Method for producing radiation resisting plates
A radiation protection and sheet technology, applied in sustainable waste treatment, solid waste management, climate sustainability, etc., can solve problems such as land occupation, swampy, polluted groundwater sources, etc., to achieve the effect of high value-added utilization
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0033] Example 1
[0034] Take 30 grams of Bayer process red mud (with iron oxide content of 32% by weight) dispersed in 1.0L of water, add 15mL of concentrated hydrochloric acid (mass fraction of 37%), and treat for 30 minutes; then add 2.0L of water, and add 2g of reducing agent sodium sulfite, And use 2mol / L sodium hydroxide solution to adjust the pH to about 9, then add 100 grams of mineral wool fiber, 30 grams of slaked lime, 5 grams of brucite fiber, 20 grams of clay, 10 grams of starch, continue to stir beating, and finally add sulfuric acid Aluminum 1.0g, stirred for 1 minute, filtered, molded, and dried at 180°C for 1 hour to obtain a radiation-proof insulation board with a thickness of 10 mm.
Example Embodiment
[0035] Example 2
[0036] Take 35 grams of Bayer process red mud (with iron oxide content of 32% by weight) dispersed in 1.0L of water, add 18mL of concentrated hydrochloric acid (mass fraction of 37%), and treat for 30 minutes; then add 2.0L of water and add 2g of reducing agent sodium sulfite, And adjust the pH to about 9 with 2mol / L sodium hydroxide solution, then add 100 grams of mineral wool fiber, 30 grams of slaked lime, 5 grams of gypsum whiskers, 20 grams of clay, 10 grams of starch, continue to stir and beating, and finally add polypropylene 0.5 g of amide, stirred for 1 minute, filtered, molded, and dried at 180°C for 1 hour to obtain a radiation-proof and thermal insulation board with a thickness of 10 mm.
Example Embodiment
[0037] Example 3
[0038] Take 40 grams of Bayer process red mud (iron oxide content of 40% by weight) and disperse in 1.0L of water, add 20mL of concentrated hydrochloric acid (mass fraction of 37%), and treat for 30 minutes; then add 2.0L of water and add 1.2g of reducing agent to hydrate Hydrazine (concentration 80% by weight), and adjust the pH to about 9 with 2mol / L sodium hydroxide solution, then add 100 grams of mineral wool fiber, 40 grams of slaked lime, 5 grams of wollastonite fiber, 15 grams of clay, and 10 grams Starch, stir and beat, finally add 1 g of aluminum sulfate, stir for 1 minute, filter, shape, and dry at 180°C for 1 hour to obtain a radiation-proof insulation board with a thickness of 10 mm.
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap