Multifunctional SSF/B type polyester finishing agent and preparation method thereof

A multifunctional, finishing agent technology, applied in the direction of anti-staining/anti-fouling fibers, improved hand fibers, etc., can solve the problems of not meeting other functions, single performance, containing chemical components, etc.

Inactive Publication Date: 2017-03-29
江苏海云花新材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the performance of textiles directly affects people's quality of life. Textiles will be exposed to various chemicals during the production and processing process, especially after finishing processing will use a wide variety of finishing agents. Finishing is to improve product grade and added value. However, som

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional SSF/B type polyester finishing agent and preparation method thereof
  • Multifunctional SSF/B type polyester finishing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method of SSF / B type polyester multifunctional finishing agent, which is characterized in that it comprises the following steps:

[0031] 1. Add 450kg polyethylene glycol and 100kg triethylene glycol into a 1500L stainless steel reactor with stirring and mechanical seal, start stirring, slowly heat up to 98°C, turn on vacuum, and control the vacuum degree at -0.086MPa Dehydrate for 1 hour, then cool down to 60°C;

[0032] 2. Then add 240kg of methyl phthalate, 70kg of toluene, and 6kg of calcium acetate catalyst respectively, start stirring, heat up, the temperature rises to 105°C, and prepolymerizes for 3 hours; continue to heat up to 135°C, and the vacuum degree is controlled at - Distill for 4 hours under the condition of 0.095MPa, so that part of the remaining triethylene glycol can be fully removed, and the recovered alcohol can be reused;

[0033] 3. After the distillation is completed, continue to heat up to 230°C, turn on the vacuum, and control t...

Embodiment 2

[0036] A preparation method of SSF / B type polyester multifunctional finishing agent, which is characterized in that it comprises the following steps:

[0037] 1. Add 650kg polyethylene glycol and 150kg triethylene glycol into a 1500L stainless steel reactor with stirring and mechanical seal, start stirring, slowly heat up to 96°C, turn on vacuum, and control the vacuum degree at -0.088MPa Dehydrate for 1 hour, then cool down to 60°C;

[0038] 2. Then add 350kg of methyl phthalate, 100kg of toluene, and 8kg of calcium lactate catalyst respectively, start stirring, heat up, the temperature rises to 110°C, and prepolymerizes for 3.5 hours; continue to heat up to 140°C, and the vacuum degree is controlled at - Distill for 3.5 hours under the condition of 0.096MPa, so that part of the remaining triethylene glycol can be fully removed, and the recovered alcohol can be reused;

[0039] 3. After the distillation is completed, continue to heat up to 240°C, turn on the vacuum, and cont...

Embodiment 3

[0042] A preparation method of SSF / B type polyester multifunctional finishing agent, which is characterized in that it comprises the following steps:

[0043] 1. Add 500kg polyethylene glycol and 120kg triethylene glycol into a 1500L stainless steel reactor with stirring and mechanical seal, start stirring, slowly heat up to 101°C, turn on vacuum, and control the vacuum degree at -0.087MPa Dehydrate for 1 hour, then cool down to 60°C;

[0044] 2. Then add 300kg of methyl phthalate, 80kg of toluene, and 9kg of calcium gluconate catalyst respectively, start stirring, heat up, the temperature rises to 112°C, and prepolymerizes for 4 hours; continue to heat up to 130°C, and the vacuum degree is controlled at - Distill for 3 hours under the condition of 0.095MPa, so that part of the remaining triethylene glycol can be fully removed, and the recovered alcohol can be reused;

[0045] 3. After the distillation is completed, continue to heat up to 235°C, turn on the vacuum, and contro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a multifunctional SSF/B type polyester finishing agent and a preparation method thereof. The finishing agent is prepared from, by weight, 30-65 parts of polyethylene glycol, 5-15 parts of triethylene glycol, 13-35 parts of methyl phthalate, 3-10 parts of methylbenzene and 0.1-1 part of a calcium salt catalyst. The preparation method includes steps of material preparation, dewatering, pre-polymerization reaction, negative-pressure dealcoholization, polymerization reaction, flaking and packaging. The finishing agent has a modification effect on polyester fiber materials, and the modified polyester fiber materials have great moisture absorption and sweat release performances and have advantages of high fluffiness, coziness, softness, antistatic performance, smoothness, hydrophilcity, easiness in decontamination and the like. In addition, the finishing agent is also applicable to functional finishing of chemical fiber yarns and fabrics of polyamide fibers and the like.

Description

technical field [0001] The invention relates to the technical field of post-processing of textiles, in particular to an SSF / B type polyester multifunctional finishing agent and a preparation method thereof. Background technique [0002] Finishing agent is to endow textiles with excellent use, safety, appearance and other properties in order to meet some special requirements of textiles. Since the functional finishing of textiles is aimed at certain specific properties of textiles, it has strong purpose and good effect. The value is also high. After the textiles are functionally finished, their purpose and scope of use are clear, and they are very popular among consumers. [0003] With the development of social economy and the improvement of people's living standards, people pay more attention to the most basic elements of life, such as clothing, food, housing and transportation. Among them, the performance of textiles directly affects people's quality of life. Textiles will...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/507C08G63/672D06M101/32
CPCD06M15/507C08G63/672D06M2101/32D06M2200/01D06M2200/50
Inventor 瞿运丁祥祥
Owner 江苏海云花新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap