Preparation method of ceramsite permeable road brick

A technology of permeable pavement bricks and ceramsite, applied in the directions of roads, roads, pavement details, etc., can solve the problems of poor frost resistance, poor water permeability, insufficient strength, etc., and achieve the effect of good frost resistance, good water permeability and novel style.

Inactive Publication Date: 2017-08-01
柯步哨
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Among them, there are various forms of permeable pavement brick products in the prior art; however, for the existing permeable pavement brick products, they generally have the defects of poor water permeability, insufficient strength, and poor frost resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Embodiment 1, a preparation method of ceramsite permeable pavement bricks, including the following process steps, specifically:

[0048] a. Preparation of colored surface layer material: put colored cement or white cement, pigment powder, and sand in a ball mill for mixed ball milling treatment. The time for mixing ball milling treatment is 5-20 minutes. The purpose of mixing ball milling treatment is to ensure the colored surface layer The smoothness and color uniformity of the material; among them, the weight of each material in the color surface material is as follows:

[0049] Colored cement or white cement 6kg

[0050] Pigment powder 0.3 kg

[0051] 8 kg of sand;

[0052] b. Preparation of base material: put ceramsite, sand, stone, cement, and curing agent in a wheel mill for mixing and mixing. The time for mixing and mixing is 5-30 minutes; Large, the amount of cement and curing agent is small, so the quality of mixing will directly affect the strength and qual...

Embodiment 2

[0061] Embodiment 2, a preparation method of ceramsite permeable pavement bricks, including the following process steps, specifically:

[0062]a. Preparation of colored surface layer material: put colored cement or white cement, pigment powder, and sand in a ball mill for mixed ball milling treatment. The time for mixing ball milling treatment is 5-20 minutes. The purpose of mixing ball milling treatment is to ensure the colored surface layer The smoothness and color uniformity of the material; among them, the weight of each material in the color surface material is as follows:

[0063] Colored cement or white cement 3 kg

[0064] Pigment powder 0.1 kg

[0065] 5 kg of sand;

[0066] b. Preparation of base material: put ceramsite, sand, stone, cement, and curing agent in a wheel mill for mixing and mixing. The time for mixing and mixing is 5-30 minutes; Large, the amount of cement and curing agent is small, so the quality of mixing will directly affect the strength and qual...

Embodiment 3

[0075] Embodiment 3, a preparation method of ceramsite permeable pavement bricks, including the following process steps, specifically:

[0076] a. Preparation of colored surface layer material: put colored cement or white cement, pigment powder, and sand in a ball mill for mixed ball milling treatment. The time for mixing ball milling treatment is 5-20 minutes. The purpose of mixing ball milling treatment is to ensure the colored surface layer The smoothness and color uniformity of the material; among them, the weight of each material in the color surface material is as follows:

[0077] Colored cement or white cement 8kg

[0078] Pigment powder 0.4 kg

[0079] 10 kg of sand;

[0080] b. Preparation of base material: put ceramsite, sand, stone, cement, and curing agent in a wheel mill for mixing and mixing. The time for mixing and mixing is 5-30 minutes; Large, the amount of cement and curing agent is small, so the quality of mixing will directly affect the strength and qua...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a ceramsite permeable road brick. The preparation method comprises the following steps of a. preparing a color surface material: putting 3-8kg of color cement or white cement, 0.1-0.4kg of pigment powder and 5-10kg of sand into a ball mill for mixing and ball milling, wherein mixing and ball milling consume 5-20 minutes; b. preparing a base material: putting 20-100kg of ceramsite, 5-50kg of sand, 5-50kg of stone material, 10-40kg of cement and 0.5-10kg of curing agent into a wheel mill for stirring and mixing, wherein stirring and mixing consume 5-30 minutes; c. pressing and shaping by a hydraulic brick machine; and d. demoulding and curing. Through adoption of the above steps, the ceramsite permeable road brick prepared by the preparation method has high water permeability, high strength, and high freezing resistance, is novel in design, is colorful, and has the compression strength reaching up to MU20-30.

Description

technical field [0001] The invention relates to the technical field of permeable pavement bricks, in particular to a preparation method of ceramsite permeable pavement bricks. Background technique [0002] Permeable pavement brick is a concrete pavement product that can not only bear a large load, but also allow water to penetrate through the concrete surface to the bottom and even underground; as my country is constantly advocating sponge cities, the demand for permeable pavement bricks is also increasing. bigger. [0003] Among them, there are various forms of permeable pavement brick products in the prior art; however, for the existing permeable pavement brick products, they generally have the defects of poor water permeability, insufficient strength, and poor frost resistance. Contents of the invention [0004] The purpose of the present invention is to provide a method for preparing ceramsite permeable pavement bricks in view of the deficiencies in the prior art. The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More