Antibacterial anti-shrinkage finishing process of wool fabric

A technology of anti-shrinkage finishing and fabric, which is applied in the field of antibacterial and anti-shrinkage finishing technology and functional wool fabrics, which can solve the problems that wool textiles cannot be combined and reacted, and antibacterial wool textiles have not been commercialized on a large scale, so as to achieve good antibacterial and anti-shrinkage Excellent performance, antibacterial durability and dimensional stability

Inactive Publication Date: 2018-04-24
WUXI HAOYU ENERGY SAVING ENVIRONMENTAL PROTECTION EQUIP CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, great progress has been made in the research of wool fabrics, such as the application of antibacterial agents such as heavy metal particles silver or heavy metal complexes, chitin, biological lysozyme, and cationic quaternary ammonium salts for antibacterial finishing of wool, but due to the special structure of wool itself And its chemical composition, usually wool textiles without pretreatment can not directly react with the finishing agent with antibacterial activity
Because of this technical difficulty, antibacterial wool textiles have not been commercialized on a large scale

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial anti-shrinkage finishing process of wool fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of antibacterial anti-shrinkage finishing technology of wool fabric, described technology comprises the following steps:

[0017] (1) The wool fabric is placed in a 16% aqueous solution of sodium hydroxide, and carried out an alkalization reaction at room temperature for 1.5 hours. After the reaction, adding a volume fraction of 4% hydrochloric acid neutralizes the residual sodium hydroxide , repeatedly washed with deionized water, and dried naturally;

[0018] (2) Immerse the wool fabric treated in step (1) in the finishing solution A, the bath ratio of the fabric and the finishing solution A is 1:25, the reaction temperature is 25°C, the pH is 8.0, and the reaction time is 30min. Rinse with deionized water and dry at 80°C;

[0019] (3) Soak the wool fabric finished in step (2) in the finishing solution B, the bath ratio of the fabric to the finishing solution B is 1:40, the reaction temperature is 40°C, the reaction time is 25min, and immediately put it in an ...

Embodiment 2

[0026] A kind of antibacterial anti-shrinkage finishing technology of wool fabric, described technology comprises the following steps:

[0027] (1) The wool fabric is placed in a 28% sodium hydroxide aqueous solution by mass fraction, and carried out an alkalization reaction at room temperature for 2.5 hours. After the reaction, adding a volume fraction of 7% hydrochloric acid to neutralize the residual sodium hydroxide , repeatedly washed with deionized water, and dried naturally;

[0028] (2) Immerse the wool fabric treated in step (1) in the finishing solution A, the bath ratio of the fabric and the finishing solution A is 1:28, the reaction temperature is 30°C, the pH is 8.3, and the reaction time is 45min. Rinse with deionized water and dry at 80°C;

[0029] (3) Dip the woolen fabric finished in step (2) into the finishing solution B, the bath ratio of the fabric to the finishing solution B is 1:45, the reaction temperature is 45°C, the reaction time is 30min, and immedi...

Embodiment 3

[0036] A kind of antibacterial anti-shrinkage finishing technology of wool fabric, described technology comprises the following steps:

[0037] (1) The wool fabric is placed in a 40% aqueous sodium hydroxide solution by mass fraction, and carried out an alkalization reaction at room temperature for 4 hours. After the reaction, adding a volume fraction of 11% hydrochloric acid to neutralize residual sodium hydroxide , repeatedly washed with deionized water, and dried naturally;

[0038] (2) Immerse the wool fabric treated in step (1) in the finishing solution A, the bath ratio of the fabric and the finishing solution A is 1:30, the reaction temperature is 35°C, the pH is 8.5, and the reaction time is 60min. Rinse with deionized water and dry at 80°C;

[0039] (3) Soak the woolen fabric finished in step (2) in the finishing solution B, the bath ratio of the fabric to the finishing solution B is 1:50, the reaction temperature is 50°C, the reaction time is 40min, and it is placed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antibacterial anti-shrinkage finishing process of a wool fabric. The process comprises the steps of pretreatment, antibacterial finishing, anti-shrinkage finishing and the like. (1) According to the finishing process of the invention, an immersion treatment way is mainly used, an antibacterial anti-shrinkage finishing solution can be easily arranged on the surface of thewool fabric by virtue of a series of pretreatment steps; and (2) the wool fabric after being finished by the finishing process of the invention has good antibacterial and anti-shrinkage performance,and the antibacterial durability and size stability of the fabric after being repeatedly washed are relatively good.

Description

technical field [0001] The invention belongs to the technical field of textiles, and relates to a functional wool fabric, in particular to an antibacterial and shrink-proof finishing process of the wool fabric. Background technique [0002] In a suitable temperature and humidity environment, natural fibers, especially protein fibers, become a good medium for microbial growth. The massive growth of microorganisms in textiles can cause textiles to degrade, produce spots, bad smells, etc. Antibacterial finishing of textiles is one of the ideal methods to solve these problems. Antimicrobial finishes can kill bacteria or inhibit their growth. [0003] At present, great progress has been made in the research of wool fabrics, such as the application of antibacterial agents such as heavy metal particulate silver or heavy metal complexes, chitin, biological lysozyme, and cationic quaternary ammonium salts for antibacterial finishing of wool, but due to the special structure of wool ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/56D06M11/54D06M15/37D06M11/38D06M101/12
Inventor 胡晓荣俞娟胡瑜
Owner WUXI HAOYU ENERGY SAVING ENVIRONMENTAL PROTECTION EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap