Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Special active solvent for making surface textures of PVC (polyvinyl chloride) wood-plastic product

An active solvent and wood-plastic product technology, applied in the field of wood-plastic composite products, can solve the problem of special active solvent for the surface texture of PVC wood-plastic products, etc., and achieve high hardness, realistic texture pattern effect and good wear resistance. Effect

Inactive Publication Date: 2016-09-07
GUILIN SHUKANG BUILDING MATERIAL
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] PVC wood-plastic products are wood-plastic products of different shapes made by mixing biomass materials such as crop straw, wood powder, wood fiber and PVC (polyvinyl chloride) in proportion. See the relevant reports about the special active solvent used for making the surface texture of PVC wood-plastic products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special active solvent for making surface textures of PVC (polyvinyl chloride) wood-plastic product
  • Special active solvent for making surface textures of PVC (polyvinyl chloride) wood-plastic product
  • Special active solvent for making surface textures of PVC (polyvinyl chloride) wood-plastic product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Weigh each raw material according to Table 1 below, mix evenly, and let stand for 30 minutes before use.

Embodiment 2

[0020] Weigh each raw material according to Table 1 below, mix evenly, and let stand for 30 minutes before use.

Embodiment 3

[0022] Weigh each raw material according to Table 1 below, mix evenly, and let stand for 30 minutes before use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a special active solvent for making surface textures of a PVC (polyvinyl chloride) wood-plastic product. The special active solvent is prepared from the following raw materials in parts by weight: 10 to 20 parts of dimethylbenzene, 10 to 20 parts of banana oil, 5 to 10 parts of acetone, 1 to 5 parts of butanone, 1 to 5 parts of cyclohexanone, 3 to 8 parts of 502 glue, 1 to 5 parts of haze remover and 1 to 5 parts of finish paint. Compared with the prior art, the special active solvent for making the surface textures of the PVC wood-plastic product has the advantages that when the active solvent is combined with a hydraulic pressure covering adhesion process, a pattern on a printed film can be clearly and firmly attached to the surface of a wood-plastic product blank with the adhesion force of 0 level, a texture pattern on the surface of the obtained wood-plastic product is vivid, the surface is smooth and clean, and a paint film of the obtained product is higher in hardness (capable of reaching 6H or more than 6H) and wear resistance (the wear value g / 100r is less than or equal to 0.01).

Description

technical field [0001] The invention relates to wood-plastic composite material products, in particular to a special active solvent used for making surface textures of PVC wood-plastic products. Background technique [0002] Wood-plastic composite material is a new type of environmentally friendly material prepared by mixing biomass materials such as crop straw, wood powder, and wood fiber with polymer materials obtained from waste plastics in proportion to a certain process. Recycling of industrial materials. Wood-plastic composite materials have the advantages of both biomass materials and polymer materials, so they are widely used in packaging, warehousing, urban construction and architectural decoration industries. [0003] There are mainly the following types of decoration for wood-plastic composite materials: ①Processing colored profiles, that is, adding a certain colorant to the wood-plastic composite material batching process to achieve the effect of decoration, but...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J7/02
CPCC08J7/02
Inventor 严秀芹陆绍荣卢李勤曾岑卢秋宇谢超韦明罗崇禧
Owner GUILIN SHUKANG BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com