A kind of baking-type single-layer water-based flash paint for aluminum alloy wheel hub and preparation method thereof

An aluminum alloy wheel, flash paint technology, applied in coatings, anti-corrosion coatings, etc., can solve problems such as limitations, and achieve excellent recoating adhesion, good weather resistance, salt spray resistance, and acid and alkali resistance.

Active Publication Date: 2019-06-07
广东四方威凯新材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, manufacturers using water-based coatings mostly use composite coating technology, and the application of such products is greatly restricted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of baking-type single-layer water-based flash paint for aluminum alloy wheel hub and preparation method thereof
  • A kind of baking-type single-layer water-based flash paint for aluminum alloy wheel hub and preparation method thereof
  • A kind of baking-type single-layer water-based flash paint for aluminum alloy wheel hub and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The aluminum alloy wheel hub of the present embodiment is made up of following composition with baking type single-layer water-based flash paint:

[0032] Table 1: Baking type single-layer water-based flash paint (embodiment 1) for aluminum alloy wheels

[0033]

[0034]

[0035] The preparation method of the baking-type single-layer water-based flash paint for the aluminum alloy wheel hub of the present embodiment may further comprise the steps:

[0036] S1: Add the water-based silver paste to the reaction kettle A, then add the second solvent and thickener, stir until it becomes a uniform slurry, then soak for 2 hours under this condition, and set aside;

[0037] S2: Add the acrylic resin to the reaction kettle B, and add a neutralizing agent to adjust the pH value to 7.5-8.5 under the condition of a rotating speed of 500 RPM;

[0038] S3: Add the first solvent into the reaction kettle B, and disperse for 10 minutes at a rotation speed of 500 RPM;

[0039] S4:...

Embodiment 2

[0045] The aluminum alloy wheel hub of the present embodiment is made up of following composition with baking type single-layer water-based flash paint:

[0046] Table 2: Baking type single-layer water-based flash paint (embodiment 2) for aluminum alloy wheels

[0047]

[0048]

[0049] The preparation method of the baking-type single-layer water-based flash paint for the aluminum alloy wheel hub of the present embodiment may further comprise the steps:

[0050] S1: Add the water-based silver paste to the reaction kettle A, then add the second solvent and thickener, stir until it becomes a uniform slurry, then soak for 1 hour under this condition, and set aside;

[0051] S2: Add the acrylic resin to the reaction kettle B, and add a neutralizing agent to adjust the pH value to 7.5-8.5 under the condition of a rotating speed of 1000 RPM;

[0052] S3: Add the first solvent into the reaction kettle B, and disperse for 5 minutes at a rotation speed of 1000 RPM;

[0053] S4: A...

Embodiment 3

[0059] The aluminum alloy wheel hub of the present embodiment is made up of following composition with baking type single-layer water-based flash paint:

[0060] Table 3: Baking type single-layer water-based flash paint (embodiment 3) for aluminum alloy wheels

[0061]

[0062]

[0063] The preparation method of the baking-type single-layer water-based flash paint for the aluminum alloy wheel hub of the present embodiment may further comprise the steps:

[0064] S1: Add the water-based silver paste to the reaction kettle A, then add the second solvent and thickener, stir until it becomes a uniform slurry, then soak for 2 hours under this condition, and set aside;

[0065] S2: Add the acrylic resin to the reaction kettle B, and add a neutralizing agent to adjust the pH value to 7.5-8.5 under the condition of a rotating speed of 800 RPM;

[0066] S3: Add the first solvent into the reaction kettle B, and disperse for 10 minutes at a rotation speed of 800 RPM;

[0067] S4:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to bake type single-layer waterborne flashing paint for an aluminum alloy hub. The single-layer waterborne flashing paint is prepared from components in parts by weight as follows: 40.0-55.0 parts of acrylic resin, 20.0-39.0 parts of a first solvent, 0.2-1.2 parts of a neutralizer, 0.2-1.0 part of a levelling agent, 0.2-1.0 part of a defoaming agent, 0.5-2.5 parts of a thickener, 5.0-9.0 parts of amino resin, 1.5-3.0 parts of an adhesion accelerator, 5.0-10.0 parts of waterborne silver paste and 4.0-8.0 parts of a second solvent. The invention further provides a preparation method of the bake type single-layer waterborne flashing paint for the aluminum alloy hub. Conventional properties such as hardness, initial adhesion force and the like of a film of the bake type single-layer waterborne flashing paint for the aluminum alloy hub can meet demands, the repainting adhesion is excellent, the water resistance, the salt mist resistance and the acid-base resistance are good, corrosion and other conditions are avoided, and the weather resistance is excellent.

Description

technical field [0001] The invention relates to the technical field of paint and its preparation, in particular to a baking-type single-layer water-based flash paint for an aluminum alloy wheel hub and a preparation method thereof. Background technique [0002] The coating of motorcycle aluminum alloy wheels mainly includes three processes: single-layer color paint, primer topcoat and powder primer plus topcoat. The coating products of the first two processes account for more than 80% of the total. The coatings used for the coating of aluminum alloy wheels mainly include solvent-based coatings, powder coatings and water-based coatings. At present, solvent-based coatings are mainly used in this field. With the improvement of environmental protection requirements, the application of water-based coatings will become a future development trend. Due to the relatively complex structure of the motorcycle wheel hub, many concave and convex surfaces on the surface, and the need for ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D161/32C09D7/62C09D7/63C09D7/65C09D5/08
CPCC08L2205/035C09D5/08C09D7/62C09D7/63C09D7/65C09D133/00C08L83/12C08L75/04C08L61/32C08L63/00C08K9/10C08K2003/0806C08K5/17
Inventor 吴清双朱洪江李淑艳闵建国郑静康孙志强
Owner 广东四方威凯新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More