Waterproof self-adhesive coiled material prepared from butyl rubber and preparation method of coiled material

A technology of butyl rubber and self-adhesive membrane, which is applied in the direction of adhesives, film/sheet adhesives, non-polymer adhesive additives, etc., and can solve waterproof membrane bonding, rapid aging, product flow, etc. question

Inactive Publication Date: 2016-05-18
广州市伟能高分子材料有限公司
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Waterproof membranes are often used to paste underground waterproofing with concrete cushions, but waterproof membranes cannot be directly bonded to the main underground structure, causing the waterproof layer to be separated from the main structure, so that the ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A butyl rubber waterproof self-adhesive coiled material, comprising the following raw materials in parts by weight: 7 parts of butyl rubber; 0.5 parts of carbon black; 10 parts of polyisobutylene; 0.3 parts of petroleum resin; 2 parts of white oil; 60 parts of kaolin; 0.1 part.

[0019] The preparation method of above-mentioned butyl rubber waterproof self-adhesive roll material, comprises the following steps:

[0020] 1) Take by weighing 700g butyl rubber, 50g carbon black, 1kg polyisobutylene, 30g petroleum resin, 200g white oil, 6kg kaolin and 10g antioxidant;

[0021] 2) Put the above-mentioned raw materials in a kneader, knead them for 30 minutes at a temperature of 80° C., and extrude them on an extruder after cooling to obtain a waterproof self-adhesive layer of butyl rubber;

[0022] 3) The butyl rubber waterproof self-adhesive layer obtained in step 2) is separated and curled with a release paper to obtain a butyl rubber waterproof self-adhesive coiled materia...

Embodiment 2

[0024] A butyl rubber waterproof self-adhesive coiled material, comprising the following raw materials in parts by weight: 15 parts of butyl rubber; 5 parts of carbon black; 16 parts of polyisobutylene; 2 parts of petroleum resin; 8 parts of white oil; 80 parts of kaolin; 0.8 servings.

[0025] The preparation method of above-mentioned butyl rubber waterproof self-adhesive roll material, comprises the following steps:

[0026] 1) Take by weighing 1.5kg butyl rubber, 500g carbon black, 1.6kg polyisobutylene, 200g petroleum resin, 800g white oil, 8kg kaolin and 80g antioxidant;

[0027] 2) Put the above raw materials in a kneader, knead for 15 minutes at a temperature of 120° C., and extrude on an extruder after cooling to obtain a waterproof self-adhesive layer of butyl rubber;

[0028] 3) The butyl rubber waterproof self-adhesive layer obtained in step 2) is separated and curled with a release paper to obtain a butyl rubber waterproof self-adhesive coiled material.

Embodiment 3

[0030] A butyl rubber waterproof self-adhesive coiled material, comprising the following raw materials in parts by weight: 10 parts of butyl rubber; 1 part of carbon black; 12 parts of polyisobutylene; 0.5 parts of terpene resin; 5 parts of white oil; 65 parts of kaolin; 0.5 parts of the agent.

[0031] The preparation method of above-mentioned butyl rubber waterproof self-adhesive roll material, comprises the following steps:

[0032] 1) Weigh 1kg butyl rubber, 100g carbon black, 1.2kg polyisobutylene, 50g terpene resin, 500g white oil, 6.5kg kaolin and 50g antioxidant;

[0033] 2) Put the above-mentioned raw materials in a kneader, knead for 15 minutes at 100°C, and extrude on an extruder after cooling to obtain a waterproof self-adhesive layer of butyl rubber;

[0034] 3) The butyl rubber waterproof self-adhesive layer obtained in step 2) is separated and curled with a release paper to obtain a butyl rubber waterproof self-adhesive coiled material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a waterproof self-adhesive coiled material prepared from butyl rubber. The coiled material is prepared from, by weight, 7-15 parts of the butyl rubber, 0.5-5 parts of carbon black, 10-16 parts of polyisobutene, 0.3-2 parts of resin, 2-8 parts of white oil, 60-80 parts of kaolin and 0.1-0.8 part of anti-aging agent. The invention further discloses a preparation method of the waterproof self-adhesive coiled material prepared from the butyl rubber. The waterproof self-adhesive coiled material prepared from the butyl rubber has the advantages of being good in chemical stability, good in aging resistance, capable of being used for a long time under the environmental condition of -40 DEG C-80 DEG C, capable of prolonging the service life, long in service life, environmentally friendly, safe, easy, convenient and rapid to use, good in air tightness and water tightness, strong in viscosity, capable of being firmly bonded with a building main structure and the like.

Description

technical field [0001] The invention relates to building waterproof materials, in particular to a butyl rubber waterproof self-adhesive coiled material and a preparation method thereof. Background technique [0002] Building waterproofing is an important part of construction engineering, and the quality of waterproofing projects directly affects the service life and safety of buildings. Waterproof membrane is a commonly used material in building construction and plays an important role in preventing leakage. Nowadays, the waterproof membrane is often used to paste the concrete cushion for underground waterproofing, but the waterproof membrane cannot be directly bonded to the underground main structure, causing the waterproof layer to be separated from the main structure, so that the waterproof layer is easily damaged. Traditional waterproof self-adhesive materials will flow, rapidly age, and dry out under extreme conditions of repeated alternating cold and heat, which will ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J123/22C09J11/04C09J7/00
CPCC08L2201/08C08L2205/025C08L2205/035C09J7/00C09J11/04C09J123/22C09J2301/408C09J2423/00C08L23/22C08K3/346C08K3/04
Inventor 王辉
Owner 广州市伟能高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap