Wood floor repairing agent and using method thereof

A technology of repairing agent and wooden floor, which is applied in the field of floor repairing agent and wooden floor repairing agent. It can solve the problems of weak bonding between the repairing agent and the surrounding wood, lower production efficiency, and heavy workload, and achieve good market application prospects. , improve efficiency, improve the effect of repair quality

Inactive Publication Date: 2017-06-23
DAYA JIANGSU FLOOR
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are two problems with the use of repairing agent to finish and then manual repair: 1. The efficiency of manual repair is not high, especially for the surface plate with low repair level. The workload of manual repair is large, which reduces the production efficiency; 2. The repair agent is not firmly bonded to the surrounding wood, especially to the surrounding knots.
Existing repairing methods are wasteful and the repairing effect is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The repair agent uses Shanghai Resin Factory Lubao brand 618 epoxy resin and Lubao brand 5618 epoxy resin curing agent. It is prepared according to the weight ratio of 100:50. When preparing, first pour 100g of epoxy resin into a disposable plastic cup , then add 50g of curing agent and stir evenly, add 2g of black essence and mix evenly, dip it with a wooden stick and drop it on the knots. After repairing, the floors are separated by spacers with an average thickness of about 9mm, 10-12h After the epoxy resin is cured, the prepared repair agent is cured in the cup for 20-40 minutes.

Embodiment 2

[0028]The repair agent adopts Shanghai Resin Factory Lubao brand 618 epoxy resin and Lubao brand 5618 epoxy resin curing agent. It is prepared according to the weight ratio of 100:65. When preparing, first pour 100g of epoxy resin into a disposable plastic cup , then add 65g of curing agent and stir evenly, add 0.5g of black essence and mix evenly, dip it with a wooden stick and drop it on the knots. After repairing, separate the floors with spacers with an average thickness of about 9mm, After 12 hours, the epoxy resin is cured, and the prepared repair agent is cured after 20-40 minutes in the cup.

Embodiment 3

[0030] The repair agent uses Shanghai Resin Factory Lubao brand 618 epoxy resin and Lubao brand 5618 epoxy resin curing agent. It is prepared according to the weight ratio of 100:50. When preparing, first pour 100g of epoxy resin into a disposable plastic cup , then add 50g of curing agent and stir evenly, add 20g of wood powder to mix evenly, dip it with a wooden stick and drop it on the knots, and after repairing, separate the floors with spacers with an average thickness of about 9mm, 10-12h After the epoxy resin is cured, the prepared repair agent is cured in the cup for 20-40 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of chemical adhesives, and relates to a wood floor repairing agent and a using method thereof. The wood floor repairing agent is prepared by compounding and blending epoxy resin and an epoxy resin curing agent, wherein the epoxy resin is bisphenol A-type epoxy chloropropane with low molecular weight; the epoxy resin curing agent is polyethylenimine, wherein the weight ratio of the epoxy resin to the epoxy resin curing agent is 100: (50-70). The invention further discloses the using method of the repairing agent. By adopting the wood floor repairing agent disclosed by the invention, the efficiency of manual repair of a solid wood composite floor can be improved, and when the veneer floor with low repair grade is repaired, compared with the repairing efficiency of the quick-drying putty, the efficiency is improved by about 100%; the repairing agent is firmly adhered to the surrounding wood, cracking and detachment between the repairing agent with knots and the wood are avoided, and the detection requirements of 6.2.5 surface hot-cold cycle resistant test in the standard LY/T1700-2007 of wood based flooring for ground with a heating system can be met. The improvement of the repairing quality of the material species rich in the medullary spot and resin pocket is more obvious, and the repairing agent has a good application prospect.

Description

technical field [0001] The invention belongs to the technical field of chemical adhesives, and relates to a floor repair agent, in particular to a wooden floor repair agent and a use method. Background technique [0002] The surface of the three-layer solid wood composite floor generally uses 3-4mm hard wood species as the surface board, and the cork veneer used for the core board and the bottom board is mostly fast-growing wood such as spruce, sylvestris pine, poplar, and eucalyptus. The hard wood used to make the panel generally has natural or post-processing defects such as knots and cracks. Knots include dead knots, leaky knots, and cracked joints. Cracks include closed cracks and open cracks. Completely eliminating these wood defects will greatly reduce the utilization rate of wood. In the current situation of increasingly tight natural wood resources, it is necessary to Study how to make good use of limited wood resources efficiently. [0003] At present, there are g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/00C08G59/50
CPCC09J163/00C08G59/502
Inventor 高雅纪娟
Owner DAYA JIANGSU FLOOR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap