Environment-friendly all-purpose adhesive

A kind of universal glue, environmental protection technology, applied in the field of universal glue, can solve the problems of harming the body, shrinking market, polluting the environment, etc.

Inactive Publication Date: 2017-02-08
无锡万能胶粘剂有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The chloroprene-type universal glue used in traditional decoration contains toxic solvents such as toluene, which pollutes the environment and harms the body. Therefore, as people's environmental protection requirements become increasingly strict, its market will gradually shrink.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] An environment-friendly universal adhesive, which is made of the following components: polybutadiene liquid rubber, dimethyl carbonate, polyacrylate / nano-SiO with a particle size of 200nm 2 Composite particles, 2-(4-bromomethylphenyl) ethyl propionate, 3-(2-pyridylamino) ethyl propionate and bisbenzylisoquinoline betaine, the weight content of each component is: 53 parts of polybutadiene liquid rubber, 30 parts of dimethyl carbonate, polyacrylate / nano-SiO with a particle size of 200nm 2 20 parts of composite particles, 42 parts of ethyl 2-(4-bromomethylphenyl)propionate, 28 parts of ethyl 3-(2-pyridylamino)propionate and 20 parts of bisbenzylisoquinoline betaine.

Embodiment 2

[0014] An environment-friendly universal adhesive, which is made of the following components: polybutadiene liquid rubber, dimethyl carbonate, polyacrylate / nano-SiO with a particle size of 300nm 2 Composite particles, 2-(4-bromomethylphenyl) ethyl propionate, 3-(2-pyridylamino) ethyl propionate and bisbenzylisoquinoline betaine, the weight content of each component is: 45 parts of polybutadiene liquid rubber, 200 parts of dimethyl carbonate, polyacrylate / nano-SiO with a particle size of 300nm 2 15 parts of composite particles, 35 parts of ethyl 2-(4-bromomethylphenyl)propionate, 20 parts of ethyl 3-(2-pyridylamino)propionate and 15 parts of bisbenzylisoquinoline betaine.

Embodiment 3

[0016] An environment-friendly universal adhesive, which is made of the following components: polybutadiene liquid rubber, dimethyl carbonate, polyacrylate / nano-SiO with a particle size of 250nm 2 Composite particles, 2-(4-bromomethylphenyl) ethyl propionate, 3-(2-pyridylamino) ethyl propionate and bisbenzylisoquinoline betaine, the weight content of each component is: 60 parts of polybutadiene liquid rubber, 40 parts of dimethyl carbonate, polyacrylate / nanometer SiO with a particle size of 250nm 2 25 parts of composite particles, 50 parts of ethyl 2-(4-bromomethylphenyl)propionate, 35 parts of ethyl 3-(2-pyridylamino)propionate and 25 parts of bisbenzylisoquinoline betaine.

[0017] The beneficial effect of the environment-friendly universal glue of the invention is that the invention is environment-friendly and safe, neither pollutes the environment nor harms the body.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly all-purpose adhesive. The all-purpose adhesive is prepared from the following components (by weight): 45-60 parts of polybutadiene liquid rubber, 20-40 parts of dimethyl carbonate, 10-30 parts of polyacrylate / nano-SiO2 composite particles, 35-50 parts of 2-(4-bromomethylphenyl)ethyl propionate, 20-35 parts of 3-(2-pyridineamino)ethyl propionate and 10-28 parts of bisbenzylisoquinoline betaine. Through the above mode, the all-purpose adhesive is environment-friendly and safe, will not pollute the environment and will not harm human body.

Description

technical field [0001] The invention relates to the field of universal glue, in particular to an environment-friendly universal glue. Background technique [0002] All-purpose adhesive is a kind of adhesive with super strong adhesion, which is widely used, such as self-bonding of rubber, leather, fabric, cardboard, wood-based panel, wood, foam plastic, ceramics, concrete, metal, etc. Or stick to each other. Mainly used for, leather, fabric, cardboard, wood-based panel, wood, foam plastic, ceramic, concrete, metal, etc. Suitable for bonding with each other such as PP, PE, TPR, PET, ABS, PS, finish, glass, wood, etc. [0003] The neoprene-type universal glue used for traditional decoration contains toxic solvents such as toluene, which not only pollutes the environment, but also harms the body. Therefore, as people's environmental protection requirements become increasingly strict, its market will gradually shrink. Contents of the invention [0004] The technical problem ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J109/00C09J11/04C09J11/06C09J11/08
CPCC09J109/00C08K2201/011C09J11/04C09J11/06C09J11/08C08L33/04C08K13/02C08K3/36C08K5/109C08K5/101C08K5/3432