High-strength ceramic brick with bionic bamboo culm wall structure and preparation method thereof

A wall structure and biomimetic bamboo technology, applied in the field of ceramic tiles, can solve problems such as potential safety hazards, increase production costs, and self-importance of ceramic tiles, and achieve the effects of being convenient for large-scale production and application, controllable structural changes, and simple preparation methods.

Active Publication Date: 2017-08-25
安徽省亚欧陶瓷有限责任公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the weight of the tiles, when pasted on the wall, the keel is easily deformed and displaced after being stressed. Over time, it will cause problems such as hollowing and falling, which not only affects the appearance but also poses safety hazards. Therefore, the lightweight and high-strength tiles Ceramic tiles are becoming more and more popular in the market
At present, the research and development of the production of light-weight and high-strength ceramic tiles mainly focuses on improving the formula and sintering process, which greatly increases the production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] A high-strength ceramic brick with a bionic bamboo wall structure, comprising a ceramic base and a glaze layer covered on the ceramic base, the ceramic base is composed of a porous or solid ceramic core and a ceramic with a bamboo wall structure surrounding the ceramic core .

[0027] The preparation method of the ceramic tile of a kind of high-strength bionic bamboo wall structure, comprises the following steps:

[0028] (1) Preparation of ceramic slurry:

[0029] Mix ceramic aggregate, dispersant, binder, and water according to the ratio of 100:1:1:20, and then ball mill them to make ceramic slurry 1 for later use;

[0030] Mix ceramic aggregate, dispersant, binder, spherical pore-forming agent, and water according to the ratio of 100:1:1:5:20, and then ball mill them to prepare ceramic slurry 2 for later use;

[0031] Mix ceramic aggregate, dispersant, binder, fibrous pore-forming agent, and water according to the ratio of 100:1:1:10:20, and then ball mill them to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength ceramic brick with a bionic bamboo culm wall structure. The high-strength ceramic brick comprises a ceramic matrix and a glaze surface layer covering the ceramic matrix, wherein the ceramic matrix is composed of a porous or solid ceramic core and bamboo culm wall structure simulated ceramic wrapping the ceramic core. The ceramic brick disclosed by the invention has an extremely strong load capability and the structural change of the ceramic brick is controllable; compared with a traditional porous ceramic brick, the strength is higher and an application range of a product is wider; the preparation method is simple and is convenient for large-scale production and application.

Description

technical field [0001] The invention relates to the technical field of ceramic bricks, in particular to a ceramic brick with a high-strength bionic bamboo wall structure and a preparation method thereof. Background technique [0002] Ceramic bricks can be seen everywhere in daily life. They are an important building material. They are plate or block ceramic products produced by molding and sintering processes from clay and other inorganic non-metallic raw materials. They are used to decorate and protect buildings. , The walls and floors of structures are usually formed by dry pressing, extrusion or other molding methods at room temperature, then dried and fired at a certain temperature. Due to the weight of the tiles, when pasted on the wall, the keel is easily deformed and displaced after being stressed. Over time, it will cause problems such as hollowing and falling, which not only affects the appearance but also poses safety hazards. Therefore, the lightweight and high-st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/06C04B33/13C04B33/34B28B1/00B28B1/16
CPCB28B1/007B28B1/16C04B33/13C04B33/1305C04B33/34C04B38/0645C04B38/067C04B38/0675C04B38/068C04B2235/6562C04B2235/6567C04B2235/661
Inventor 郑辉
Owner 安徽省亚欧陶瓷有限责任公司