Anti-short-circuit AGM partition plate

An anti-short circuit and separator technology, which is applied in the direction of circuits, electrical components, battery pack components, etc., can solve the problems of short circuit, penetration of fine lead powder on the plate, etc., and achieve excellent comprehensive performance, high porosity, and avoid short circuit Effect

Active Publication Date: 2016-12-28
ZHEJIANG CHANGTONG SCI & TECH
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to solve the problem that the AGM separators in the prior art easily cause short circuit caused by fine lead powder on the pole plate penetrating into the separators, and provides a scientific and reasonable formula with high porosity, uniform voids, excellent comprehensive performance, and Anti-short circuit AGM separator to effectively avoid battery short circuit

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An anti-short circuit AGM separator, made of the following raw materials in mass percentage: 4% modified nano-vermiculite powder, 4% polyethylene oxide, 7% modified bamboo fiber, 12% water-soluble polyethylene with a diameter of 2 μm and a length of 4 mm Alcohol fiber, 7% polyimide fiber with a diameter of 0.4 μm and a length of 4 mm, 32% high-alkali glass fiber with a diameter of 0.6 μm and a length of 4 mm, and the balance is high-alkali glass fiber with a diameter of 3.5 μm and a length of 3.5 mm ,in,

[0020] The modified nano vermiculite powder is prepared by the following method: adding nano vermiculite powder into dilute sulfuric acid, heating to 87°C for 4 hours, filtering, washing with deionized water until the pH is neutral, drying, calcining at 850°C and adding modified After shearing and dispersing in the liquid, shake it at 35°C for 6 hours, filter and dry to obtain the modified nano-vermiculite powder. The modified liquid is composed of the following compo...

Embodiment 2

[0023] An anti-short circuit AGM separator, made of the following raw materials in mass percentage: 5% modified nano-vermiculite powder, 5% polyethylene oxide, 10% modified bamboo fiber, 15% water-soluble polyethylene with a diameter of 3 μm and a length of 5 mm Alcohol fiber, 10% polyimide fiber with a diameter of 0.5 μm and a length of 5 mm, 35% of a high-alkali glass fiber with a diameter of 0.7 μm and a length of 5 mm, and the balance being a high-alkali glass fiber with a diameter of 4 μm and a length of 5 mm. ,

[0024] The modified nano-vermiculite powder is prepared by the following method: adding the nano-vermiculite powder into dilute sulfuric acid, heating to 90°C for 3 hours, filtering, washing with deionized water until the pH is neutral, drying, calcining at 900°C and adding modified After shearing and dispersing in the liquid, shake it at 40°C for 5 hours, filter and dry to obtain the modified nano-vermiculite powder. The modified liquid is composed of the follo...

Embodiment 3

[0027] An anti-short circuit AGM separator made of the following raw materials in mass percentage: 3% modified nano-vermiculite powder, 3% polyethylene oxide, 5% modified bamboo fiber, 10% water-soluble polyethylene with a diameter of 1 μm and a length of 3 mm Alcohol fiber, 5% polyimide fiber with a diameter of 0.3 μm and a length of 3 mm, 30% of a high-alkali glass fiber with a diameter of 0.5 μm and a length of 3 mm, and the balance being a high-alkali glass fiber with a diameter of 3 μm and a length of 3 mm. ,

[0028] The modified nano-vermiculite powder is prepared by the following method: adding the nano-vermiculite powder into dilute sulfuric acid, heating to 85°C for 5 hours, filtering, washing with deionized water until the pH is neutral, drying, calcining at 800°C and adding modified After shearing and dispersing in the liquid, shake it at 30°C for 7 hours, filter and dry to obtain the modified nano-vermiculite powder. The modified liquid is composed of the following ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-short-circuit AGM partition plate. The anti-short-circuit AGM partition plate is prepared from, by mass, 3%-5% of modified nano-vermiculite powder, 3%-5% of polyoxyethylene, 5%-10% of modified bamboo fibers, 10%-15% of water-soluble polyvinyl alcohol fibers, 5%-10% of polyimide fibers, 30%-35% of high-alkali glass fibers with the diameter ranging from 0.5 micrometer to 0.7 micrometer and the balance high-alkali glass fibers with the diameter ranging from 3 micrometers to 4 micrometers. According to the anti-short-circuit AGM partition plate, a traditional pure glass fiber formula is abandoned, the plate is creatively woven by multiple fibers in a blending mode, the modified bamboo fibers and the polyimide fibers are creatively added especially, the components such as the nano-vermiculite powder and polyoxyethylene are added to serve as auxiliary materials, therefore, the partition plate is high in porosity and uniform in pore, the comprehensive performance is excellent, and the condition that positive electrode lead powder penetrates through the partition plate to a negative electrode to cause a short circuit can be effectively avoided.

Description

technical field [0001] The invention relates to an AGM separator, in particular to an anti-short circuit AGM separator. Background technique [0002] Glass microfiber separator (AGM) is one of the key materials of valve-regulated lead-acid batteries. The main functions of AGM separators for valve-regulated lead-acid batteries are: (1) to prevent positive / negative plates from contacting each other and causing internal damage to the battery. short circuit; (2) make the battery tightly assembled and reduce the battery volume; (3) prevent the plate from being deformed, bent and active material from falling off; (4) store a necessary amount of electrolyte in the porous separator between the plates to To ensure high conductivity and the need for battery reaction; (5) to prevent some substances harmful to the battery from migrating and diffusing through the separator. Therefore, the AGM separator is called the third electrode of the valve-regulated lead-acid battery. [0003] At ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M2/16H01M50/44
CPCH01M50/431H01M50/44H01M50/446H01M50/411Y02E60/10
Inventor 陈连强黄建忠郑书根应志超
Owner ZHEJIANG CHANGTONG SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com