Method for manufacturing ocean glaze

A production method and marine technology, applied in the field of marine glaze production, can solve rare problems and achieve the effect of strong three-dimensional sense and high artistic ornamental value

Active Publication Date: 2016-10-26
HUNAN LILING CHUHUA CERAMIC INDAL
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are not many ceramic products re

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing ocean glaze
  • Method for manufacturing ocean glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A manufacturing method of marine glaze includes the following steps:

[0029] (1) Prepare base glaze and top glaze according to the following components and parts by weight ratio;

[0030] A. Base glaze

[0031] Potash feldspar 40 parts

[0032] 30 parts of high fire clay

[0033] Shi Ying 20 parts

[0034] 10 parts of calcite

[0035] Iron red 15 parts;

[0036] B. Surface glaze

[0037] 30 parts of potassium feldspar

[0038] 20 parts of albite

[0039] Spodumene 10 parts

[0040] Zinc oxide 12 parts

[0041] 25 servings of tea mountain mud

[0042] 4 parts of titanium oxide;

[0043] (2) Wet ball mill the base glaze prepared in step (1) with the ball and water at a mass ratio of 1:2:0.5 for 16 hours. After ball milling, the glaze is passed through a 160 mesh sieve, and then adjusted to 45 Baume. The glaze slurry is manually applied to the body, and it will be used after natural drying;

[0044] (3) The surface glaze prepared in step (1) is wet-milled with the ball and water at a mass ra...

Embodiment 2

[0047] A manufacturing method of marine glaze includes the following steps:

[0048] (1) Prepare base glaze and top glaze according to the following components and parts by weight ratio;

[0049] A. Base glaze

[0050] 42 parts of potassium feldspar

[0051] 33 parts of high fire clay

[0052] Shi Ying 21 copies

[0053] 11 parts of calcite

[0054] Iron red 17 parts;

[0055] B. Surface glaze

[0056] Potash feldspar 32 parts

[0057] 22 parts of albite

[0058] 11 parts of spodumene

[0059] Zinc oxide 20 parts

[0060] 27 servings of tea mountain mud

[0061] 5 parts of titanium oxide;

[0062] (2) Wet ball mill the base glaze prepared in step (1) with the ball and water at a mass ratio of 1:2:0.5 for 15 hours. After ball milling, the glaze is passed through a 160-mesh sieve, and then adjusted to 40 Baume The glaze slurry is manually applied to the body, and it will be used after natural drying;

[0063] (3) The surface glaze prepared in step (1) is wet-milled with the ball and water at a mass...

Embodiment 3

[0066] A manufacturing method of marine glaze includes the following steps:

[0067] (1) Prepare base glaze and top glaze according to the following components and parts by weight ratio;

[0068] A. Base glaze

[0069] Potash feldspar 45 parts

[0070] High fire clay 35 parts

[0071] Shi Ying 22 copies

[0072] 12 parts of calcite

[0073] Iron red 20 parts;

[0074] B. Surface glaze

[0075] Potash feldspar 35 parts

[0076] 25 parts of albite

[0077] Spodumene 12 parts

[0078] 25 parts of zinc oxide

[0079] 30 servings of tea mountain mud

[0080] 6 parts of titanium oxide;

[0081] (2) Wet ball mill the base glaze prepared in step (1) with the ball and water at a mass ratio of 1:2:0.5 for 17 hours. After ball milling, the glaze is passed through a 160 mesh sieve, and then adjusted to 50 Baume The glaze slurry is manually applied to the body, and it will be used after natural drying;

[0082] (3) The surface glaze prepared in step (1) is wet-milled with the ball and water at a mass ratio of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A method for manufacturing ocean glaze comprises a step (1) of preparing ground glaze and cover glaze, wherein the ground glaze is prepared from 40-45 parts of potassium feldspar, 30-35 parts of high duty fire clay, 20-22 parts of quartz, 10-12 parts of calcite and 15-20 parts of iron oxide red; and the cover glaze is prepared from 30-35 parts of potassium feldspar, 20-25 parts of albite, 10-12 parts of spodumene, 12-25 parts of zinc oxide, 25-30 parts of Chashan clay and 4-6 parts of titanium oxide; a step (2) of performing wet method ball milling on the ground glaze, balls and water, performing sieving, forming glaze slip at 40-50 baume degrees, manually applying the glaze slip to a green body, and performing natural drying; a step (3) of performing wet method ball milling on the cover glaze, balls and water, performing sieving, forming glaze slip at 30-40 baume degrees, brushing the cover glaze slip onto the green body coated with the ground glaze, and forming the product through firing at a temperature of 1100-1200 DEG C. The manufactured ocean glaze is high in stereoscopic impression and attractive, has high art enjoying value, and is deeply welcome by consumers.

Description

Technical field [0001] The invention relates to a manufacturing method of marine glaze. Background technique [0002] At present, there are many types of glazes, and different glazes have their unique features and reflect different beauty. As far as consumers are concerned, different consumers prefer different glazes. For example, some consumers have a soft spot for the beauty of marine glaze. However, ceramic products related to marine glaze are rare in the market. Summary of the invention [0003] The technical problem to be solved by the present invention is to provide a manufacturing method of marine glaze. [0004] The technical proposal adopted by the present invention to solve its technical problems is: a manufacturing method of marine glaze, including the following steps: [0005] (1) Prepare base glaze and top glaze according to the following components and parts by weight ratio; [0006] A. Base glaze [0007] Potash feldspar 40-45 parts [0008] 30-35 parts of high fire cla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00
CPCC03C8/00
Inventor 吴华吴德勇
Owner HUNAN LILING CHUHUA CERAMIC INDAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap