A voltage-resistant paint for motors

A voltage-resistant and paint-resistant technology, which is applied in coatings, polyurea/polyurethane coatings, etc., can solve problems such as short service life and poor electric shock resistance, and achieve long service life, strong voltage resistance and excellent overall performance.

Active Publication Date: 2018-04-13
NANJING GAOQI ELECTRIC
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are many kinds of paints for motors and various functions, but there are still some defects, such as poor resistance to electric shock, short service life, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A voltage-resistant paint for motors

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Party:

[0020] 100 parts of polyacrylic resin, 40 parts of polyurethane, 2 parts of diethyl maleate, 15 parts of xylene, 1 part of linseed oil, 2 parts of silica bath clay, 1 part of talcum powder, 2 parts of glass powder , 1 part of nano silica gel, 1 part of graphite powder, 1 part of pigment.

[0021] The degree of polymerization of the polyacrylic resin is 80.

[0022] The average particle size of the nano silica gel is 200 nm.

[0023] Preparation:

[0024] In the molten state, mix polyacrylic resin, polyurethane, diethyl maleate, xylene and linseed oil, add fully crushed silica bath clay, talcum powder, glass powder, nano silica gel, graphite Powder and pigment are evenly dispersed, ready to be obtained.

Embodiment 2

[0026] Party:

[0027] 100 parts of polyacrylic resin, 60 parts of polyurethane, 12 parts of diethyl maleate, 25 parts of xylene, 5 parts of linseed oil, 8 parts of silica bath clay, 5 parts of talcum powder, 6 parts of glass powder , 7 parts of nano silica gel, 7 parts of graphite powder, 5 parts of pigments.

[0028] The degree of polymerization of the polyacrylic resin is 100.

[0029] The average particle size of the nano silica gel is 400 nm.

[0030] Preparation:

[0031] In the molten state, mix polyacrylic resin, polyurethane, diethyl maleate, xylene and linseed oil, add fully crushed silica bath clay, talcum powder, glass powder, nano silica gel, graphite Powder and pigment, evenly dispersed, ready to be obtained.

Embodiment 3

[0033] Party:

[0034] 100 parts of polyacrylic resin, 50 parts of polyurethane, 7 parts of diethyl maleate, 20 parts of xylene, 3 parts of linseed oil, 5 parts of silica bath clay, 3 parts of talcum powder, 4 parts of glass powder , 4 parts of nano silica gel, 4 parts of graphite powder, 3 parts of pigments.

[0035] The degree of polymerization of the polyacrylic resin is 90.

[0036] The average particle size of the nano silica gel is 300 nm.

[0037] Preparation:

[0038] In the molten state, mix polyacrylic resin, polyurethane, diethyl maleate, xylene and linseed oil, add fully crushed silica bath clay, talcum powder, glass powder, nano silica gel, graphite Powder and pigment are evenly dispersed, ready to be obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a voltage-resistant paint for motors. The voltage-resistant paint for motors is mainly prepared from, by weight, 100 parts of polyacrylic resin, 40-60 parts of polyurethane, 2-12 parts of diethyl maleate, 15-25 parts of xylene, 1-5 parts of linseed oil, 2-8 parts of kieselguhr, 1-5 parts of talcum powder, 2-6 parts of glass powder, 1-7 parts of nano-silica gel, 1-7 parts of graphite powder and 1-5 parts of pigment. Compared with the prior art, the voltage-resistant paint for motors is low in cost, simple in process, high in voltage resistance, long in service life and excellent in overall performance.

Description

Technical field [0001] The invention relates to a voltage-resistant paint for a motor, and belongs to the technical field of paint for a motor. Background technique [0002] The power industry originated in the late 19th century and has achieved rapid development more than 100 years after its birth. Electricity has become the lifeblood of the development of the national economy. The development of the power industry reflects the development of the national economy. With the development of the power industry, the use of power facilities is increasing. Most of the motors run outdoors, and they endure long-term wind, sun, and rain. They are also exposed to air pollution such as dust, sulfur dioxide, nitrogen oxides and other emissions, as well as acid rain, lightning, electric shocks and other pollution and corrosion. This can cause cracks, equipment shells, steel frames and other facilities to rust. At the same time, some areas are still minefields, threatening the safe operation ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D175/04C09D7/61C09D7/63
CPCC08K2201/011C08L2205/03C09D7/61C09D7/63C09D7/65C09D7/68C09D133/00C08L75/04C08L91/00C08K13/02C08K5/11C08K3/34C08K3/40C08K3/36C08K3/04
Inventor 徐榕锋
Owner NANJING GAOQI ELECTRIC