A high-strength daily-use ceramic

A high-strength, daily-use technology, used in applications, home appliances, other home appliances, etc., can solve the problems of intolerance, poor toughness, slow heat transfer, etc., and achieve low production costs, long service life, and cheap materials. Effect

Inactive Publication Date: 2018-12-07
安徽省德邦瓷业有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ceramic products are widely used all over the world. Daily-use ceramics have become an indispensable part of people's daily life. Ceramic tableware is beautiful, easy to wash, durable, good thermal stability, and slow heat transfer. However, The existing ceramic tableware has poor toughness and impact resistance, therefore, its performance needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] The present invention adopts the following technical solutions to achieve: this high-strength daily-use ceramics is composed of the following raw materials in parts by weight: 15-30 parts of silicon dioxide, 10-30 parts of calcareous clay, 10-25 parts of this clay, 5~10 parts of ceramic fiber, 5~15 parts of kaolin, 10~15 parts of aluminum silicate fiber, 2~6 parts of lapis lazuli, 10~16 parts of ball clay, 1~4 parts of barium carbonate, 6~12 parts of aluminum oxide parts, magnesium oxide 0.5~2.4 parts, sodium tripolyphosphate 2~5 parts, macroporous resin 10~18 parts and active catalyst 2~6 parts.

[0009] As a preferred version of the present invention, the high-strength daily-use ceramics are made up of the following raw materials in parts by weight: 18-27 parts of silicon dioxide, 12-25 parts of calcareous clay, 15-22 parts of this clay, 6-9 parts of ceramic fiber 8~12 parts of kaolin, 13~15 parts of aluminum silicate fiber, 3~6 parts of lapis lazuli, 13~15 parts of b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-strength ceramics for daily use. The ceramics are prepared from the following raw materials in parts by weight: 15-30 parts of silicon dioxide, 10-30 parts of calcareous clay, 10-25 parts of green blank mud, 5-10 parts of ceramic fibers, 5-15 parts of kaolin, 10-15 parts of aluminum silicate fibers, 2-6 parts of celestine, 10-16 parts of ball clay, 1-4 parts of barium carbonate, 6-12 parts of aluminum oxide, 0.5-2.4 parts of magnesia, 2-5 parts of sodium tripolyphosphate, 10-18 parts of macroporous resin and 2-6 parts of active catalyst. The high-strength ceramics for daily use have good strength, toughness and impact resistance, are large in load capacity and good in chemical properties and are resistant to oil stains, the materials are cheap and readily available, the production cost is low, and the service life is long.

Description

technical field [0001] The invention relates to daily-use ceramic products, in particular to a high-strength daily-use ceramic. Background technique [0002] Ceramic products are widely used all over the world. Daily-use ceramics have become an indispensable part of people's daily life. Ceramic tableware is beautiful, easy to wash, durable, good thermal stability, and slow heat transfer. However, The existing ceramic tableware has poor toughness and impact resistance, therefore, its performance needs to be improved. Contents of the invention [0003] The purpose of the present invention is to solve the above problems and provide a high-strength ceramics for daily use. [0004] In order to achieve the above object, the present invention provides a high-strength ceramics for daily use, which is composed of the following raw materials in parts by weight: 15-30 parts of silicon dioxide, 10-30 parts of calcareous clay, 10-25 parts of this clay, 5~10 parts of ceramic fiber, 5~...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/36
CPCC04B33/13C04B33/1305C04B33/131C04B33/36
Inventor 姚永祥
Owner 安徽省德邦瓷业有限公司