Asbestos fiber reinforced EPDM rubber/POE waterproof coiled material and preparation method thereof

A technology of EPDM rubber and asbestos fiber is applied in the field of building waterproof materials, which can solve the problems of flammability of the waterproof layer, hidden dangers and unsatisfactory problems, and achieve the effects of promoting dispersion, increasing strength and improving processability.

Inactive Publication Date: 2016-12-14
BENGBU TRIUMPH ENG TECH CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the EPDM waterproof membranes sold in the market are basically produced according to the national polymer waterproof membrane standards. When used on buildings, they have good waterproof effects and long working life. The fly in the ointment is that : Both the EPDM waterproof membrane and the waterproof layer used to generate it are easy to burn when exposed to open flames, so there are certain safety hazards, especially not suitable for waterproof and anti-corrosion projects for buildings with high fire protection requirements Therefore, it is not ideal from the perspective of practicality and economy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The asbestos fiber-reinforced EPDM / POE waterproof membrane of the present embodiment is prepared from the following raw materials in parts by weight: 500 parts of EPDM rubber, 80 parts of butyl rubber, 60 parts of POE, 1 , 12 parts of 3-bis(tert-butylperoxydiisopropyl)benzene, 15 parts of triallyl isocyanurate, 20 parts of stearic acid, 8 parts of 2-mercaptobenzimidazole, and 8 parts of lanthanum oxide , 20 parts of propylene glycol sebacate polyester, 10 parts of methyltriethoxysilane, 10 parts of citric acid, 6 parts of crosslinking agent TAC, 80 parts of γ-mercaptopropyltrimethoxysilane, polyoxyethylene octyl 4 parts of ether, 30 parts of zinc oxide, 2 parts of chloroplatinic acid, 30 parts of asbestos fiber, 200 parts of 10% sodium hydroxide solution, 10 parts of sodium lignosulfonate, 8 parts of benzophenone imine, tributyl citrate 8 parts of ester, 12 parts of 2,2'-dithiodibenzothiazole, appropriate amount of deionized water.

[0016] The asbestos fiber reinforce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strength at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to an asbestos fiber reinforced EPDM rubber / POE waterproof coiled material. The waterproof coiled material is characterized by being prepared from the following raw materials in parts by weight: EPDM rubber, butyl rubber, POE, 1,3-bis(tert-butyl peroxy diisopropyl)benzene, triallyl isocyanurate, stearic acid, 2-mercapto benzimidazole, lanthanum oxide, propanediol sebacate polyester, methyl triethoxysilane, citric acid, a crosslinking agent TAC, gamma-mercaptopropyl trimethoxysilane, polyoxyethylene octylphenol ether, zinc oxide, chloroplatinic acid, asbestos fiber, 8-10% sodium hydroxide solution, sodium lignin sulfonate, benzophenone imine, tributyl citrate, 2,2'-dithio-dibenzo thiazole and deionized water. Due to addition of non-inflammable asbestos fiber resistant to heat, water, acid and chemical corrosion, heat insulation and energy saving effect, flame resistance and weather resistance of the waterproof coiled material are enhanced.

Description

technical field [0001] The invention relates to a building waterproof material, in particular to an asbestos fiber-reinforced EPDM / POE waterproof coiled material and a production method thereof. technical background [0002] EPDM membrane is recognized as the waterproof membrane with the best comprehensive performance in the world, and EPDM has been used in a large number of Chinese construction projects because of its excellent physical properties. In recent years, with the advancement of social science and technology and the enhancement of people's awareness of environmental protection, the industry's requirements for building waterproof materials have changed from the previous single waterproof function to the multifunctional direction of long life, flame retardancy, and ozone aging resistance. At present, the EPDM waterproof membranes sold in the market are basically produced according to the national polymer waterproof membrane standards. When used on buildings, they ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L23/22C08L23/08C08L71/02C08K13/06C08K7/12C08K5/47C08K5/11C08K3/22C08K9/06C08K9/04C08K5/09
CPCC08L23/16C08L2201/02C08L2201/08C08L2205/035C08L23/22C08L23/0815C08L71/02C08K13/06C08K7/12C08K5/47C08K5/11C08K2003/2296C08K9/06C08K9/04C08K5/09
Inventor 宋方轲邢宝山郑纤秀王亮许新林
Owner BENGBU TRIUMPH ENG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com