A method for improving the cohesion of fresh cocoon threads

A technology of cocoon silk and mixing tank, which is applied in the chemical post-processing of fibers, textile and papermaking, fiber processing, etc., can solve the problems of inability to produce fresh cocoon silk with cohesion requirements, reduce the dissolution of sericin, improve the cohesion index, The effect of improving swelling performance

Active Publication Date: 2018-06-22
SHANGLIN ZHONGXING SILK
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitation of its own technology, this method cannot produce fresh cocoon silk with higher cohesion requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for improving cocoon cohesion, comprising the following steps:.

[0029] A. Put the fresh cocoon silk into the freezer, flush nitrogen into the freezer, and carry out low-temperature treatment to the fresh cocoon silk;

[0030] B, put the fresh cocoon silk processed through step A into the soaking pool, and soak;

[0031] C, put the fresh cocoon silk processed through step B into the stirring tank, and heat and stir;

[0032] D, put the fresh cocoon silk processed through step C into a vacuum tank, and carry out vacuum infiltration;

[0033] E. Cleaning and air-drying the fresh cocoon thread processed through step D.

[0034] In step A, the temperature of the freezer is kept at -10° C., and the low-temperature treatment time of the fresh cocoons is 3.5 hours.

[0035] In step B, the soaking solution in the soaking tank includes the following components in parts by mass,

[0036] 7 parts of glycerin, 18 parts of ethylene glycol, 4 parts of polyacrylamide, 3 ...

Embodiment 2

[0049] A method for improving cocoon cohesion, comprising the following steps:.

[0050] A. Put the fresh cocoon silk into the freezer, flush nitrogen into the freezer, and carry out low-temperature treatment to the fresh cocoon silk;

[0051] B, put the fresh cocoon silk processed through step A into the soaking pool, and soak;

[0052] C, put the fresh cocoon silk processed through step B into the stirring tank, and heat and stir;

[0053] D, put the fresh cocoon silk processed through step C into a vacuum tank, and carry out vacuum infiltration;

[0054] E. Cleaning and air-drying the fresh cocoon thread processed through step D.

[0055] In step A, the temperature of the freezer is kept at -15° C., and the low temperature treatment time of the fresh cocoons is 4 hours.

[0056] In step B, the soaking solution in the soaking tank includes the following components in parts by mass,

[0057] 9 parts of glycerin, 15 parts of ethylene glycol, 3 parts of polyacrylamide, 2 pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for increasing cohesive force of fresh cocoon filaments. The method comprises the following steps: A) putting the fresh cocoon filaments into a refrigerator, filling nitrogen into the refrigerator and treating the fresh cocoon filaments at low temperature; B) putting the fresh cocoon filaments treated in the step A) into a soaking pool for soaking; C) putting the fresh cocoon filaments treated in the step B) into a stirring jar, heating and stirring; D) putting the fresh cocoon filaments treated in the step C) into a vacuum tank for carrying out vacuum infiltration; and E) cleaning and air-drying the fresh cocoon filaments treated in the step D). According to the method provided by the invention, the defects of the prior art can be overcome, and the cohesive force of the fresh cocoon filaments can be further increased.

Description

technical field [0001] The invention relates to the technical field of raw silk processing, in particular to a method for improving cohesion of fresh cocoon silk. Background technique [0002] The cohesion of raw silk refers to the degree of difficulty in breaking apart the cocoon threads that make up raw silk after friction, reflecting the firmness of the cocoon threads that make up raw silk. The cohesion of raw silk has a lot to do with the cocoon cooking process. The sericin swelling of uncooked cocoon silk is not sufficient, and the cocoon silk cannot be wrapped together when the raw silk is reeled, and the cocoon silk has poor bundling property; The silk fibroin and sericin of boiled fresh cocoon silk have poor binding force, so the sericin is easy to fall off during weaving, and after the pre-weaving treatment, the surface of the silk strip is uneven and fluffy, the silk strip splits, and the fresh cocoon silk cohesion The decline in indicators has become a major prob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01C3/00
CPCD01C3/00
Inventor 殷建勋
Owner SHANGLIN ZHONGXING SILK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products