High-hardness silicone-cored pipe with effect of protecting optical fibers

A technology for protection and silicon core tube, applied in the field of silicon core tube, can solve the problems of general weather resistance, oxidation resistance and solvent resistance, poor compatibility of organic materials, limited application scope, etc. The effect of high thermal performance and wide application prospects

Inactive Publication Date: 2016-12-14
黄振东
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Among silicone oil greases, methyl silicone oil grease is the most researched one. Since dimethyl silicone oil has poor thickening performance and poor compatibility with organic materials, methyl silicone oil grease has poor lubricating properties, etc. problem, which limits its scope of application
In the article "Preparation and Performance Research of Hydrocarbyl-Modified Silicone Oil Grease", Zhu Guojian used hydrogen-containing silicone oil and linear α-olefins for hydrosilylation reaction to obtain hydrocarbon-based modified silicone oil, and then made it with 12 hydroxystearic acid. Hydrocarbon-modified silicone grease was prepared by saponification reaction. The results showed that under similar viscosity, the oil film strength of hydrocarbon-modified silicone oil was greater than that of methyl silicone oil, and the lubricity was better. The refractive index of hydrocarbon-modified silicone oil was higher than that of methyl silicone oil. , closer to mineral oil, fat and organic matter, better compatibility with them, higher transparency, but the sintering load is close to that of methyl silicone oil, without improvement, and the properties of weather resistance, oxidation resistance and solvent resistance are average, The use field is reduced. In order to make the silicone oil grease can be well utilized in the silicon core tube, the present invention expands and modifies it on the basis of it, so that the prepared silicon core tube can meet the requirements of today's optical fiber for the silicon core tube. , actively reduce costs, save resources and protect the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A silicon core tube with a protective effect on optical fibers and high hardness, prepared from the following raw materials in parts by weight (kg): n-decane 190, linear undecene 65, hydrogen-containing silicone oil 190, hydroxystearic acid 15 , lithium hydroxide 4, PE carrier resin 45, color masterbatch 5, high-density polyethylene 60, sepiolite fiber 3.4, silica sol 5, antioxidant 0.3, benzotriazole 0.3, silane coupling agent a1710.3 , Deionized water amount.

[0014] The silicon core tube with high hardness and protective effect on optical fibers is prepared by the following specific steps:

[0015] (1) Stir and mix n-decane and linear undecene olefin evenly, raise the temperature to 120°C, react for 3 hours, then slowly add hydrogen-containing silicone oil and an appropriate amount of chloroplatinic acid, continue to raise the temperature to 130°C, and stir React for 6h, remove the low boilers after the reaction is finished, and obtain the olefin-modified silicone ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-hardness silicone-cored pipe with an effect of protecting optical fibers. The silicone-cored pipe is prepared from the following raw materials in parts by weight: 190-200 parts of n-decyl hydrocarbon, 65-75 parts of linear C11 olefin, 190-200 parts of hydrogen-containing silicone oil, 15-20 parts of hydroxystearic acid, 4-6 parts of lithium hydroxide, 45-55 parts of a PE carrier resin, 5-7 parts of color master batch, 60-70 parts of high density polyethylene, 3.4-5 parts of sepiolite fiber, 5-7 parts of silica sol, 0.3-0.4 part of an antioxidant, 0.3-0.4 part of benzotriazole, 0.3-0.5 part of a silane coupling agent a171 and a proper amount of deionized water. The silicone-cored pipe prepared by the invention is low in preparation cost, excellent in wear resistance, high in environmental load resistance, wide in application prospect and worthy of popularization, and the service life is prolonged.

Description

technical field [0001] The invention relates to the technical field of silicon core tubes, in particular to a silicon core tube with a protective effect on optical fibers and high hardness. Background technique [0002] The 21st century is the era of information, the fastest growing is the information industry, the optical cable is the most important channel in the transmission of information, because only the optical cable can transmit a large amount of information at the fastest speed, and it will not be disturbed or lost. The rapid development of China's telecommunications industry in recent years has crossed the historical development stage from cable communication to optical cable, from civilian to military, from telephone to multimedia, and has entered the era of optical fiber communication, which has also greatly promoted the plastic optical cable sheathed pipe. development of. The optical cable is usually buried underground. In order to effectively protect the optic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/05C08L23/06C08K13/04C08K7/10C08K5/3475C08K3/36C08K3/22C08K5/09
CPCC08L83/04C08L2201/08C08L2203/18C08L2205/025C08L2205/03C08L2207/062C08L23/06C08K13/04C08K7/10C08K5/3475C08K3/36C08K2003/2203C08K5/09
Inventor 黄振东
Owner 黄振东
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products