Light rubber composite material and process for manufacturing belt by adopting material
A composite material, rubber and plastic technology, applied in the field of composite materials, can solve the problems of high price of natural leather, low strength of PU leather, and untrue effect of imitation leather, etc., and achieve the effect of soft texture, high effect of imitation leather, and easy processing
Inactive Publication Date: 2017-08-11
福建福沃德橡塑制品有限公司
View PDF5 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] At present, rubber and plastic soles for shoes generally have defects such as heavy weight, strong smell, and unreal imitation leather effect.
However, the belt has always been made of genuine leather or PU leather, and there are problems such as the shortage of natural leather and the high price, and the low strength of PU leather.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0025] In order to facilitate understanding of the present invention, the present invention enumerates the following examples. Those skilled in the art should understand that the examples are only used to help understand the present invention, and should not be regarded as specific limitations on the present invention.
[0026] Unless otherwise specified, various raw materials of the present invention can be obtained commercially; or prepared according to conventional methods in the art. Unless otherwise defined or stated, all professional and scientific terms used herein have the same meaning as is familiar to those skilled in the art. In addition, any methods and materials similar or equivalent to those described can be applied to the method of the present invention.
[0027] Unless otherwise indicated, all professional and scientific terms used herein have the same meaning as is familiar to those skilled in the art.
[0028] In addition, any methods and materials similar ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a light rubber composite material and a process for manufacturing a belt by adopting the material. The light rubber composite material is formed by mixing a rubber and plastic composite material, filler, a foaming agent, foaming aids, a lubricant, a crosslinking agent and a colorant. The weight ratio of the ingredients is 100: 70: 2: 3: 3: 1.38: 2. The invention further discloses the process for manufacturing the belt by adopting the light rubber composite material. The light rubber composite material is reasonable in formula, easy to obtain, gentle in texture, high in leather simulation effect, strength and abrasion resistance, easy to process and suitable for manufacturing products such as belts.
Description
technical field [0001] The invention relates to a composite material, in particular to a lightweight rubber-plastic composite material, and also relates to a process for making a waist belt using the material. Background technique [0002] At present, rubber and plastic soles for shoes generally have defects such as heavy weight, strong smell, and unreal imitation leather effect. As for belts, genuine leather or PU leather has been used all the time, and there are problems such as the shortage of natural leather and the high price, and the low strength of PU leather. Contents of the invention [0003] In order to solve the above technical problems, the present invention provides a lightweight rubber-plastic composite material for belts, which is soft in texture, high in imitation leather effect, high in strength and high in wear resistance. [0004] For realizing the purpose of the present invention, the technical scheme that takes is: [0005] A lightweight rubber-plast...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L7/00C08L9/06C08L47/00C08K13/02C08K3/22C08K3/26C08K3/34C08K5/14C08K5/09C08K5/098C08J9/10B29C69/00B29C43/24B29C59/04B29C44/34
CPCC08L23/0853B29C43/24B29C44/3442B29C44/3446B29C59/04B29C69/00C08J9/103C08J2203/04C08J2323/08C08J2407/00C08K2003/2296C08K2003/265C08K2201/011C08L2205/03C08L7/00C08L9/06C08K13/02C08K3/22C08K3/26C08K3/346C08K5/14C08K5/09C08K5/098C08L47/00
Inventor 吕必阳
Owner 福建福沃德橡塑制品有限公司