Surface treatment process for wire rod

A surface treatment and process technology, applied in the field of wire rod surface treatment technology, can solve the problems of low production efficiency, complex wire rod production process, uneven wire rod quality, etc., to improve work efficiency, eliminate repetitive processes, simple craftsmanship

Inactive Publication Date: 2016-10-05
重庆麦卡瑞机械制造有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the wire rod production process is complicated, and there is no uniform standard, resulting in uneven quality of the produced wire rod. Many repeated processes also make the production efficiency low, increase the labor burden of workers, and make the market competitiveness of the product is not high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The technical solution disclosed in the present invention is a wire rod surface treatment process, which is characterized in that it includes the following steps: 1) pickling: hydrochloric acid pool density ≥ 120;

[0015] 2) Wash and swing 2-3 times;

[0016] 3) High-pressure water washing: wash away the residual acid;

[0017] 4) Phosphating: The total acidity of the phosphating pool is 120-180 points, the free acid is 10-20 points, the total zinc content is 40-60g / L, the temperature is greater than 65°C, and the phosphating time is 2-10 minutes;

[0018] 5) High pressure water washing;

[0019] 6) Saponification: saponification tank temperature ≥ 85 ℃, PH value ≥ 8;

[0020] 7) Dry naturally.

[0021] The method has simple process, eliminates many repetitive processes, and improves work efficiency.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a surface treatment process for a wire rod. The surface treatment process is characterized by comprising the following steps: 1) acid pickling, wherein the density of a hydrochloric acid pool is no less than 120; 2) water scrubbing and swinging twice to three times; 3) flushing with high pressure water so as to totally remove residual acid; 4) phosphatization, wherein the total acidity of a phosphatization pool is 120 to 180 points, free acid is 10 to 20 points, total zinc amount is 40 to 60 g / L, temperature is greater than 65 DEG C, and phosphatization time is 2 to 10 min; 5) flushing with high pressure water; 6) saponification, wherein the temperature and pH value of a saponification pool is no less than 85 DEG C and 8 respectively; and 7) natural drying. The process provided by the invention is simple, omits a plurality of repeated procedures and improves work efficiency.

Description

technical field [0001] The invention relates to a wire rod surface treatment process. Background technique [0002] Wire rod is also called wire rod, and wire rod is also called wire rod, which usually refers to small-diameter round steel in a coil. The diameter of the wire rod is in the range of 5-19mm (usually 6-9mm), and the lower limit is the minimum size of the hot-rolled steel section. [0003] In the production process of metal products, due to the existence of scale on the surface of wire rods, the subsequent drawing of steel wires is affected, so removing scale is an essential and important process in the production of metal products. [0004] At present, the wire rod production process is complex and there is no unified standard, resulting in uneven quality of the produced wire rod. Many repeated processes also make the production efficiency low, increase the labor burden of workers, and make the market competitiveness of the product is not high. Contents of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/73
Inventor 凌庭贵
Owner 重庆麦卡瑞机械制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap