PVC (Polyvinyl Chloride) building template and preparation method thereof

A technology for building formwork and chlorinated polyethylene, applied in the field of building materials, can solve the problems of poor impact resistance, hindering the large-scale popularization and use of PVC plastic plastic building formwork, and low elastic modulus.

Inactive Publication Date: 2017-09-08
六安三创建筑材料有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to its own defects such as poor thermal stability, poor heat resistance, high brittleness, and poor impact resistance, PVC building templates currently on the market generally have shortcomings such as low elastic modulus, low impact strength, and poor weather resistance. It has hindered the large-scale promotion and use of PVC plastic plastic building formwork

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A PVC building formwork proposed by the present invention comprises the following raw materials in parts by weight: 28 parts of chlorinated polyethylene, 15 parts of filler, 0.2 part of aluminum titanate coupling agent, 65 parts of polyvinyl chloride, 25 parts of straw fiber powder, 2 parts of aluminum hydroxide, 1.2 parts of zinc borate, 2 parts of stabilizer, 0.8 part of ultraviolet shielding agent, 0.8 part of antioxidant, 0.8 part of antibacterial agent, wherein the filler is calcium carbonate with a mass ratio of 4:1.5:1.8:1.2 , kaolin, wollastonite and silicon carbide; polyvinyl chloride is a mixture of new polyvinyl chloride material and recycled polyvinyl chloride material with a mass ratio of 1:3.5; the stabilizer is a rare earth composite stabilizer with a mass ratio of 1.2:3.5 agent and calcium-zinc composite stabilizer.

[0019] Its preparation method comprises the following steps:

[0020] S1. Add the specific gravity filler into the grinder, fully grind t...

Embodiment 2

[0025] A PVC building formwork proposed by the present invention comprises the following raw materials in parts by weight: 35 parts of chlorinated polyethylene, 18 parts of filler, 0.3 parts of aluminum titanate coupling agent, 80 parts of polyvinyl chloride, 30 parts of straw fiber powder, 3 parts of aluminum hydroxide, 1.8 parts of zinc borate, 3 parts of stabilizer, 1 part of ultraviolet shielding agent, 1 part of antioxidant, 1 part of antibacterial agent, wherein the filler is calcium carbonate with a mass ratio of 5:2:1.2:1 , kaolin, wollastonite and silicon carbide; polyvinyl chloride is a mixture of new polyvinyl chloride material and polyvinyl chloride recycled material with a mass ratio of 1:4.5; the stabilizer is a rare earth composite stabilizer with a mass ratio of 1.5:4 agent and calcium-zinc composite stabilizer.

[0026] Its preparation method comprises the following steps:

[0027] S1. Add the specific gravity filler into the grinder, fully grind through a 25...

Embodiment 3

[0032] A PVC building template proposed by the present invention comprises the following raw materials in parts by weight: 25 parts of chlorinated polyethylene, 14 parts of filler, 0.15 parts of aluminum titanate coupling agent, 60 parts of polyvinyl chloride, 22 parts of straw fiber powder, 1.5 parts of aluminum hydroxide, 1 part of zinc borate, 1.5 parts of stabilizer, 0.6 part of ultraviolet shielding agent, 0.7 part of antioxidant, 0.7 part of antibacterial agent, wherein the filler is calcium carbonate with a mass ratio of 3.5:1.2:1:1.5 , kaolin, wollastonite and silicon carbide; polyvinyl chloride is a mixture of new polyvinyl chloride material and recycled polyvinyl chloride material with a mass ratio of 1:3; the stabilizer is a rare earth composite stabilizer with a mass ratio of 1.2:3.2 agent and calcium-zinc composite stabilizer.

[0033] Its preparation method comprises the following steps:

[0034]S1. Add the specific gravity filler into the grinding machine, full...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a PVC (Polyvinyl Chloride) building template, which comprises the following raw materials in parts by weight: 22 to 35 parts of chlorinated polyethylene, 12 to 18 parts of filler, 0.1 to 0.3 part of aluminum titanate coupling agent, 50 to 80 parts of polyvinyl chloride, 20 to 30 parts of straw fiber powder, 1 to 3 parts of aluminium hydroxide, 0.8 to 1.8 parts of zinc borate, 1 to 3 parts of stabilizer, 0.5 to 1 part of ultraviolet screening agent, 0.5 to 1 part of antioxidant, and 0.5 to 1 part of antibacterial agent. Compared with an existing PVC building template in the market, the PVC building template provided by the invention has higher hardness and elasticity modulus, good shock strength, heat resistance, weather fastness and acid and alkali corrosion resistance and favorable stability, is free of deformation and warping, light in self-weight and convenient to construct, has favorable secondary fabricability, high repeating utilization ratio and long service life, and is worth popularizing since a product can be recycled and reused.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a PVC building template and a preparation method thereof. Background technique [0002] The building formwork is a temporary support structure, which is manufactured according to the design requirements, so that the concrete structure and components are formed according to the specified position and geometric size, maintain their correct position, and bear the self-weight of the building formwork and the external load acting on it. The purpose of formwork engineering is to ensure the quality of concrete engineering and construction safety, speed up the construction progress and reduce engineering costs. At present, the types of building formwork used in my country's construction industry mainly include wooden building formwork, tempered building formwork, building wood plywood, steel and bamboo building formwork, plastic building formwork, etc. Among them, plastic bui...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/28C08L97/02C08K13/06C08K9/04C08K3/26C08K3/34C08K3/22C08K3/38
CPCC08L27/06C08K2003/2227C08K2003/265C08K2003/387C08K2201/014C08L2201/02C08L2201/08C08L2205/025C08L2205/035C08L2205/16C08L23/286C08L97/02C08K13/06C08K9/04C08K3/26C08K3/34C08K3/22C08K3/38C08K3/346
Inventor 李和兵
Owner 六安三创建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap