Rosin used for scaling powder as well as preparation method and application

A technology of flux and rosin, used in welding equipment, welding media, manufacturing tools, etc., can solve the problems of easy decomposition of rosin, irregular solder joints, uneven film formation, etc., to achieve good thermal stability, full solder joints, Good film forming effect

Active Publication Date: 2017-05-10
广东科茂林产化工股份有限公司 +2
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to improve the fluxing activity of rosin, the existing technology also uses rosin to add unsaturated carboxylic acid to prepare rosin, but this kind of rosin is easy to decompose at high temperature, resulting in uneven film formation and irregular solder joints

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rosin used for scaling powder as well as preparation method and application
  • Rosin used for scaling powder as well as preparation method and application
  • Rosin used for scaling powder as well as preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of embodiment of the rosin for soldering flux of the present invention, the rosin for soldering flux described in this embodiment is made up of the following components of mass percent: Laudanane type resin dibasic acid 12.0%, abietic acid 2.28%, dehydroabietic acid Acid 10.31%, dihydroabietic acid 57.3%, tetrahydroabietic acid 18.11%.

[0030] The composition of the above-mentioned rosin for soldering flux was analyzed by gas chromatography, and the softening point was 85.0° C. and the acid value was 175.0 mg KOH / g as measured by ring and ball method.

[0031] The preparation method of rosin for soldering flux described in the present embodiment is:

[0032] (1) Distillation: Weigh 700 grams of Nanya pine rosin, crush it and put it into a distillation bottle, and add tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]pentaerythritol ester 0.7 grams, vacuumize, heat to 240 ° C, observe the proportion of the distilled matter according to the receiving b...

Embodiment 2

[0035] A kind of embodiment of the rosin for soldering flux of the present invention, the rosin for soldering flux described in this embodiment is made up of the component of following mass percent: Laudanane type resin dibasic acid 15.82%, abietic acid 2.33%, dehydroabietic acid Acid 10.66%, dihydroabietic acid 53.21%, tetrahydroabietic acid 17.98%.

[0036] The composition of the above-mentioned rosin for soldering flux is obtained by gas chromatography analysis, and its softening point is 92° C., and its acid value is 193.7 mg KOH / g as measured by ring and ball method.

[0037] The preparation method of rosin for soldering flux described in the present embodiment is:

[0038] (1) Distillation: Weigh 700 grams of Nanya pine rosin, crush it and put it into a distillation bottle, and add tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]pentaerythritol ester 0.7 grams, vacuumize, heat to 243 ° C, observe the proportion of the distillate according to the receiving b...

Embodiment 3

[0041] A kind of embodiment of the rosin for soldering flux of the present invention, the rosin for soldering flux described in this embodiment is made up of the component of following mass percent: Laudanane type resin dibasic acid 18.31%, abietic acid 2.5%, dehydroabietic acid Acid 12.51%, dihydroabietic acid 51.35%, tetrahydroabietic acid 15.33%.

[0042] The composition of the above-mentioned rosin for soldering flux was analyzed by gas chromatography, and the softening point was 98° C., and the acid value was 201 mg KOH / g as measured by the ring and ball method.

[0043] The preparation method of rosin for soldering flux described in the present embodiment is:

[0044] (1) Distillation: Weigh 700 grams of Nanya pine rosin, crush it and put it into a distillation bottle. Observing the distillate ratio in the receiving bottle with a good scale, distilling until the mass percentage of nanya pine acid in the residue in the distillation bottle is 19%, stop the distillation an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to rosin used for scaling powder as well as a preparation method and application, belonging to the field of basic resin used for the scaling powder. Rosin which contains mercusicacid is taken as a raw material to prepare the rosin used for the scaling powder. The rosin used for the scaling powder has excellent solubility and crystallization resistance in a scaling powder solvent system, is high in weld-aid activity and low in corrosivity, and has very good wettability for brazing filler metal free of lead; and the rosin used for the scaling powder is good in both heat stability and film-forming property, and the formed welding spot is full, bright and regular.

Description

technical field [0001] The invention relates to a basic resin for soldering flux, in particular to a rosin for soldering flux, its preparation method and application. Background technique [0002] Rosin is a natural resource, and rosin and its prepared resin are important chemical raw materials, which are widely used in the fields of ink, coating, adhesive and electronics. [0003] Rosin is a mixture of resin acids with similar structures, containing double bonds and carboxyl groups. People have used these groups of rosin to modify them in order to broaden their application. [0004] In the electronic product industry, rosin has been widely used as the basic resin for soldering flux. Chinese patent, special-grade modified rosin and process for the electronic industry, publication number CN1065474A, discloses a kind of electronic rosin, namely refined rosin, refined hydrogenated rosin, alcohol Soluble maleated rosin glyceride and polymerized rosin are compounded to meet the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09F1/02C09F1/04B23K35/362B23K35/363
CPCB23K35/362C09F1/02C09F1/04
Inventor 陈就记徐社阳曾昭君范斌
Owner 广东科茂林产化工股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com