Frost resistance paint applied in ceramics

A technology for ceramic handicrafts and antifreeze coatings, applied in the direction of coating, etc., can solve problems such as deformation, discoloration, and affecting the appearance of ceramic handicrafts, and achieve the effect of simple preparation process, good quality, and good antifreeze performance

Inactive Publication Date: 2017-01-04
安徽省恒益工艺品有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Handicrafts are mainly divided into ceramic handicrafts, resin handicrafts, iron handicrafts and plastic handicrafts, etc. Among them, ceramic handicrafts are widely used. Ceramic handicrafts are usually coated with 10% paint before leaving the factory. Discoloration or slight deformation is prone to occur in winter, which seriously affects the appearance of ceramic crafts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] An antifreeze coating for ceramic handicrafts, the antifreeze coating consists of the following components by weight: 70 parts of resin, 11 parts of methyl methacrylate, 5 parts of sodium hexametaphosphate, 3 parts of glyceryl monostearate 7 parts of octadecyl stearic acid, 11 parts of ethyl acetate, 3 parts of hydroxypropyl methylcellulose, 20 parts of zeolite, 9 parts of cresol, 1 part of inorganic aluminum salt water repellent, 12 parts of pigment and 18 parts of water share.

[0014] Described water type is deionized water.

[0015] The type of resin is polyvinyl alcohol resin.

Embodiment 2

[0017] An antifreeze coating for ceramic handicrafts, the antifreeze coating consists of the following components by weight: 80 parts of resin, 13 parts of methyl methacrylate, 6 parts of sodium hexametaphosphate, 4 parts of glyceryl monostearate 8 parts of octadecyl stearic acid, 12 parts of ethyl acetate, 4 parts of hydroxypropyl methylcellulose, 25 parts of zeolite, 11 parts of cresol, 2 parts of inorganic aluminum salt water repellent, 14 parts of pigment and 19 parts of water share.

[0018] Described water type is deionized water.

[0019] The type of resin is polyvinyl alcohol resin.

Embodiment 3

[0021] An antifreeze coating for ceramic handicrafts, the antifreeze coating consists of the following components in parts by weight: 90 parts of resin, 15 parts of methyl methacrylate, 7 parts of sodium hexametaphosphate, 5 parts of glyceryl monostearate 9 parts of octadecyl stearic acid, 13 parts of ethyl acetate, 6 parts of hydroxypropyl methylcellulose, 30 parts of zeolite, 13 parts of cresol, 4 parts of inorganic aluminum salt water repellent, 17 parts of pigment and 20 parts of water share.

[0022] Described water type is deionized water.

[0023] The type of resin is polyvinyl alcohol resin.

[0024] The antifreeze coatings prepared through implementation 1, implementation 2 and implementation 3, compared with the common coatings in the prior art, the antifreeze coatings prepared by the present invention through the examples have less preparation components, simple preparation process and good antifreeze performance After the antifreeze paint prepared by the present ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to frost resistance paint applied in ceramics. The components of the frost resistance paint include, by weight, 70-90 parts of resin, 11-15 parts of methylmethacrylate, 5-7 parts of hexameta, 3-5 parts of Monostearin, 7-9 parts of eighteen carbon stearic acid, 11-13 parts of ethyl acetate, 3-6 parts of HCMC, 20-30 parts of zeolite, 9-13 parts of cresols, 1-4 parts of inorganic Aluminum Salt Waterproof Agent, 12-17 parts of pigment and 18-20 parts of water. The invention getting frost resistance paint by the preparing method above is characterized by less preparation components, simple preparation process and good antifreeze properties. After coating the frost resistance paint from the invention on the ceramics, the surface of the ceramics will not be discolored or cracked in the cold winter for the frost resistance paint has good quality and stable property.

Description

technical field [0001] The invention relates to a coating, in particular to an antifreeze coating for ceramic handicrafts. Background technique [0002] Handicrafts, that is, products made by processing raw materials and semi-finished products by hand or machine, are a general term for a group of valuable artworks. Handicrafts come from life, but they create a value higher than life; it is the crystallization of people's wisdom, fully It embodies the creativity and artistry of human beings and is a priceless treasure of human beings. [0003] Handicrafts are mainly divided into ceramic handicrafts, resin handicrafts, iron handicrafts and plastic handicrafts, etc. Among them, ceramic handicrafts are widely used. Ceramic handicrafts are usually coated with 10% paint before leaving the factory. Discoloration or slight deformation is prone to occur in winter, which seriously affects the appearance of ceramic handicrafts. Contents of the invention [0004] In view of the abov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/12
CPCC09D4/06
Inventor 叶邦生
Owner 安徽省恒益工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com