A 3D lens, polarized lens technology, applied in the field of polarized 3D lenses, can solve the problem of no polarized light, unable to protect the eyes, etc., to achieve the effect of preventing damage and broad market application prospects

Inactive Publication Date: 2017-02-15
DONGXING HUAHONG OPTICAL TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In recent years, with the popularity of 3D movies, 3D lenses have ushered in a leapfrog development. The market prospect of 3D lenses is broad, but the existing 3D lenses generally have no polarizing effect. For some scenes with high light intensity, It cannot protect the eyes, so it is necessary to invent a polarized 3D lens

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polarized light 3D eyeglass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A kind of polarized 3D lens, in 3D lens 1, doped with nanometer metal particles, is coated with a layer of zirconium dioxide film 2 on the outer layer of 3D lens 1, is coated with a layer of SFM film 3 in the inner layer of 3D lens 1; The particle diameter of the nano metal particles is 35nm, which is a mixture of copper oxide and iron oxide, and the mixing ratio of cobalt oxide and nickel oxide is 1:1.

[0013] The nanometer metal particles account for 0.25% of the total weight of the nanocomposite polarizing lens.

Embodiment 2

[0015] A kind of polarizing 3D lens, in 3D lens 1 doped with nano metal particles, on the outer layer of 3D lens is coated with a layer of zirconium dioxide film 2, in the inner layer of 3D lens 1 is coated with a layer of SFM film 3; The particle size of the metal particles is 40nm, which is a mixture of copper oxide and iron oxide, and the mixing ratio of cobalt oxide and nickel oxide is 1:1.

[0016] The nanometer metal particles account for 0.40% of the total weight of the nanocomposite polarizing lens.

Embodiment 3

[0018] A kind of polarized 3D lens, in 3D lens 1, doped with nanometer metal particles, is coated with a layer of zirconium dioxide film 2 on the outer layer of 3D lens 1, is coated with a layer of SFM film 3 in the inner layer of 3D lens 1; The particle diameter of the nano metal particles is 45nm, which is a mixture of copper oxide and iron oxide, and the mixing ratio of cobalt oxide and nickel oxide is 1:1.

[0019] The nanometer metal particles account for 0.55% of the total weight of the nanocomposite polarizing lens.

[0020] Embodiment 2 is the best embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention discloses a polarized light 3D eyeglass, belonging to the polarized light eyeglass field. Nano-metal particles are mixed in the 3D eyeglass, the outer layer of the 3D eyeglass is coated with one layer of zirconium dioxide film, and the inner layer of the 3D eyeglass is coated with one layer of SFM film; and the particle sizes of the nano-metal particles are 35-45nm, the nano-metal particles are the nano-metal mixture of the copper oxide and the iron oxide, and the mixing proportion of the cobaltous oxide and the nickel oxide is 1:1. The polarized light 3D eyeglass can effectively prevent eyes from being damaged by hard light and has a wide market application prospect.

Description

technical field [0001] The invention relates to a polarized lens, in particular to a polarized 3D lens. Background technique [0002] In recent years, with the popularity of 3D movies, 3D lenses have ushered in a leapfrog development. The market prospect of 3D lenses is broad, but the existing 3D lenses generally have no polarizing effect. For some scenes with high light intensity, Can't play the effect of protecting eyes, therefore it is necessary to invent a kind of polarizing 3D lens. Contents of the invention [0003] In order to solve the above technical problems, the present invention aims to provide a nanocomposite polarizer. [0004] Technical scheme of the present invention: [0005] A kind of polarizing 3D lens, in 3D lens, doped nanometer metal particle, is coated with a layer of zirconium dioxide film on the outer layer of 3D lens, is coated with a layer of SFM film in the inner layer of 3D lens; The diameter is 35-45nm, which is a mixture of copper oxide an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02B5/30G02B27/26G02B30/25
CPCG02B5/3041G02B30/25
Inventor 刘德兴
Owner DONGXING HUAHONG OPTICAL TECH