Epoxidized hydroxyl-terminated polybutadiene liquid rubber and preparation method thereof

A technology for epoxidizing hydroxyl-terminated polybutadiene and hydroxyl-terminated polybutadiene is applied in the field of hydroxyl-terminated polybutadiene liquid rubber and preparation thereof, and the field of epoxidation of hydroxyl-terminated polybutadiene liquid rubber and preparation thereof , which can solve the problems of high epoxidation value and low epoxidation value

Inactive Publication Date: 2017-05-31
高成龙
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims to solve the problem of low epoxidation value of epoxidized hydroxyl-terminated polybutadiene liquid rubber in the prior art, and provides a kind of epoxidized hydroxyl-terminated polybutadiene liquid rubber. Butadiene liquid rubber has a higher epoxy value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] An epoxidized hydroxyl-terminated polybutadiene liquid rubber, comprising the following raw materials in parts by weight:

[0023] 50 parts of hydroxyl-terminated polybutadiene

[0024] h 2 0 2 60 copies

[0025] 20 parts of formic acid

[0026] 120 parts of toluene

[0027] Acetone 80 parts

[0028] 3 parts of hydrochloric acid.

Embodiment 2

[0030] An epoxidized hydroxyl-terminated polybutadiene liquid rubber, comprising the following raw materials in parts by weight:

[0031] 60 parts of hydroxyl-terminated polybutadiene

[0032] h 2 0 2 70 copies

[0033] 25 parts of formic acid

[0034] 150 parts of toluene

[0035] Acetone 100 parts

[0036] 5 parts of hydrochloric acid.

Embodiment 3

[0038] An epoxidized hydroxyl-terminated polybutadiene liquid rubber, comprising the following raw materials in parts by weight:

[0039] 55 parts of hydroxyl-terminated polybutadiene

[0040] h 2 0 2 65 copies

[0041] 22 parts of formic acid

[0042] 130 parts of toluene

[0043] Acetone 90 parts

[0044] 4 parts of hydrochloric acid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to epoxidized hydroxyl-terminated polybutadiene liquid rubber and a preparation method thereof, and belongs to the technical field of hydroxyl-terminated polybutadiene liquid rubber. The liquid rubber is prepared from the following raw materials in parts by weight: 50-60 parts of hydroxyl-terminated polybutadiene, 60-70 parts of H2O2, 20-25 parts of formic acid, 120-150 parts of methylbenzene, 80-100 parts of acetone and 3-5 parts of hydrochloric acid. By adopting a formic acid oxidation technology, the epoxidized hydroxyl-terminated polybutadiene liquid rubber with a relatively high epoxide number is prepared. The epoxide number of the prepared epoxidized hydroxyl-terminated polybutadiene liquid rubber can reach 0.45-0.5.

Description

technical field [0001] The invention relates to a hydroxyl-terminated polybutadiene liquid rubber and a preparation method thereof, more specifically, the present invention relates to an epoxidized hydroxyl-terminated polybutadiene liquid rubber and a preparation method thereof, belonging to the hydroxyl-terminated polybutadiene rubber Olefin liquid rubber technical field. Background technique [0002] Hydroxyl-terminated polybutadiene liquid rubber (abbreviated as hydroxybutadiene, abbreviated as HTPB) is a liquid telechelic polymer. HTPB is an important variety in liquid rubber. At present, there are three main ways to modify hydroxyl-terminated polybutadiene: one is the modification of terminal functional groups, such as introducing epoxy groups into terminal groups or reacting with polyisocyanate to produce damping parts after maleic anhydride; the other The second is the modification of double bonds in the molecular structure, such as epoxidation for semiconductor com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08C19/06
CPCC08C19/06
Inventor 高成龙
Owner 高成龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap