Leather tanning agent and preparing method thereof
A technology for tanning agent and leather, applied in the field of leather tanning agent and its preparation, can solve the problems of complex preparation method, unenvironmental protection of leather tanning agent, poor tanning effect, etc., and achieve the effects of soft hand feeling, high tanning efficiency and plump surface.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] A leather tanning agent, comprising the following raw materials in parts by weight: 10 parts of graphene oxide, 90 parts of modified starch, 50 parts of 3-aminopropyltriethoxysilane, and 30 parts of 3,4-ethylenedioxythiophene.
[0018] Its preparation method comprises the following processing steps:
[0019] (1) Preparation of graphene oxide dispersion liquid: add sodium nitrate, concentration to the concentrated sulfuric acid of 98% in graphite powder, stir, temperature is controlled at 1 ℃ during stirring, add potassium permanganate after stirring for 5min, slowly heat up to 36 ℃, stir while raising the temperature, keep the reaction for 5h when the temperature rises to 36℃, then add deionized water dropwise, the dropping time of deionized water is controlled at 20min, then raise the temperature to 60℃, react for 30min, add dropwise hydrogen oxidation Sodium solution, wait for the solution to turn golden yellow, then react for 30 minutes, then centrifuge, precipitate,...
Embodiment 2
[0024] A leather tanning agent, comprising the following raw materials in parts by weight: 13 parts of graphene oxide, 102 parts of modified starch, 60 parts of 3-aminopropyltriethoxysilane, and 36 parts of 3,4-ethylenedioxythiophene.
[0025] A preparation method of a leather tanning agent, comprising the following processing steps:
[0026] (1) Preparation of graphene oxide dispersion liquid: add sodium nitrate, concentration to the concentrated sulfuric acid of 98% in graphite powder, stir, temperature is controlled at 2 ℃ during stirring, add potassium permanganate after stirring 7min, slowly heat up to 38 ℃, stir while raising the temperature, keep the reaction for 5.5h when the temperature rises to 38℃, then add deionized water dropwise, the dropping time of deionized water is controlled at 22min, then raise the temperature to 63℃, react for 33min, then add hydrogen dropwise Sodium oxide solution, wait for the solution to turn golden yellow, then react for 33 minutes, th...
Embodiment 3
[0031] A leather tanning agent, comprising the following raw materials in parts by weight: 15 parts of graphene oxide, 110 parts of modified starch, 65 parts of 3-aminopropyltriethoxysilane, and 40 parts of 3,4-ethylenedioxythiophene.
[0032] Its preparation method comprises the following processing steps:
[0033] (1) Preparation of graphene oxide dispersion liquid: add sodium nitrate, concentrated sulfuric acid with a concentration of 98% to the graphite powder, stir, the temperature is controlled at 4°C during stirring, add potassium permanganate after stirring for 10min, and slowly heat up to 40°C ℃, stir while raising the temperature, keep the reaction for 6h when the temperature rises to 40℃, then add deionized water dropwise, the dropping time of deionized water is controlled at 25min, then raise the temperature to 65℃, react for 35min, add dropwise hydrogen oxidation Sodium solution, wait for the solution to turn golden yellow, then react for 35 minutes, then centrifu...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com