Metal corrosion inhibitor and preparation method thereof

A technology of metal corrosion inhibitor and sodium tungstate, which is applied in the field of metal corrosion inhibition, can solve the problems of paint foaming, poor paint compatibility, and peeling, and achieve good antirust performance, good oil removal ability, and avoid re-rusting Effect

Inactive Publication Date: 2017-03-15
HUNAN JINYU CHEM
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Generally, metal corrosion inhibitors or antirust agents on the market can also be used for antirust treatment, but they are not compatible with paint. Spraying paint directly without washing after antirust treatment will cause paint blistering and peeling off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 8-12

[0027] The composition of table 2 embodiment 8-12 and comparative example 1-3 metal corrosion inhibitor

[0028] Example 8 9 10 11 12 Comparative example 1 Comparative example 2 Comparative example 3 Sodium Tungstate 20 20 20 22 22 10 22 - Sodium molybdate - - - - - - - 22 Ethylene glycol 60 45 55 55 50 50 50 50 ethanol 10 10 10 10 10 10 10 10 ammonium citrate 5 5 5 5 5 5 5 5 Zirconium Carbonate 55 50 50 50 50 50 30 50 water 295 290 295 305 300 300 300 300

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a metal corrosion inhibitor. The metal corrosion inhibitor is prepared from the following raw materials in parts by weight: 15 to 25 parts of sodium tungstate, 40 to 60 parts of ethylene glycol, 7 to 15 parts of ethyl alcohol, 4 to 9 parts of ammonium citrate, 40 to 60 parts of zirconium carbonate, and 250 to 350 parts of water. A preparation method comprises the following steps of adding water into a glass container, adding the sodium tungstate to stir for dissolving, sequentially adding the ethylene glycol, the ethyl alcohol, the ammonium citrate and the zirconium carbonate, stirring, and dissolving, so as to obtain the metal corrosion inhibitor. The metal corrosion inhibitor has the advantages that water washing after use is not needed, paint can be directly painted, the foaming, falling and the like of the paint are avoided, and the adhesion force of a paint film reaches level 0.

Description

technical field [0001] The invention belongs to the technical field of metal corrosion inhibition, and in particular relates to a metal corrosion inhibitor and a preparation method thereof. Background technique [0002] General construction machinery parts must be cleaned and then painted before assembly. The heavy oil and heavy dirt on the surface of these parts are dry and hard to remove. At this time, general construction machinery manufacturers use shot peening and sand blasting to remove the grease on the surface, and then use special metal corrosion inhibitors for degreasing and antirust treatment, without washing, and spray paint directly after drying. [0003] Generally, metal corrosion inhibitors or antirust agents on the market can also be used for antirust treatment, but their compatibility with paint is poor. Spraying paint directly without washing after antirust treatment will cause the paint to foam and fall off. Contents of the invention [0004] One of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23F11/18
CPCC23F11/187
Inventor 桂成方桂林刘春花
Owner HUNAN JINYU CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products