A kind of preparation method of chitosan fabric based on graphene foam modification

A technology of graphene foam and chitosan, applied in the field of textile materials, can solve the problems of difficult dispersion and easy polymerization of graphene, difficulty in controlling the amount of graphene, difficulty in uniform dispersion and quantification, etc., to achieve excellent nano-characteristics, unique biological activity and Physiological function, performance and stable effect

Active Publication Date: 2018-08-10
青岛莫特斯家居用品有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to the above-mentioned prior art, the application of graphene in textiles is mostly attached to the surface of the fiber in the form of a film, or blended with a mixture to form a fiber, but the problem of difficult dispersion and easy polymerization of graphene will make it difficult to control graphene in the fiber. Difficult to evenly disperse and quantify for internal and surface dosage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) The chitosan fiber and the chitosan oligosaccharide fiber are blended at a ratio of 60:40 to form a blended yarn of 16.7 tex. The blended yarn is immersed in a mass fraction of 25% with a bath ratio of 1:40. In the isopropanol aqueous solution of chloro-2-hydroxypropyl trimethyl ammonium chloride, the pH value is 8, heating and stirring at 60 ℃ for 30 minutes, fully washing with ethanol, and drying to obtain quaternary ammonium salt modified chitosan Blended fiber with Chitooligosaccharide. The quaternary ammonium salt-modified chitosan and chitosan oligosaccharide blended fiber is used as the raw material, and the chitosan woven fabric is formed by weaving.

[0024] (2) Adding hydrazine hydrate, nano titanium dioxide and sodium dodecylbenzene sulfonate into the aqueous solution and fully stirring to form a finishing solution, wherein the mass fraction of hydrazine hydrate is 15%, and the mass fraction of nano titanium dioxide is 5%.

[0025] (3) The chitosan fabric is ...

Embodiment 2

[0027] (1) The chitosan fiber and the chitosan oligosaccharide fiber are blended at a ratio of 80:20 to form a 20.4tex blended yarn. The blended yarn is immersed in a mass fraction of 30% with a bath ratio of 1:50. In the isopropanol aqueous solution of chloro-2-hydroxypropyl trimethyl ammonium chloride, the pH value is 8.5, heated and stirred at 80°C for 30 minutes, washed thoroughly with ethanol, and dried to obtain quaternary ammonium salt modified chitosan Blended fiber with Chitooligosaccharide. The quaternary ammonium salt-modified chitosan and chitosan oligosaccharide blended fiber is used as a raw material and woven to form a chitosan non-woven fabric.

[0028] (2) Adding hydrazine hydrate, nano titanium dioxide and sodium dodecylbenzene sulfonate into the aqueous solution and fully stirring to form a finishing solution, wherein the mass fraction of hydrazine hydrate is 20% and the mass fraction of nano titanium dioxide is 10%.

[0029] (3) The chitosan fabric is immersed ...

Embodiment 3

[0031] (1) The chitosan fiber and the chitosan oligosaccharide fiber are blended at a ratio of 70:30 to form a 18.2tex blended yarn. The blended yarn is immersed in a mass fraction of 28% with a bath ratio of 1:45. In the isopropanol aqueous solution of chloro-2-hydroxypropyl trimethyl ammonium chloride, the pH value is 8.2, heated and stirred at 70°C for 30 minutes, washed with ethanol, and dried to obtain quaternary ammonium salt modified chitosan Blended fiber with Chitooligosaccharide. The quaternary ammonium salt-modified chitosan and chitosan oligosaccharide blended fiber is used as the raw material, and the chitosan knitted fabric is formed by weaving.

[0032] (2) Adding hydrazine hydrate, nano titanium dioxide and sodium dodecylbenzene sulfonate into the aqueous solution and fully stirring to form a finishing solution, wherein the mass fraction of hydrazine hydrate is 18%, and the mass fraction of nano titanium dioxide is 8%.

[0033] (3) The chitosan fabric is immersed i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a chitosan fabric based on graphene foam modification. The preparation method comprises the following steps: blending chitosan fibers and chitooligo saccharide fibers to form blended yarns, soaking the blended yarns into a solution with 3-chlorine-2-hydroxypropyl trimethyl ammonium chloride, performing heating stirring and ethanol washing, and drying to obtain quaternary ammonium salt modified chitosan and chitooligo saccharide blended fibers; weaving the quaternary ammonium salt modified chitosan and chitooligo saccharide blended fibers serving as a raw material to prepare the chitosan fabric; soaking the chitosan fabric into a graphene oxide solution, oscillating, taking out, drying and curing the fabric, then soaking the fabric in finishing liquid with a reducing agent and nanometer titania, performing heating reaction, taking out the fabric, drying in vacuum, washing to remove substances which are combined to the surface loosely, and drying to obtain the chitosan fabric based on graphene foam modification.

Description

Technical field [0001] The invention belongs to the technical field of textile materials, and specifically relates to a preparation method of a chitosan fabric modified based on graphene foam. Background technique [0002] With the increase of people's health and health awareness, multifunctional green fabrics are more and more popular among consumers. Polysaccharide is a natural polymer compound. Chitin is a natural polysaccharide extracted from the shells of shrimps and crabs and fungal agent algae cell walls. Chitosan is deacetylated chitin. Chitosan has high biological activity. Chitooligosaccharides are also known as chitosan. Chitosan is a chitosan with a low degree of polymerization. With the decrease of molecular weight, chitosan has some characteristics of chitosan, but also shows more excellent water solubility. The development of fabric products based on chitosan and its derivatives has many properties, such as moisture absorption and water-locking properties, antibac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M11/74D06M11/46D06M13/463D06M13/256D02G3/04D06M101/10D06M101/04
CPCD02G3/042D06M11/46D06M11/74D06M13/256D06M13/463D06M2101/04D06M2101/10D06M2200/25D10B2201/01D10B2211/01
Inventor 王文庆
Owner 青岛莫特斯家居用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com