A technology of non-fired bricks and thermal insulation materials, applied in the field of building materials, can solve the problems of restricting the promotion and use of thermal insulation bricks, poor adhesion of thermal insulation bricks, and poor adhesion, and achieve the effects of increasing strength, saving resources, and protecting the environment

Inactive Publication Date: 2017-01-18
岳佐星
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the popularization and application of insulation bricks, the poor adhesion and low strength of insulation bricks have gradually become common problems in the field of building materials, which further limits the promotion and use of insul

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preparation method for thermal insulation unburned bricks, comprising the steps of:

[0027] (1) Pre-mixing

[0028] Mix coal gangue, steel slag, gasification slag, and boiler slag according to a certain mass ratio, add water and stir until uniformly mixed, and add CaO, Na 2 SO 4 As an activator, the gangue accounts for 50 parts by weight, 10 parts by weight of steel slag, 20 parts by weight of gasification slag, 15 parts by weight of boiler slag, and the CaO, Na 2 SO 4 content of 8% and 24% respectively;

[0029] (2) aging

[0030] Place the pre-stirred mixture in a steam curing room at 70°C for 2 hours;

[0031] (3) Secondary stirring

[0032] The aged material is then added cement with a certain proportioning quality, and water is added to stir evenly, and the cement is 10 parts by weight;

[0033] (4) Forming

[0034] Put the mixed material after the secondary stirring into a mold and place it on a vibrating table with a vibration frequency of 60 times / min...

Embodiment 2

[0040] A preparation method for thermal insulation unburned bricks, comprising the steps of:

[0041] (1) Pre-mixing

[0042] Mix coal gangue, steel slag, gasification slag, and boiler slag according to a certain mass ratio, add water and stir until uniformly mixed, and add CaO, Na 2 SO 4 As an activator, the coal gangue accounts for 55 parts by weight, 15 parts by weight of steel slag, 25 parts by weight of gasification slag, and 20 parts by weight of boiler slag. The CaO, Na 2 SO 4 content of 9% and 3% respectively;

[0043] (2) aging

[0044] Place the pre-stirred mixture in a steam curing room at 75°C for 3 hours;

[0045] (3) Secondary stirring

[0046] Add cement of certain proportioning quality to the material after aging, add water and stir evenly, and the cement is 15 parts by weight;

[0047] (4) Forming

[0048] Put the mixed material after the secondary stirring into a mold and place it on a vibrating table with a vibration frequency of 60 times / min, and vi...

Embodiment 3

[0054] A preparation method for thermal insulation unburned bricks, comprising the steps of:

[0055] (1) Pre-mixing

[0056] Mix coal gangue, steel slag, gasification slag, and boiler slag according to a certain mass ratio, add water and stir until uniformly mixed, and add CaO, Na 2 SO 4 As an activator, the coal gangue accounts for 0 parts by weight, 20 parts by weight of steel slag, 30 parts by weight of gasification slag, 25 parts by weight of boiler slag, and the CaO, Na 2 SO 4 content of 10% and 4% respectively;

[0057] (2) aging

[0058] Place the pre-stirred mixture in a steam curing room at 80°C for 4 hours;

[0059] (3) Secondary stirring

[0060] Add cement of a certain proportioning quality to the aged material, add water and stir evenly, and the cement is 20 parts by weight;

[0061] (4) Forming

[0062] Put the mixed material after the secondary stirring into a mold and place it on a vibrating table with a vibration frequency of 60 times / min, and vibrate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of an insulating baking-free brick. The preparation method comprises the following steps: (1) premixing: adding water into raw materials including gangue, steel slag, gasification slag and boiler slag according to a certain mass ratio and stirring until the materials are uniformly mixed; (2) aging; (3) moulding; (4) press-fitting; (5) steam curing; and premixing and adding CaO and Na2SO4 as excitant, and adding a binder into a heat-insulation layer. By the preparation method, strength of the insulating brick is greatly enhanced; and gangue and steel slag, etc. are changed from waste into valuable things so as to save resources and protect the environment. The preparation method of the invention is simple and feasible, and is easy to realize. Strength of the brick prepared by the method is 3 times higher than strength of a common brick. The brick of the invention has huge market potential and wide prospect.

Description

technical field [0001] The invention belongs to the field of building materials, and more specifically, the invention relates to a method for preparing heat-retaining unburned bricks. Background technique [0002] With the popularization and application of thermal insulation bricks, the poor cohesion and low strength of thermal insulation bricks have gradually become a common problem in the field of building materials, which further limits the promotion and use of thermal insulation bricks. The currently used insulation bricks are common, with high cost, poor adhesion, and strength defects. Therefore, it is a social development trend to develop an insulation brick with high strength, strong adhesion, and low cost. Contents of the invention [0003] The problem to be solved by the present invention is to provide a method for preparing heat-retaining non-burning bricks. [0004] In order to achieve the above object, the technical scheme that the present invention takes is: ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00B28B1/087B28B1/00
CPCC04B28/00B28B1/002B28B1/0873C04B2201/50C04B18/12C04B18/142C04B18/06C04B18/10C04B22/064C04B22/147
Inventor 岳佐星
Owner 岳佐星
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap