PET transfer basement film and preparation method thereof

A technology for base film and film, applied in the field of PET transfer base film and its preparation, to achieve the effect of safe transfer, stable quality, and excellent anti-shrinkage performance

Inactive Publication Date: 2017-05-10
江苏三房巷薄膜股份有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the thermal shrinkage rate of the produced PET transfer base film is generally between 0.1% and 0.5%, whi...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PET transfer basement film and preparation method thereof
  • PET transfer basement film and preparation method thereof
  • PET transfer basement film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] The specific implementation manners of the present invention will be further described below in conjunction with the drawings and examples. The following examples are only used to illustrate the technical solution of the present invention more clearly, but not to limit the protection scope of the present invention.

[0031] Such as Figure 1-Figure 4 As shown, a PET transfer base film includes a core layer 2 located in the middle and surface layers 17 arranged on both surfaces of the core layer 2, and the surface layer 17 and the core layer 2 are integrally formed by co-extrusion and biaxial stretching. The core layer 2 is a PET layer, and the surface layer 17 is a PET layer mixed with an antiblocking agent.

[0032] The weight ratio of the raw material components of the surface layer 17 and the core layer 2 is: surface layer 17: 80% to 90% of polyester melt for film, 10% to 20% of anti-blocking agent masterbatch; core layer 2: polyester melt for film Body 100%; the o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a PET transfer basement film and a preparation method thereof. The PET transfer basement film comprises a core layer and surface layers, wherein the core layer is positioned in the middle of the PET transfer basement film; the surface layers are arranged on the two surfaces of the core layer; the surface layers and the core layers are integrally formed by co-extrusion and bidirectional stretching; the core layer is a PET layer; and each surface layer is a PET layer mixed with an anti-blocking agent. The preparation method comprises the following steps: polyester synthesizing, blending, co-extruding, die head casting, longitudinal stretching, transverse stretching, traction and edge cutting, rolling, slitting and finished product obtaining. The thickness is 12-20 mu m, the breadth is 8,700 mm, the heat resistance temperature exceeds 120 DEG C, the tensile strength is greater than or equal to 220 MPa, the heat shrinkage rate is less than or equal to 3.5%, and the friction coefficient of the surface of the basement film is less than or equal to 0.55. Compared with the conventional transfer basement film, the PET transfer basement film has excellent shrinkage preventing property. The transfer basement film has excellent heat stability and high tensile strength, and can meet requirements of clients. Transfer films which do not deform at high temperature, are complete in transfer and full and clear in image-texts are produced.

Description

technical field [0001] The invention relates to a PET transfer base film and a preparation method thereof. Background technique [0002] As we all know, transfer film is also called heat transfer film, which is characterized by high tensile strength, good thermal stability, low thermal shrinkage, smooth surface and good peelability. In recent years, the market has a great demand for transfer base film. Usually, the base film produced from PET raw materials is used as the carrier of vacuum aluminizing. After aluminizing by an aluminizing machine, the glue is coated with paper, and then the PET film is peeled off. , The aluminum molecular layer is transferred to the surface of the cardboard through gluing, forming the so-called aluminum-coated cardboard. The cardboard is a kind of cardboard with metallic luster, and it is a high-level novel packaging material developed in recent years. This kind of aluminized cardboard has bright color, strong metallic feeling, and bright and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/36B32B27/18B41M5/41B65D65/40B29D7/01
CPCB32B27/36B29D7/01B32B27/08B32B27/18B32B2307/306B41M5/41B41M2205/36B65D65/40
Inventor 薛超於冬雷赵涛
Owner 江苏三房巷薄膜股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap