Single crystalline silicon solar cell surface texture solution containing notoginsenoside and preparation method thereof

A technology of solar cell sheet and notoginseng saponin, which is applied in the field of solar cells, can solve the problems of high price of isopropanol, poor reaction uniformity, and fast volatilization speed, and achieve the effects of small particles, fast reaction speed, and high recycling rate

Inactive Publication Date: 2016-10-12
CHINALAND SOLAR ENERGY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, chemical etching is the most commonly used method for surface texture of single crystal silicon, and the commonly used texturing liquid is NaOH / isopropanol system, but isopropanol is expensive, volatilizes quickly, costs high and is not conducive to environmental protection
Patent 201010161287.8 discloses a monocrystalline silicon additive texturing solution, which is composed of alkaline corrosion solution, surfactant and organic acid or salt, does not contain isopropanol and is fast and efficient, but it has the problem of poor uniformity of reaction, which is easy to cause After texture, the pyramids on the silicon surface are too large and local over-corrosion, etc., the quality of the silicon wafers needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A monocrystalline silicon solar cell surface texture liquid containing notoginsenoside, prepared from the following component raw materials by weight (kg):

[0015] Notoginseng saponin 0.05, maltodextrin 0.05, styrene 1.5, 5-10% ammonium persulfate solution 1, sodium lauryl sulfate 0.1, potassium fulvic acid 0.1, dodecafluoroheptylpropyltrimethoxysilane 0.1 , sodium hydroxide 3, citric acid 0.3, polyethylene glycol monomethyl ether 0.1, water 100.

[0016] A preparation method of a monocrystalline silicon solar cell surface texture liquid containing notoginsenoside, comprising the following steps:

[0017] (1) Weigh raw materials by weight, first add sodium lauryl sulfate to 1 / 3 weight of water and stir evenly, then slowly add the mixture of styrene and dodecafluoroheptylpropyltrimethoxysilane and stir for 0.5h , and finally slowly add ammonium persulfate solution dropwise and stir at 70°C for 2 hours, keep warm for 3 hours and then cool to obtain a composite emulsion;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
reflectanceaaaaaaaaaa
Login to view more

Abstract

The invention discloses a single crystalline silicon solar cell surface texture solution containing notoginsenoside. The single crystalline silicon solar cell surface texture solution is prepared from, by weight, 0.05-0.1 part of notoginsenoside, 0.05-0.1 part of maltodextrin, 1.5-2.5 parts of styrene, 1-2 parts of a 5-10% ammonium persulfate solution, 0.1-0.2 part of lauryl sodium sulfate, 0.1-0.15 part of BSFA, 0.1-0.15 part of dodecafluoroheptyl-propyl-trimethoxysilane, 3-5 parts of sodium hydroxide, 0.3-0.5 part of citric acid, 0.1-0.15 part of polyethylene glycol monoethylether and 100-120 parts of water. The silicon slice texture solution is high in reaction speed, moderate in corrosion, small in thickness reduction and high in repeated utilization factor, the obtained texture pyramid is uniform in size, granules are small, the decontamination effect is good, and subsequent handling silicon slice treatment is promoted.

Description

technical field [0001] The invention relates to the technical field of solar cells, in particular to a liquid for surface texturing of monocrystalline silicon solar cells containing notoginsenoside and a preparation method thereof. Background technique [0002] As the world's energy crisis becomes more serious, solar energy has become the most potential alternative energy source, and a solar cell is an electronic component that directly converts solar energy into electrical energy. The main problem hindering the development of solar cell technology is its high manufacturing cost. At present, in order to reduce the cost of monocrystalline silicon solar cells and improve the photoelectric conversion efficiency, silicon surface texturing is the easiest and most efficient method. Texture, also known as velvet, uses the principle of light trapping to make the incident light reflect multiple times to prolong its propagation path on the surface of the battery, thereby improving th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C30B33/10H01L31/0236H01L31/18
CPCC30B33/10H01L31/02363H01L31/1804Y02E10/547Y02P70/50
Inventor 李尚荣王可胜程晓民孟祥法郭万东袁艺琴
Owner CHINALAND SOLAR ENERGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products