Preparation method of acid-doped pyrrole-m-toluidine copolymer and modified anticorrosion coating

A technology of anti-corrosion coating and toluidine, which is applied in the field of material engineering, can solve the problems of poor anti-corrosion performance, poor thermal stability and chemical stability, etc., and achieve the effect of good anti-corrosion performance, good corrosion resistance and good coating binding force

Active Publication Date: 2020-05-01
SICHUAN UNIVERSITY OF SCIENCE AND ENGINEERING
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For the above-mentioned deficiencies that exist in the prior art, the purpose of the present invention is to provide a kind of preparation method of acid-doped pyrrole-m-toluidine copolymer, and with described pyrrole-m-toluidine copolymer modified epoxy resin, solve the present problem There are problems of poor anticorrosion performance, poor thermal stability and chemical stability of polypyrrole anticorrosion coatings; the application of the modified anticorrosion coatings is also provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of acid-doped pyrrole-m-toluidine copolymer and modified anticorrosion coating
  • Preparation method of acid-doped pyrrole-m-toluidine copolymer and modified anticorrosion coating
  • Preparation method of acid-doped pyrrole-m-toluidine copolymer and modified anticorrosion coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Paint preparation:

[0025] Take 10g epoxy resin in beaker with electronic balance; Add 1-methyl-2-pyrrolidone (diluent) of 1g in epoxy resin and stir with glass rod; Add 0.6g ethylenediamine (curing agent) in beaker ), and stir evenly to obtain pure epoxy resin coating. And then evenly coated on Q235 carbon steel.

Embodiment 2

[0027] 1. Preparation of polypyrrole:

[0028] ① Weigh ammonium persulfate and deionized water to make 0.4M ammonium persulfate solution, set aside;

[0029] ②Pyrrole monomer and m-toluidine monomer are added dropwise into a clean beaker at a volume ratio of 1:0 (1=0.5ml);

[0030] ③Add 10ml of 0.5M citric acid to the beaker in step ②, then put it into an ultrasonic cleaner and shake for 5-8 minutes, so that there is a layer of white transparent oil on the surface;

[0031] ④ Take out the beaker of step ③ and slowly add 5ml of the ammonium persulfate solution prepared in step ①, and shake the beaker while adding, the reaction is rapid, and the color of the solution gradually changes from colorless and transparent to purple red and finally to purple black;

[0032] ⑤ Seal the beaker with plastic wrap, place it at room temperature, and let it stand for 20-24 hours;

[0033] ⑥ Cross-wash with deionized water and absolute ethanol, and perform suction filtration while washing to ...

Embodiment 3

[0041] 1. Preparation of acid-doped pyrrole-m-toluidine copolymer:

[0042] ① Weigh ammonium persulfate and deionized water to make 0.4M ammonium persulfate solution, set aside;

[0043] ② Add dropwise monomers and m-toluidine monomers into a clean beaker at a volume ratio of 1:1 (1=0.5ml);

[0044] ③Add 10ml of 0.5M citric acid to the beaker in step ②, then put it into an ultrasonic cleaner and shake it for 5-8 minutes, so that there is a layer of white transparent oil on the surface;

[0045] ④ Take out the beaker of step ③ and slowly add 5ml of the ammonium persulfate solution prepared in step ①, and shake the beaker while adding, the reaction is rapid, and the color of the solution gradually changes from colorless and transparent to purple red and finally to purple black;

[0046] ⑤ Seal the beaker with plastic wrap, place it at room temperature, and let it stand for 20-24 hours;

[0047] 6. Cross-wash with deionized water and absolute ethanol, and carry out suction filt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides preparation methods of an acid-doped pyrrole-m-toluidine copolymer and a modified anticorrosive coating. An acid-doped pyrrole-m-toluidine copolymer material is prepared by a chemical oxidative polymerization method, E-44 epoxy resin is modified with the pyrrole-m-toluidine copolymer material, the acid-doped pyrrole-m-toluidine copolymer material is added in the epoxy resin, Q235 carbon steel is coated with the modified epoxy resin, and the anticorrosive performance of the coated Q235 carbon steel is studied. When the volume ratio of pyrrole and m-toluidine is 2 to 1, the synthesized copolymer, as filler, is added in the epoxy resin to be used as a coating, and a coating layer of the coating is largest in resistance and smallest in corrosion current density, i.e. the corrosion resistance performance of the coating is the best. By passing through binding force rating, the coating can reach a primary standard and has very good constructability. The coating has dual advantages of polypyrrole and the m-toluidine and is very good in conductivity, good in anticorrosive performance, small in pollution and low in cost.

Description

technical field [0001] The invention relates to an anti-corrosion coating, in particular to a preparation method and application of an acid-doped pyrrole-m-toluidine copolymer modified anti-corrosion coating, which belongs to the field of material engineering. Background technique [0002] Metal corrosion will cause huge losses, but no matter now or in the future, metal materials occupy an important position in the field of materials with their excellent mechanical and technological properties. Therefore, research on metal corrosion protection methods to control metal corrosion and reduce corrosion losses, It is of great significance to the development of the national economy. The most commonly used method is to coat the metal surface with an anti-corrosion coating to isolate the corrosive medium from contacting the metal substrate. With the development of construction, transportation, petrochemical, electric power and other industries, the market size of anti-corrosion coa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G73/06C09D163/00C09D179/04C09D5/08
CPCC08G73/0611C08L2201/08C09D5/08C09D5/18C09D163/00C08L79/04
Inventor 王红林果邹彦昭张颖君杨瑞嵩雷英
Owner SICHUAN UNIVERSITY OF SCIENCE AND ENGINEERING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com