree, the effect of reducing the load

Active Publication Date: 2016-03-23
CHINA UNIV OF PETROLEUM (BEIJING)
View PDF9 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, if the hydrothermal synthesis method is used, large hydroxides are prone to appear and cannot enter the pores of the molecular sieve.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthesis method for zeolite-coated precious metal particles and application of zelite-coated precious metal particles in light paraffin isomerization

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The synthesis of the Beta zeolite of the BEA structure of embodiment 1 containing Pt or Pd

[0031] First, 0.75g NaOH and 2.3g TEAOH were mixed with 11.7g water and stirred vigorously to produce a clear solution. Then add 0.27g of NaAlO 2 into solution and vigorously stirred to produce clear Solution A.

[0032] 0.025g of [Pt(NH 3 ) 4 ]Cl 2 Solution B was obtained by adding 5 mL of water. Solutions A and B were mixed and stirred vigorously, then 5.0g of white carbon black was added and stirred vigorously for 2h to obtain a uniform gel. The molar ratio composition of the resulting gel is SiO 2 :0.014Al 2 o 3 :0.125Na 2 O: 0.060TEAOH: 30H 2 O.

[0033]The gel was dried at 333K in an air atmosphere to obtain a dried gel. Grind dry glue into powder for later use. Weigh 5g of dry glue fine powder, place it in the middle of a 150mL dry glue steam-assisted method (SAC) crystallization kettle, and then add 1.0mL of water to the bottom of it, and the dry glue does n...

Embodiment 2

[0044] The synthesis of the Beta zeolite molecular sieve of the BEA structure of embodiment 2 containing Pt-Pd

[0045] Take 6.00g silica, 19.88gTEAOH and 2.00gNH 4 F was mixed and stirred vigorously for 2h. Then take 0.01g and 0.1g of K 2 [PtCl 4 ] and K 2 [PdCl 4 ] was dissolved in 1.6mL deionized water to form a solution, added dropwise to the above system, and continued to stir for 2h to obtain a uniform gel. Then, the gel was dried at 333K in an air atmosphere to obtain a dry gel. Grind dry glue into powder for later use.

[0046] Weigh 2g of dry glue fine powder, place it in the middle of a SAC crystallization kettle with a volume of 150mL, and then add 1.5mL of water to the bottom, the dry glue does not directly contact with the bottom water of the kettle. At the crystallization temperature of 453K, the bottom of the kettle was converted into water vapor and crystallized for 6 hours. After the reaction, the obtained sample was washed, dried, and roasted at 823K f...

Embodiment 3

[0051] The synthesis of the mordenite of the MOR structure containing Pt or Pd in ​​the channel of embodiment 3

[0052] 1.13g NaAlO 2 and 1.32 g of NaOH were dissolved in water to produce a clear solution. Then 20.1 g of bis(triethoxysilyl)methane (BTESM) was added. After mixing for 3 hours, then add 0.04g [Pt(NH 3 ) 4 ]Cl 2 solution 4mL. Stir for 1 hour, then vigorously stir for 30 minutes to form a viscous gel, and dry it at 333K to obtain dry gel. Move the above-mentioned dry glue into the middle of a 150mL crystallization kettle, and then add 10mL of water to the bottom, so that the dry glue does not directly contact with the bottom water of the kettle. After static crystallization at 453K for 3 days, it was taken out and cooled, filtered, washed, dried at 373K and roasted at 823K for 6 hours, then introduced hydrogen, and reduced at 623K for 3 hours to obtain Pt / MOR (catalyst F).

[0053] [Pt(NH 3 ) 4 ]Cl 2 Replaced with 0.05g [Pd(NH 3 ) 4 ](NO 3 ) 2 Soluti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a synthesis method for zeolite-coated precious metal particles. The synthesis method comprises the steps that 1, a metal salt solution of platinum-containing soluble salt and/or palladium-containing soluble salt is taken to be mixed with a silicon source and/or an aluminum source, a template agent, a pH value regulating agent and water, gel is obtained through stirring, and dry gel is obtained through drying; 2, crystallization is performed by adopting a dry gel steam assisting method; 3, a product obtained through crystallization is calcined for 5-8 hours in an air atmosphere and then reduced for 2-4 hours in a hydrogen atmosphere. According to the method, by learning from the characteristics of synthesizing Silicate-1-coated precious metal through a steam assisting converting method, a precursor of solid superacid is introduced in the synthesizing process of mordenite and Beta zeolite, synthesis of a zeolite molecular sieve of which pore channels contain precious metal is successfully achieved, and the catalytic property of the catalyst in a light paraffin isomerization reaction is further improved.

Description

technical field [0001] The invention belongs to the field of catalysts, in particular to a ten-membered ring and twelve-membered ring zeolite-coated noble metal catalyst and its application in light alkane isomerization. Background technique [0002] At present, about 80% of my country's motor gasoline comes from catalytic cracking gasoline, and the content of olefins and aromatics in gasoline is high. As my country's environmental protection requirements become increasingly stringent, automotive gasoline products urgently need to achieve quality upgrades by reducing olefins and aromatics. Therefore, the proportion of alkylated, isomerized and reformed gasoline in my country's motor gasoline will increase rapidly in the future. Alkane isomerization technology, which can convert low-octane normal paraffins into high-octane isoparaffins, is one of the most economical methods to increase the octane number of gasoline. [0003] In recent years, with the development of shale ga...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J29/80C10G45/64
CPCB01J29/80C10G45/64
Inventor 吴志杰赵凯强闫会燕窦涛
Owner CHINA UNIV OF PETROLEUM (BEIJING)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap