Washing-resistant agent for polyester fiber and preparation method thereof

A polyester fiber and detergent-resistant technology, which is applied in the field of detergent and its preparation, can solve the problems of easy static electricity, fluffy softness of polyester fiber, moisture absorption and sweat-wicking antistatic performance, poor decontamination performance, and taking To solve the problems of poor durability, achieve the effect of excellent washability, good fluffy and soft feeling

Active Publication Date: 2015-08-05
DUPLUS CHEM OF ZHANGJIAGANG CITY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As we all know, polyester fiber is poor in fluffy softness, moisture absorption and perspiration, antistatic performance, and easy decontamination performance.
Therefore, the textiles processed with polyester fibers have poor wearability and are prone to static electricity, which has caused certain harm to the health of the human body. Although the modified agent can also modify polyester fibers, it will become invalid after 5 to 10 times of washing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Washing-resistant agent for polyester fiber and preparation method thereof
  • Washing-resistant agent for polyester fiber and preparation method thereof
  • Washing-resistant agent for polyester fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] 1) Weigh 800 grams of polyethylene glycol, 150 grams of ethylene glycol, 180 grams of dimethyl terephthalate, 800 grams of polyamide, and 10 grams of magnesium acetate;

[0016] 2) Put the above materials into the reaction kettle, raise the temperature to 140°C and keep it for 190 minutes, continue to raise the temperature to 220°C and keep it for 70 minutes, then carry out the polymerization reaction at a vacuum degree of -0.08MP and a temperature of 230°C to generate a number average molecular weight of 5000~ The block copolymer of polyester polyether polyamide of 6000 is cooled to 190°C and discharged to obtain the finished product.

Embodiment 2

[0018] l) Weigh 900 grams of polyethylene glycol, 140 grams of ethylene glycol, 170 grams of dimethyl terephthalate, 700 grams of polyamide, and 7 grams of zinc acetate;

[0019] 2) Put the above materials into the reactor, raise the temperature to 150°C and keep it for 160 minutes, continue to raise the temperature to 210°C and keep it for 60 minutes, then carry out the polymerization reaction at a vacuum degree of -0.08MP and a temperature of 240°C to generate a number average molecular weight of 8000~ 9000 block copolymer of polyester polyether polyamide, after cooling down to 200°C, discharge the material to obtain the finished product.

Embodiment 3

[0021] l) Weigh 700 grams of polyethylene glycol, 160 grams of ethylene glycol, 190 grams of dimethyl terephthalate, 900 grams of polyamide, and 8 grams of calcium acetate;

[0022] 2) Put the above materials into the reaction kettle, raise the temperature to 180°C and keep it for 180 minutes, continue to raise the temperature to 210°C and keep it for 60 minutes, then carry out the polymerization reaction at a vacuum degree of -0.09MP and a temperature of 280°C to generate a number average molecular weight of 14000~ The block copolymer of polyester polyether polyamide of 15000 is cooled to 200°C and discharged to obtain the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a washing-resistant agent used for polyester fiber, and a preparation method thereof. The washing-resistant agent comprises the components of, by weight: 60-160 parts of polyethylene glycol, 13-40 parts of glycol, 14-26 parts of dimethyl terephthalate, 15-100 parts of polyamide, and 0.2-1 parts of metal acetate as a catalyst. The washing-resistant agent provided by the invention can be used for modifying polyester fiber. Modified polyester fiber has fluffy and soft texture, antistatic property, hydrophilic smoothness, and the like. The modification agent has excellent washing resistance, and does not fail for at least 30 times of washing.

Description

technical field [0001] The invention relates to a washing-resistant agent for polyester fibers and a preparation method thereof. Background technique [0002] As we all know, polyester fiber has poor fluffy softness, moisture absorption and perspiration, antistatic performance, and easy decontamination performance. Therefore, the textiles processed with polyester fibers have poor wearability and are prone to static electricity, which has caused certain harm to the health of the human body. Although the modified agent can also modify polyester fibers, it will become invalid after 5 to 10 times of washing. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a wash-resistant agent for polyester fibers. [0004] Another technical problem to be solved by the present invention is to provide a preparation method of a wash-resistant agent for polyester fibers. [0005] In order to solve the above technical problems, the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/59C08G69/44D06M101/32
Inventor 陈金辉吴玉春方玉琦贾刚
Owner DUPLUS CHEM OF ZHANGJIAGANG CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap