A low-temperature early-strength high-strength underwater grouting material

An underwater grouting and early-strength technology, which is applied in the field of building materials, to achieve the effect of improving later strength, improving low-temperature early-strength, and good low-temperature early-strength

Active Publication Date: 2018-05-04
JIANGSU SOBUTE NEW MATERIALS
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the problem of grouting quality in underwater low-temperature environment, the invention provides a cement-based grouting material suitable for underwater low-temperature environment, with fast early-strength strength increase, high final strength and strong underwater dispersion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low-temperature early-strength high-strength underwater grouting material
  • A low-temperature early-strength high-strength underwater grouting material
  • A low-temperature early-strength high-strength underwater grouting material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Low-temperature early-strength high-strength underwater grouting material is mixed with the following components by weight:

[0038]

[0039] Among them, the mineral powder is ultra-fine mineral powder with a specific surface area of ​​1500m 2 / kg; the bulk density of encrypted silica fume is 500kg / m 3 The composite expansion agent is a mixture of alkali metal plastic expansion agent and sulphoaluminate expansion agent with a mass ratio of 1:60; the early-strength powder water reducer adopts PCA-500P high-performance polycarboxylic acid of Jiangsu Subote Co., Ltd. Early-strength water reducer; nano calcium silicate hydrate is nano calcium silicate hydrate powder; anti-dispersion compound is a mixture of 6 million molecular weight polyacrylamide and hydroxypropyl guar gum with a mass ratio of 1:3.

Embodiment 2

[0041] Low-temperature early-strength high-strength underwater grouting material is mixed with the following components by weight:

[0042]

[0043]

[0044] Among them, the mineral powder is ultra-fine mineral powder with a specific surface area of ​​1700m 2 / kg; the bulk density of encrypted silica fume is 700kg / m 3 The composite expansion agent is a mixture of alkali metal plastic expansion agent and sulphoaluminate expansion agent with a mass ratio of 1:60; the early-strength powder water reducer adopts PCA-500P high-performance polycarboxylic acid of Jiangsu Subote Co., Ltd. Early-strength water reducer; nano calcium silicate hydrate is nano calcium silicate hydrate powder; anti-dispersion compound is a mixture of 6 million molecular weight polyacrylamide and hydroxypropyl guar gum with a mass ratio of 1:4.

Embodiment 3

[0046] Low-temperature early-strength high-strength underwater grouting material is mixed with the following components by weight:

[0047]

[0048] Among them, the mineral powder is ultra-fine mineral powder with a specific surface area of ​​1500m 2 / kg; the bulk density of encrypted silica fume is 600kg / m 3 The composite expansion agent is a mixture of alkali metal plastic expansion agent and sulphoaluminate expansion agent with a mass ratio of 1:60; the early-strength powder water reducer adopts PCA-500P high-performance polycarboxylic acid of Jiangsu Subote Co., Ltd. Early-strength water reducer; nano calcium silicate hydrate is nano calcium silicate hydrate powder; anti-dispersion compound is a mixture of 6 million molecular weight polyacrylamide and hydroxypropyl guar gum with a mass ratio of 1:3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
densityaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention provides a low-temperature early-strength high-strength underwater grouting material. The low-temperature early-strength high-strength underwater grouting material consists of the following ingredients in parts by weight: 30-45 parts of ordinary Portland cement, 45-60 parts of fine aggregate, 5-10 parts of mineral powder, 2-4 parts of encryption silica fume, 0.5-1 part of a compound expanding agent, 0.2-0.5 part of an early-strength powdery water reducer, 0.1-0.5 part of nano hydrated calcium silicate, 0.3-0.5 part of a compound early-strength agent and 0.1-0.3 part of a dispersion-resistant compound. The low-temperature early-strength, low-temperature high-strength and dispersion resistant properties of the low-temperature early-strength high-strength underwater grouting material in water are improved at the same time in the four aspects of reducing the void ratio of the aggregate, optimizing the expanding components and improving the nano early strength and the dispersion resistance, the construction performance, such as the water holding performance and the viscosity, of the grouting material are remarkably improved, the 1d strength and the 28d strength of the grouting material under the undersea low-temperature condition are effectively improved, and the underwater dispersion resistance of the grouting material can be greatly improved. The low-temperature early-strength high-strength underwater grouting material has favorable low-temperature early-strength, low-temperature high-strength and underwater dispersion resistant functions.

Description

technical field [0001] The invention belongs to the field of building materials, in particular to a low-temperature early-strength high-strength underwater grouting material. Background technique [0002] As a common repair and reinforcement material, cement-based grout has been widely studied and applied. In recent years, with the increase in the scale of infrastructure construction in my country, the scope of use of grouting materials has also been fully expanded to fields such as electric power, ports, and oceans, and has been gradually applied to complex environments such as low temperature and water on the seabed. The low-temperature early strength, low-temperature high-strength and anti-dispersion properties put forward higher requirements. [0003] The ambient temperature has a very important influence on the hardening speed and mechanical properties of the grouting material. Especially under the low temperature condition of the seabed, ordinary Portland cement has sl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B24/24C04B22/08C04B24/04C04B111/70C04B111/74C04B103/12
CPCC04B28/04C04B40/0039C04B2103/0082C04B2103/12C04B2111/70C04B2111/74C04B2201/50C04B14/068C04B18/141C04B18/146C04B2103/0068C04B24/24C04B22/08C04B24/04C04B22/085C04B24/2652C04B24/38
Inventor 徐海源沙建芳郭飞吴洲刘建忠
Owner JIANGSU SOBUTE NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com