Eletroforming processing method for K gold jewellery

A processing method and gold jewelry technology, applied in electroforming, clothing, electrolysis process, etc., can solve problems such as capital backlog cost burden, affect market competitiveness, and unfavorable development of manufacturers, so as to facilitate development, improve competitiveness, and be easy to wear Effect

Inactive Publication Date: 2017-08-18
深圳市金玉福珠宝首饰有限公司
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing K gold manufacturing technology adopts the inverted molding process, that is, it is produced by the inverted molding process of molten gold casting. The products produced by the casting are all solid products, and their weight is relatively heavy. When the jewelry is large in size, it is extremely inconvenient. It i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Eletroforming processing method for K gold jewellery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] In order to make the object, technical solution and advantages of the present invention more clear, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0026] see figure 1 , the electroforming processing method of a kind of K gold ornament of the present invention, it comprises:

[0027] 101. Using low-melting point alloys to form blanks

[0028] Pour the melted low-melting point alloy into a mold, and after the low-melting point alloy is cooled and formed, remove the mold outside the low-melting point alloy to obtain a green body composed of the low-melting point alloy;

[0029] Preferably, the low melting point alloy is tin alloy.

[0030] 102. Carry out body surface treatment

[0031] Smooth the edges and corners of the outer surface of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of jewellery processing, and specifically relates to an eletroforming processing method for K gold jewellery. The eletroforming processing method for the K gold jewellery comprises the following steps: pouring a melted low-melting-point alloy into a die, carrying out cooling forming on the low-melting-point alloy, and then removing the die to obtain a blank body composed of the low-melting-point alloy; eletroforming a K gold layer on the outer surface of the blank body to obtain a jewellery prototype; punching convection holes in the jewellery prototype; boiling the jewellery prototype punched with the convection holes, melting the low-melting-point alloy and enabling the low-melting-point alloy to flow out from the convection holes; then filling and sealing the convection holes in the surface of the jewellery prototype by virtue of a sealing wax; and carrying out surface treatment on the jewellery prototype with the filled-sealed convection holes to obtain finished jewellery. The eletroforming processing method for the K gold jewellery is capable of producing the hollow K gold jewellery, and the weight and the content of the K gold jewellery are effectively lowered, so that the K gold jewellery can be conveniently worn by a user, the production cost is greatly lowered, and the competitiveness of the product is effectively improved; and moreover, a fund demand on manufacturers is lowered, so that the development of the manufacturers is benefited.

Description

technical field [0001] The invention relates to the technical field of jewelry processing, in particular to an electroforming method for K gold jewelry. Background technique [0002] K gold is an alloy made of gold and other metals. The existing K gold manufacturing technology adopts the inverted molding process, that is, it is produced by the inverted molding process of molten gold casting. The products produced by the casting are all solid products, and their weight is relatively heavy. When the jewelry is large in size, it is extremely inconvenient. It is only suitable for light and simple styles or inlaid styles. Since K gold mainly uses gold as the main raw material, a solid K gold jewelry is not much cheaper than pure gold jewelry in terms of labor costs. A large backlog of funds and cost burdens have been caused, which is not conducive to the development of various manufacturers. Contents of the invention [0003] In order to overcome the above defects, the objec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25D1/00A44C27/00
CPCC25D1/00A44C27/00
Inventor 陈奖
Owner 深圳市金玉福珠宝首饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap