Modified polyvinyl alcohol copolymer and preparation thereof as well as gel polymer electrolyte

A technology of polyvinyl alcohol copolymer and gel polymer, which is applied in the direction of hybrid capacitor electrolyte, etc., can solve the problems of poor electrolyte resistance and easy flocculation, and achieve the effect of improving mechanical properties and capacitance properties, and excellent electrolyte resistance

Active Publication Date: 2017-06-13
GUANGDONG PHARMA UNIV
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In addition, the PVA-based gel polymer aqueous solution has poor electrolyte resistance and is easy to flocculate, so it is not suitable for the preparation of water-based gel polymer electrolytes with adjustable water content.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified polyvinyl alcohol copolymer and preparation thereof as well as gel polymer electrolyte
  • Modified polyvinyl alcohol copolymer and preparation thereof as well as gel polymer electrolyte
  • Modified polyvinyl alcohol copolymer and preparation thereof as well as gel polymer electrolyte

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1, modified polyvinyl alcohol copolymer of the present invention and preparation thereof

[0031] S1. Dissolution of polyvinyl alcohol: Weigh 10g of polyvinyl alcohol solid and place it in a three-necked flask, add 50mL of water, heat it in a water bath at 60°C, stir and swell for 0.5h, and add water during the swelling process to make the total volume 60mL ; Then raise the temperature to 95°C, keep stirring at 95°C until the polyvinyl alcohol solid is completely dissolved, and cool naturally to obtain a polyvinyl alcohol solution for later use;

[0032] S2. Graft modification of polyvinyl alcohol: Weigh 8 g of the polyvinyl alcohol solution, put it into a three-necked flask, and heat it in a water bath at 40-45°C; then pass argon gas into the three-necked flask for 4 After ~6min, add 7mL of N-vinylpyrrolidone and 0.4mL of 2-hydroxyethyl methacrylate, stir evenly, then add acidic cerium ion solution; keep the water bath temperature at 40-45°C, continue argon ...

Embodiment 2

[0034] Embodiment 2, modified polyvinyl alcohol copolymer of the present invention and preparation thereof

[0035] S1. Dissolution of polyvinyl alcohol: Weigh 10g of polyvinyl alcohol solid and place it in a three-necked flask, add 50mL of water, heat it in a water bath at 60°C, stir and swell for 0.5h, and add water during the swelling process to make the total volume 60mL ; Then raise the temperature to 95°C, keep stirring at 95°C until the polyvinyl alcohol solid is completely dissolved, and cool naturally to obtain a polyvinyl alcohol solution for later use;

[0036] S2. Graft modification of polyvinyl alcohol: Weigh 12 g of the polyvinyl alcohol solution, put it into a three-necked flask, and heat it in a water bath at 40-45°C; then pass argon gas into the three-necked flask, 4 After ~6min, add 14mL of N-vinylpyrrolidone and 1mL of glycidyl methacrylate, stir well, then add acidic cerium ion solution; keep the temperature of the water bath at 40-45°C, continue to pass ar...

Embodiment 3

[0038] Embodiment 3, modified polyvinyl alcohol copolymer of the present invention and preparation thereof

[0039] S1. Dissolution of polyvinyl alcohol: Weigh 10g of polyvinyl alcohol solid and place it in a three-necked flask, add 50mL of water, heat it in a water bath at 60°C, stir and swell for 0.5h, and add water during the swelling process to make the total volume 60mL ; Then raise the temperature to 95°C, keep stirring at 95°C until the polyvinyl alcohol solid is completely dissolved, and cool naturally to obtain a polyvinyl alcohol solution for later use;

[0040] S2. Grafting modification of polyvinyl alcohol: Weigh 10 g of the polyvinyl alcohol solution, put it into a three-necked flask, and heat it in a water bath at 40-45°C; then pass argon gas into the three-necked flask, 4 After ~6min, add 12mL of N-vinylpyrrolidone and 0.7mL of 2-hydroxyethyl methacrylate, stir evenly, then add acidic cerium ion solution; keep the water bath temperature at 40-45°C, continue argo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention particularly discloses a modified polyvinyl alcohol copolymer and a preparation method thereof, and gel polymer electrolyte containing the modified polyvinyl alcohol copolymer. The preparation method of the modified polyvinyl alcohol copolymer comprises the following steps: weighing a polyvinyl alcohol solid; adding water and swelling; after raising the temperature and dissolving, heating in a water bath at 40 DEG C to 45 DEG C; introducing argon gas and adding N-vinylpyrrolidone and a functional monomer; and after uniformly stirring, adding an acidic cerium ion solution and reacting for 3h to 5h to prepare the modified polyvinyl alcohol copolymer. The modified polyvinyl alcohol copolymer has a good electrolyte resisting performance. The neutral and alkaline gel polymer electrolyte with ideal mechanical properties and capacitive properties is prepared by taking the modified polyvinyl alcohol copolymer as a matrix material, taking glutaraldehyde or borax as a cross-linking agent and adding a proper amount of electrolyte (LiCl or LiOH); and the moisture content in gel is adjusted, and meets good application requirements in a flexible solid-state super-capacitor.

Description

technical field [0001] The invention belongs to the technical field of organic synthesis, and specifically relates to a modified polyvinyl alcohol copolymer, a preparation method thereof, and a gel polymer electrolyte containing the modified polyvinyl alcohol copolymer. Background technique [0002] As a necessary functional material for the assembly of flexible solid supercapacitors, gel polymer electrolyte not only directly affects its capacitance, rate performance, high and low temperature performance, etc., but also can avoid liquid leakage, and is safe and convenient to use. It is very suitable for flexible electronics and energy storage devices. [0003] Currently, gel polymer electrolytes used in the assembly of flexible solid supercapacitors usually consist of three parts: gel polymer (matrix material), organic / aqueous solvent (plasticizer) and electrolyte. Typical representatives of matrix materials are: polyacrylic acid (PAA or PAAK), polyethylene oxide (PEO), pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F261/04C08F226/10C08F220/28C08F220/32C08F4/40C08J3/24C08J3/075H01G11/56C08L51/00
CPCH01G11/56C08F4/40C08F261/04C08J3/075C08J3/24C08J2351/00C08F220/325C08F220/281Y02E60/13
Inventor 刘意肖儒坚王昊
Owner GUANGDONG PHARMA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap