High-strength quick-drying water-resistant adhesive and preparation method thereof

An adhesive and high-strength technology, applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of reduced work efficiency, low adhesive performance, time-consuming and labor-intensive, etc., to improve work efficiency, Protective performance, the effect of simple steps

Inactive Publication Date: 2017-09-15
JIANGSU FENGMANG COMPOUND MATERIAL SCI&TECH GRP CO LTD
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Adhesives are an indispensable part of industrial manufacturing. Adhesives in the prior art require a lot of manual input to dry or use a dryer to dry, which is time-consuming and laborious, greatly reducing work efficiency, and the performance of existing adhesives is relatively low. Low, easy to damage when encountering moisture or water, increasing the scrap rate of equipment, in order to improve work efficiency, reduce production costs, save time and effort, the present invention proposes a high-strength quick-drying waterproof adhesive and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] This embodiment provides a high-strength quick-drying waterproof adhesive. The adhesive is composed of three components A, B, and C in a ratio of A:B=1:2:5. A, B, and C include the following components in parts by mass:

[0032] Component A includes the following components in parts by mass: polyarylether sulfone ketone modified resin: 19 parts, silicon carbide micropowder: 8 parts, fluorinated graphite: 4 parts, amino silicon emulsion: 17 parts, perfluoroacrylic acid Emulsion: 10 parts, diisocyanate: 15 parts, base emulsion: 18 parts, deionized water: 25 parts, antifungal agent: 8 parts, anti-flash rust agent: 14 parts, leveling agent: 18 parts, thickener : 10 copies;

[0033] Component B includes the following components in parts by mass: epoxy resin: 13 parts, water glass: 8 parts, sodium fluorosilicate: 9 parts, graphite powder: 8 parts, filler: 17 parts, antioxidant: 14 parts, nano silica: 21 parts, curing agent: 10 parts, coupling agent: 7 parts, flame retardant:...

Embodiment 2

[0045] This embodiment provides a high-strength quick-drying waterproof adhesive. The adhesive is composed of three components A, B, and C in a ratio of A:B=1:2:5. A, B, and C include the following components in parts by mass:

[0046] Component A includes the following components in parts by mass: polyarylether sulfone ketone modified resin: 22 parts, silicon carbide micropowder: 13 parts, fluorinated graphite: 9 parts, amino silicon emulsion: 22 parts, perfluoroacrylic acid Emulsion: 12 parts, diisocyanate: 19 parts, base emulsion: 21 parts, deionized water: 30 parts, antifungal agent: 13 parts, anti-flash rust agent: 19 parts, leveling agent: 26 parts, thickener : 18 copies;

[0047] Component B includes the following components in parts by mass: epoxy resin: 17 parts, water glass: 13 parts, sodium fluorosilicate: 14 parts, graphite powder: 14 parts, filler: 20 parts, antioxidant: 19 parts, nano silica: 26 parts, curing agent: 16 parts, coupling agent: 10 parts, flame reta...

Embodiment 3

[0059] This embodiment provides a high-strength quick-drying waterproof adhesive. The adhesive is composed of three components A, B, and C in a ratio of A:B=1:2:5. A, B, and C include the following components in parts by mass:

[0060] Component A includes the following components in parts by mass: polyarylether sulfone ketone modified resin: 20 parts, silicon carbide micropowder: 11 parts, fluorinated graphite: 6 parts, amino silicon emulsion: 21 parts, perfluoroacrylic acid Emulsion: 11 parts, diisocyanate: 16 parts, base emulsion: 19 parts, deionized water: 27 parts, antifungal agent: 12 parts, anti-flash rust agent: 15 parts, leveling agent: 22 parts, thickener : 16 copies;

[0061] Component B includes the following components in parts by mass: epoxy resin: 15 parts, water glass: 11 parts, sodium fluorosilicate: 12 parts, graphite powder: 12 parts, filler: 18 parts, antioxidant: 15 parts, nano silica: 24 parts, curing agent: 14 parts, coupling agent: 9 parts, flame retar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-strength quick-drying water-resistant adhesive, which is prepared from the following components in parts by weight: 19-22 parts of poly (aryl ether sulfone ketone) modified resin, 8-13 parts of silicon carbide micro powder, 4-9 parts of carbon monofluoride, 17-22 parts of an amino-functional silicone emulsion,10-12 parts of a perfluoro acrylic emulsion, 15-19 parts of diisocyanate, 18-21 parts of base latex, 25-30 parts of deionized water, 8-13 parts of a mould inhibitor, 14-19 parts of a flash rust remover, 18-26 parts of a flatting agent, 10-18 parts of a thickener, 13-17 parts of epoxy resin, 8-13 parts of water glass, 9-14 parts of sodium fluosilicate, 8-14 parts of graphite powder, 17-20 parts of a filler, 14-19 parts of an antioxidant, 21-26 parts of nano-silica, 10-16 parts of a curing agent, 7-10 parts of a coupling agent, 3-9 parts of a fire retardant, 17-26 parts of sodium fluosilicate, 9-14 parts of graphite powder, 15-19 parts of wood fiber powder, 2-9 parts of carbon fiber powder, 12-19 parts of an antifoaming agent, 4-9 parts of a fire retardant, 1-3 parts of a catalyst, 10-14 parts of a catalyst catcher and 3-9 parts of a micromolecule chain extender.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a high-strength quick-drying waterproof adhesive and a preparation method thereof. Background technique [0002] Adhesives are an indispensable part of industrial manufacturing. Adhesives in the prior art require a lot of manual input to dry or use a dryer to dry, which is time-consuming and laborious, greatly reducing work efficiency, and the performance of existing adhesives is relatively low. Low, easy to damage when encountering moisture or water, increasing the scrap rate of equipment, in order to improve work efficiency, reduce production costs, save time and effort, the present invention proposes a high-strength quick-drying waterproof adhesive and its preparation method. Contents of the invention [0003] The technical problem to be solved by the present invention is to propose a high-strength quick-drying waterproof adhesive and its preparation method in view of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/04C09J11/04C09J11/06C09J11/08
CPCC09J175/04C08K2201/011C08K2201/014C08L2205/035C08L2205/16C09J11/04C09J11/06C09J11/08C08L97/02C08K13/06C08K7/06C08K3/04C08K3/34C08K3/36
Inventor 王荣生
Owner JIANGSU FENGMANG COMPOUND MATERIAL SCI&TECH GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap