A kind of continuous annealing production method of thin-gauge cold-rolled lace-rolled hard steel plate

A continuous annealing furnace and lace rolling technology, applied in furnaces, heat treatment equipment, heat treatment furnaces, etc., can solve problems such as broken strips, easy deviation, and difficulty in stable production, and achieve the elimination of losses, good strip shape, and qualified performance Effect

Active Publication Date: 2017-12-19
SHANGHAI MEISHAN IRON & STEEL CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to provide a continuous annealing production method of thin-gauge cold-rolled lace-rolled hard steel plate, which solves the problem that the existing 0.17-0.20 mm thick cold-rolled lace-rolled hard steel plate is difficult to stabilize when annealing with a continuous annealing unit due to the presence of lace plate shape defects Production and technical problems of easy deviation and broken belt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A vertical continuous annealing furnace unit is used to uncoil, clean, anneal, smooth, and coil a cold-rolled lace-rolled hard steel plate with a plate thickness of 0.186 mm to obtain an electroplated tin substrate. Among them, the chemical composition weight of the cold-rolled lace-rolled hard steel plate The percentages are: C: 0.104%, Si: 0.0245%, Mn: 0.3816%, P: 0.0125%, S: 0.0024%, Cu: 0.0276%, Alt: 0.0562%, N: 0.0066%, and the balance is Fe and unavoidable impurity elements; the yield strength of the cold-rolled lace-rolled hard steel plate is 854MPa, the tensile strength is 935MPa, the substrate hardness HR30T is 83, and the substrate surface roughness Ra0.45um;

[0033] The strip unit tension of the cold-rolled lace-rolled hard steel plate in the cleaning section of the vertical continuous annealing furnace is from 43.02N / mm when there is no lace plate shape defect 2 Control drop to 38.80N / mm 2 ;

[0034] Eight minutes before the cold-rolled lace-rolled hard s...

Embodiment 2

[0038] Use a vertical continuous annealing furnace unit to uncoil, clean, anneal, smooth, and coil a cold-rolled lace-rolled hard steel plate with a plate thickness of 0.171mm to obtain an electroplated tin substrate; wherein, the chemical composition of the cold-rolled lace-rolled hard steel plate is For: C: 0.0976%, Si: 0.0137%, Mn: 0.3899%, P: 0.0138%, S: 0.0079%, Cu: 0.0219%, Alt: 0.0546%, N: 0.00608%, the balance is Fe and unavoidable Impurity elements; the yield strength of the cold-rolled lace-rolled hard steel plate is 886MPa, the tensile strength is 976MPa, the substrate hardness HR30T is 85, and the substrate surface roughness is 0.40um.

[0039] The strip unit tension of the cold-rolled lace-rolled hard steel plate in the cleaning section of the vertical continuous annealing furnace is from 43.02N / mm when there is no lace plate shape defect 2 Control drop to 35.62N / mm 2 ;

[0040] 10 minutes before the cold-rolled lace-rolled hard steel plate enters the vertical c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a continuous annealing production method of thin-gauge cold-rolled lace-rolled hard steel plate, which solves the problem that the existing 0.17-0.20mm thick cold-rolled lace-rolled hard steel plate is difficult to stably produce when it is annealed by a continuous annealing unit due to lace plate shape defects question. The technical solution of the present invention is to use a vertical continuous annealing furnace unit to uncoil, clean, anneal, smooth, and coil a cold-rolled lace-rolled hard steel sheet with a plate thickness of 0.17-0.20 mm to obtain an electro-tinned substrate; the strip in the cleaning section The steel unit tension is 28.05~38.89N / mm2; 5~10 minutes before the cold-rolled lace-rolled hard steel plate coil enters the vertical continuous annealing furnace unit, the strip speed in the central section of the unit is reduced to 350~500mpm, and the heating section in the annealing furnace and The temperature of the strip steel in the soaking section drops to 585~605°C; the annealing time is 54~79S; the unit tension of the strip steel in the soaking section is 11.4~15.0N / mm2.

Description

technical field [0001] The invention relates to a continuous annealing production method of cold-rolled steel plates, in particular to a continuous annealing production method of thin-gauge cold-rolled lace-rolled hard steel plates, and belongs to the technical field of iron-based alloys. Background technique [0002] Iron and steel enterprises use continuous annealing units to recrystallize and anneal the work-hardened strip steel after cold rolling to improve the microstructure and improve the plasticity and stamping formability of the strip steel. However, the high-speed thin-strip continuous annealing unit is very sensitive to the shape of the incoming strip due to the fast running speed of the strip in the annealing furnace. If the shape of the incoming strip exceeds a certain level, it is very easy to cause stripping. Steel deviation, and even lead to broken belt accidents. This causes a great loss to the continuous annealing unit in terms of production capacity, fini...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D9/56C21D1/26
Inventor 刘洪王涛陈维晋曹博蕊王海军徐烨明
Owner SHANGHAI MEISHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com