High-efficiency composite type anti-sticking smooth master batch for producing CPP (casting polypropylene) membrane

A composite and efficient technology, applied in the field of polymer compounds, can solve the problems of waste of manpower and material resources, complex process, large amount of addition, etc., and achieve the effect of saving dosage, improving dispersion effect and reducing production cost.

Inactive Publication Date: 2017-07-28
佛山市高明海能科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] For CPP heat-sealable films, in the prior art, anti-adhesive masterbatch and slip agent masterbatch need to be added to the surface layer to effectively reduce the friction coefficient of the CPP heat-seal layer and achieve the required opening performance, but this method The process is complicated, and the timing and temperature of adding the two masterbatches need to be strictly controlled. At the same time, the amount of addition is large, which wastes a lot of manpower and material resources. It is a technical problem that needs to be overcome in the production of CPP heat-sealable films.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A high-efficiency composite anti-sticking and slippery masterbatch for the production of CPP films, calculated in parts by mass, is specifically prepared from the following components: 75 parts of polypropylene materials, 7 parts of silica materials, and 8 parts of erucic acid materials , 1 part of diffusing agent; its preparation method is specifically the following steps:

[0016] (1) After the polypropylene material is frozen at -40°C for 10 minutes, it is heated and melted at 210°C, kept at a temperature of 5 minutes, and is ready for use; The acid materials are fully mixed to play a good auxiliary effect and improve their anti-sticking and smoothing effect;

[0017] (2) Raise the temperature of the polypropylene material in step (1) to 280°C, stop heating after adding the silica material and diffusing agent, and then add the erucic acid material when it cools to 200°C, and keep warm 2 minutes, and then rapidly cooled to condense to obtain the high-efficiency compo...

Embodiment 2

[0021] A high-efficiency composite anti-sticking and slippery masterbatch for the production of CPP films, calculated in parts by mass, is specifically prepared from the following components: 80 parts of polypropylene materials, 11 parts of silica materials, and 12 parts of erucic acid materials , 2 parts of diffusing agent; its preparation method is specifically the following steps:

[0022] (1) After the polypropylene material is frozen at -40°C for 15 minutes, it is heated and melted at 220°C, kept at a temperature of 5 minutes, and is set aside for use; the polypropylene material after freezing and embrittlement can be melted in silica-based materials and mustard after melting. The acid materials are fully mixed to play a good auxiliary effect and improve their anti-sticking and smoothing effect;

[0023] (2) Raise the temperature of the polypropylene material in step (1) to 290°C, stop heating after adding the silica-based material and diffusing agent, and then add the er...

Embodiment 3

[0027] A high-efficiency composite anti-sticking and slippery masterbatch for the production of CPP films, calculated in parts by mass, is specifically prepared from the following components: 80 parts of polypropylene materials, 9 parts of silica materials, and 10 parts of erucic acid materials , 2 parts of diffusing agent; its preparation method is specifically the following steps:

[0028] (1) After the polypropylene material is frozen at -40°C for 12 minutes, it is heated and melted at 215°C, kept at a temperature of 5 minutes, and is ready for use; The acid materials are fully mixed to play a good auxiliary effect and improve their anti-sticking and smoothing effect;

[0029] (2) Raise the temperature of the polypropylene material in step (1) to 285°C, stop heating after adding the silica material and diffusing agent, and then add the erucic acid material when it cools to 205°C to keep the temperature 2 minutes, and then rapidly cooled to condense to obtain the high-effic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to high-efficiency composite type anti-sticking smooth master batch for producing a CPP (casting polypropylene) membrane. The high-efficiency composite type anti-sticking smooth master batch is specifically prepared from the following components in parts by mass: 75-80 parts of a polypropylene material, 7-11 parts of a silica material, 8-12 parts of an erucic acid material and 1-2 parts of a dispersing agent. Tests show that when a CPP heat-seal type membrane is prepared, to achieve a good anti-sticking and smooth effect, the addition ratio of the master bath is 0.4%, the addition ratio of a conventional additive is 0.2%, but the ratio of a polypropylene material in the master bath is as high as 80%, that is, the amount of the silica material and the erucic acid material is only 0.08%, which is far less than the amount of 0.2% of the conventional additive, so that the amount of the master batch can be greatly reduced, and the production cost of a company can be lowered.

Description

technical field [0001] The invention belongs to the technical field of polymer compounds, and in particular relates to a high-efficiency composite anti-sticking and slippery masterbatch for CPP film production. Background technique [0002] CPP film, also known as unstretched polypropylene film, is a non-stretched, non-oriented flat extrusion film produced by melt casting quenching. Compared with blown film, it is characterized by fast production speed, high output, good film transparency, gloss, thickness uniformity, and excellent balance of isotropic properties. At the same time, because it is a flat extrusion film, the subsequent processes such as printing and lamination are extremely convenient, so it is widely used in the packaging of textiles, flowers, food, and daily necessities. [0003] For the CPP heat-sealing film, in the prior art, the surface layer needs to be added with anti-sticking agent masterbatch and slip agent masterbatch respectively, in order to effect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08K13/02C08K3/36C08K3/22C08K5/20
CPCC08K13/02C08K3/22C08K3/36C08K5/20C08K2003/222C08K2003/2227C08K2201/014C08L23/12
Inventor 刘学赞谭尚荣
Owner 佛山市高明海能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap