Optical glass
A kind of optical glass and glass technology, applied in the field of glass prefabricated parts and optical components, can solve the problems of high density, lower imaging quality, expensive raw materials, etc., and achieve the effect of low density, good transmittance, and no crystallization in transmittance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment
[0083] The present invention is explained using the following examples, but the present invention should not be limited to these examples.
[0084] [Optical glass example]
[0085] First, in order to obtain glass No.1-20 with the composition shown in Table 1-Table 3, carbonate, nitrate, sulfate, hydroxide, oxide, boric acid, etc. The raw materials are weighed in proportion, and mixed thoroughly to form a blended raw material. The blended raw material is put into a platinum crucible, heated to 1250-1450 ° C, and clarified and stirred for 3 to 5 hours to become a uniform molten glass. , then pour the molten glass into a preheated mold and keep it at 650-700° C. for 2-4 hours and then slowly cool it to obtain the optical glasses No.1-20 in the following Tables 1-3.
[0086]Moreover, the characteristic of each glass was measured by the method shown below, and the measurement result is shown in Table 1-Table 3.
[0087] (1) Refractive index (nd) and Abbe number (νd)
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com