Granular cellulose filter aid applied to titaniferous solution filter in production of titanium oxide

A production process and filter aid technology, applied in other chemical processes, alkali metal oxides/hydroxides, inorganic chemistry, etc., can solve problems such as affecting production efficiency, dust, and inability to settle, saving transportation and storage Cost, easy to promote and apply, easy to use effect

Inactive Publication Date: 2016-08-17
SHANGHAI TONNOR MATERIAL SCI
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The currently used filter aids are all in the form of powder, which occupy a large area during storage, and there is a lot of dust when feeding. In addition, the powder filter aid has a small density and is light, and will float on the surface o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Granular cellulose filter aid applied to titaniferous solution filter in production of titanium oxide
  • Granular cellulose filter aid applied to titaniferous solution filter in production of titanium oxide
  • Granular cellulose filter aid applied to titaniferous solution filter in production of titanium oxide

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0011] Example 1: The powdered organic fiber filter aid was prepared into a cylindrical particle filter aid with a length of 1 to 3 cm and a diameter of 0.6 cm. The original powdered cellulose filter aid was used for titanium dioxide addition, filtration and pre-coating. Filtration, feeding and stirring time can be shortened from the original 30min to 10min, and the feeding dust can be completely eliminated. The storage space of 1t granular cellulose products can be reduced by 1.5cm 3 Storage space reduced to 0.3 cm 3 .

Example Embodiment

[0012] Example 2: Prepare a powdered organic fiber filter aid into a bean-shaped granular filter aid with a length of 0.5 to 1 cm and a width of 0.3 to 0.6 cm. The amount of the original powdered cellulose filter aid is used for the addition and filtration of titanium dioxide. Pre-coating and filtering, the feeding and stirring time can be shortened from the original 30min to 5min, and the feeding dust can be completely eliminated. The storage space of 1t granular cellulose products can be reduced by 1.5cm 3 The storage space is reduced to 0.4cm 3 .

Example Embodiment

[0013] Example 3: Prepare powdered organic fiber filter aid into cake-like particulate filter aid with a thickness of 0.3-6 cm, and use the original powdered cellulose filter aid for titanium dioxide addition filtration and pre-coating filtration, adding and stirring The time can be shortened from the original 30min to 8min, which can significantly reduce the feeding dust. The storage space of 1t granular cellulose products can be reduced by 1.5 cm 3 Storage space reduced to 0.5 cm 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a granular cellulose filter aid used in the production process of titanium dioxide to realize the filtration of titanium liquid. The appearance of the filter aid is columnar, flake, cake, triangular, conical or other irregular Three-dimensional or planar shape, in the process of titanium dioxide production to realize the filtration of titanium liquid, the details are as follows: the filter aid can be quickly dispersed into powder after being mixed with the titanium liquid to be filtered, or with water, or with sulfuric acid liquid, and formed with liquid The suspension, which is pre-coated on the filter medium, and the filter aid pre-coating layer on the filter medium is used in the field of titanium dioxide production. The advantages of this granular filter aid compared with powdered ones are: under the same quality, the storage space can be reduced, and logistics costs such as transportation can be saved; there is no dust in the titanium liquid filtration process, which reduces the harm of dust to the health of workers and the environment. It can quickly settle into the mixing tank, reduce the time of stirring and dispersing, and improve the production efficiency of titanium liquid filtration.

Description

technical field [0001] The invention relates to a filter aid, in particular to a granular cellulose filter aid used in the production process of titanium dioxide to realize the filtration of titanium liquid. Background technique [0002] In the titanium dioxide filtration process, it is necessary to use filter aids to ensure the quality of the product. Commonly used filter aids include diatomaceous earth, activated carbon, perlite, and cellulose. The currently used filter aids are all in the form of powder, which occupy a large area during storage, and there is a lot of dust when feeding. In addition, the powder filter aid has a small density and is light, and will float on the surface of the titanium liquid in large quantities, and cannot settle to the stirring surface. At the bottom of the tank, it takes a long time to stir to make the filter aid evenly dispersed in the titanium liquid, which affects the production efficiency. Contents of the invention [0003] The purp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/24B01J20/28
CPCB01J20/24B01J20/28016
Inventor 张楠
Owner SHANGHAI TONNOR MATERIAL SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap