Multifunctional bicomponent ceramic tile gum composition and use method thereof

A two-component, composite technology, applied in the field of construction and decoration construction, can solve problems such as shedding, maladaptation, hollowing, etc., and achieve the effect of consistent deformation and excellent waterproof performance

Active Publication Date: 2016-03-23
上海贝恒人居建设集团南通有限公司
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The multi-functional two-component tile adhesive of the present invention combines the functions of conventional tile adhesive and tile adhesive, wherein the dry powder component can be used as a conventional tile adhesive after being stirred with water, and there is no need to use tile adhesive; it solves the current problem There are many types of tile adhesives and tile adhesives on the market, and the mixed use of tile adhesives and tile adhesives from various manufacturers may cause problems such as maladaptation, hollowing, shelling, and falling off.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional bicomponent ceramic tile gum composition and use method thereof
  • Multifunctional bicomponent ceramic tile gum composition and use method thereof
  • Multifunctional bicomponent ceramic tile gum composition and use method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～5

[0035] Embodiments 1 to 5 relate to a multi-functional two-component ceramic tile adhesive composition, the adhesive composition is composed of a dry powder component and a liquid component, and the dry powder is The components and contents included in the components are shown in Table 1 respectively, and the components and contents included in the liquid components are shown in Table 1 respectively in weight percent of the total weight of the liquid components;

[0036] When using, include the following steps:

[0037] S1. Thoroughly stir and mix each component in the dry powder component; obtain a dry powder inorganic material;

[0038] S2. Fully stirring each component in the liquid component to obtain a liquid component material;

[0039] S3. When using, according to the water-cement ratio of 1:3 (water-cement ratio, here refers to the weight ratio of water and dry powder components, you can choose 1:2~5), add water to the dry powder components and stir evenly to make til...

Embodiment 6

[0049] Embodiment 6, performance test

[0050] Performance tests were performed on the tile adhesives and tile back adhesives prepared in the above-mentioned Examples 1-5 and Comparative Examples 1-3.

[0051] 1) Refer to JC / T547-2005 "Ceramic Wall and Floor Tile Adhesives" testing basis and judgment standards to conduct performance tests on tile adhesives, and the results are shown in Table 2:

[0052] Table 2

[0053]

[0054] 2) Spread the tile adhesive on the wall in batches. After the tile adhesive is dry, apply the corresponding tile adhesive to the back of the tile, and then paste it on the wall. Its corresponding performance is shown in Table 3:

[0055] table 3

[0056]

[0057]

[0058] Cracks appeared in 28 days through comparative examples 1, 2, and 3 samples, and a serious shedding problem occurred after one year, and the tensile bond strength was significantly lower than that of the examples. The samples of Examples 1 to 5 showed no abnormality after...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a multifunctional bicomponent ceramic tile gum composition and a use method thereof. The composition consists of a dry powder component and a liquid component, wherein the dry powder component comprises the following components in percentage by weight based on the total weight of the dry powder: 39-55% of cement, 1-5% of an organic adhesive, 39-55% of fine sand, 1-5% of an auxiliary agent, 0.1-1% of a water retention agent and 1-2% of an inhibiting agent; and the liquid component comprises the following components in percentage by weight based on the total weight of the liquid component: 40-70% of waterproof emulsion, 0.5-1% of a regulator, 28.4-59.2% of water, 0.2-0.4% of a coalescing agent and 0.1-0.2% of a defoaming agent. The composition disclosed by the invention integrates functions of conventional ceramic tile gum and ceramic tile adhesive, and the dry powder component in the composition can be used as a conventional ceramic tile adhesive after water is added and stirred, so that the ceramic tile adhesive is not needed; and the problems of probable maladjustment, hollowing, flaking, shedding and the like caused by mixed use of different types of ceramic tile gums and ceramic tile adhesives on the market at present are solved.

Description

technical field [0001] The invention relates to the field of construction and decoration construction, in particular to a multifunctional two-component ceramic tile adhesive composition and its application method. Background technique [0002] Tile back glue can effectively improve the bonding strength between the back of the brick and the bonding material, and solve the common problems of hollowing, peeling, and falling off of the wet tile in the decoration project. It is the most effective interface bonding reinforcement material at present. . [0003] Tile adhesives are mainly used to paste decorative materials such as ceramic tiles, facing tiles, and floor tiles, and are widely used in decorative decoration places such as interior and exterior walls, floors, bathrooms, and kitchens. Its main features are high bonding strength, water resistance, freeze-thaw resistance, good aging resistance and convenient construction. It is a very ideal bonding material. [0004] Howev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
Inventor 麻新闻薛东升谢旭东
Owner 上海贝恒人居建设集团南通有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com