Waterborne environment-friendly membrane and preparation method thereof

An environmentally friendly, water-based technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of no surface protection layer, short service life, easy to wear, etc., to achieve consistency, improve service life, and wide application range Effect

Inactive Publication Date: 2016-12-14
镇江普优塑胶科技有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the products currently on the market, such as wood flooring, plastic flooring, wallpaper, machine casings, refrigerators, etc., do not have surface protection layers, or rarely use solvent-based protection layers. environmental protection and many other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A water-based environmental protection film made of the following raw materials: Bayer UV 4000 43g and Bayer H 7002 47g; BYK022 0.6g; Disperse 710 1.2g; TS100 4.0g and Irgacure 500 0.5g.

[0036] The preparation method comprises the following steps:

[0037] (1) Stir the resin at low speed first, and mix evenly; then add defoamer and dispersant in turn while stirring at low speed, the speed of low speed stirring is 600 rpm, and after adding, speed up stirring at 900 rpm for 12 Minutes; add matting powder after stirring evenly, and then increase the speed of stirring at 1900 rpm for 22 minutes after adding; add photoinitiator after stirring evenly, continue to stir at 1900 rpm for 12 minutes until evenly stirred, and let it stand for 8 minutes Hours later, the spray paint is formed for subsequent use;

[0038] (2) Evenly spray the spray paint onto the surface of the object to form a coating;

[0039] (3) Dry the coating at 80°C for 5 minutes to perform the first therma...

Embodiment 2

[0043] A water-based environmental protection film is made of the following raw materials:

[0044] Bayer UV 4000 48g and Bayer H 7002 52g; BYK 022 0.2g; Disperse 710 0.4g; TS100 3.0g and Irgacure 500 0.1g.

[0045] The preparation method comprises the following steps:

[0046] (1) Stir the resin at a low speed first, and mix evenly; then add the defoamer and dispersant in turn while stirring at a low speed, the speed of the low speed stirring is 400 rpm, and after the addition, speed up the stirring at 1100 rpm for 8 Minutes; after stirring evenly, add matting powder, and then increase the speed of stirring at 2100 rpm for 18 minutes after adding; after stirring evenly, add photoinitiator, continue to stir at 2100 rpm for 8 minutes until evenly stirred, and let it stand for 12 minutes Hours later, the spray paint is formed for subsequent use;

[0047] (2) Evenly spray the spray paint onto the surface of the object to form a coating;

[0048] (3) Dry the coating in a hot ai...

Embodiment 3

[0052] A water-based environmental protection film is made of the following raw materials:

[0053] Bayer UV 4000 38g and Bayer H 7002 57g; BYK 022 0.4g; Disperse 710 0.8g; TS100 3.5g and Irgacure 500 0.3g.

[0054] The preparation method comprises the following steps:

[0055] (1) Stir the resin at a low speed and mix evenly; then add the defoamer and dispersant in turn while stirring at a low speed. Minutes; after stirring evenly, add matting powder, and then increase the speed of stirring at 1000 rpm for 20 minutes after adding; after stirring evenly, add photoinitiator, continue to stir at 2000 rpm for 10 minutes until evenly stirred, and let it stand for 10 minutes Hours later, the spray paint was formed for use; at 23°C, the viscosity of the spray paint was measured to be 2500mPa.s;

[0056] (2) Evenly spray the spray paint onto the surface of the object to form a coating;

[0057] (3) Dry the coating in a hot air circulation heating oven and dry it at 100°C for 3 minut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a waterborne environment-friendly membrane and a preparation method thereof. The waterborne environment-friendly membrane is prepared through the steps that waterborne polyurethane resin, a defoaming agent, a dispersing agent and the like are taken as raw materials to be mixed and stirred to prepare a spraying material, then spraying is conducted, and finally a two-time curing method is adopted. The preparation method has the advantages that a preparation technology is relatively mature, and the stability is high; the prepared waterborne environment-friendly membrane has the advantages that the membrane is an elastic coating and can reduce damage of external force to a real object and isolate direct contact of the real object and the outside, environmental friendliness is achieved, wear resistance is high, skid resistance is achieved, the application range is wide, and the adhesive force is high.

Description

technical field [0001] The invention belongs to a membrane material preparation process, and in particular relates to a water-based environmental protection membrane and a preparation method thereof. Background technique [0002] Most of the products currently on the market, such as wood flooring, plastic flooring, wallpaper, machine casings, refrigerators, etc., do not have surface protection layers, or rarely use solvent-based protection layers. environmental protection and many other issues. Contents of the invention [0003] In order to solve the above-mentioned problems in the prior art, the present invention provides a water-based environmental protection membrane and a preparation method thereof. [0004] The technical solution adopted in the present invention is: a water-based environmental protection film, including the following raw materials in parts by weight: 90-100 parts of water-based polyurethane resin; 0.2-0.6 parts of defoaming agent; 0.4-1.2 parts of di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D7/12
CPCC09D175/04
Inventor 王政华
Owner 镇江普优塑胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap