Production formula and preparation method for elastic rotator

A production formula and technology of rotating body, applied in the field of production formula and preparation of elastic rotating body, can solve the problems of easy cracking, poor anti-aging performance, short service time, etc., achieve not easy cracking, good anti-aging performance, and prolong service life Effect

Active Publication Date: 2017-10-20
江苏恪铭智慧交通科技有限公司
View PDF10 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problem that the existing elastic rotating body has poor anti-aging performance and is easy to crack, so that the use time is short, the invention provides a production formula and preparation method of the elastic rotating body, which ensures that the elastic rotating body has good anti-aging performance. It is not easy to crack under force, which effectively prolongs the service life of the elastic rotating body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production formula and preparation method for elastic rotator

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The preparation method of the elastic rotating body of the present invention is carried out according to the following specific steps:

[0037](1) Internal mixing: POE, EPDM rubber, anti-shrinkage agent, filler, EVA, stearic acid, zinc stearate, zinc oxide, crosslinking agent, foaming agent, flow agent, masterbatch pigment Add it into the internal mixer for mixing and stirring, then put the stirred material into the internal mixer for 8 to 12 minutes at a temperature of 80-100°C, put it into the open mixer for uniform tableting, and then granulate. Among them, the kneading temperature is controlled within the range of 45-65°C, the kneading time is controlled within the range of 5-8 minutes, and the granulation temperature is controlled within the range of 80-100°C;

[0038] (2) Plasticizing processing: input the above granulated materials into the barrel of the injection machine for plasticizing processing, and the temperature is controlled within the range of 70-100°C;...

Embodiment 1

[0046] A production recipe of an elastic rotating body of the present invention, calculated by weight, includes the following specific components: ethylene-octene copolymer (POE) 15%, EVA 50%, EPDM rubber 15%, anti-shrinkage agent E20 -58 7.5%, talcum powder with particle size ≤200nm 2%, stearic acid 0.3%, zinc stearate 0.7%, zinc oxide 1.5%, dicumyl peroxide DCP 1%, azodicarbonamide AC Foaming agent 2%, fatty acid ester 2%, masterbatch pigment 3%, the total weight is 100%.

[0047] Such as figure 1 Shown, the preparation method of a kind of elastic rotating body of the present invention is carried out according to the following specific steps:

[0048] (1) Internal mixing: POE, EPDM rubber, EVA, anti-shrinkage agent E20-58, talcum powder, stearic acid, zinc stearate, zinc oxide, dicumyl peroxide DCP, azobis Add formamide AC foaming agent, fatty acid ester, and masterbatch into the internal mixer for mixing and stirring, and then mix the stirred materials with the internal m...

Embodiment 2

[0053] A production formula of an elastic rotating body of the present invention, calculated by weight, includes the following specific components: ethylene-octene copolymer (POE) 10%, EVA 60%, EPDM rubber 10%, anti-shrinkage agent E20 -58 5%, 2% talc powder with particle size ≤ 200nm, 1% calcium carbonate with particle size ≤ 200nm, 0.5% stearic acid, 1% calcium stearate, 2% zinc oxide, dicumyl peroxide DCP 0.7%, azodicarbonamide AC blowing agent 1.8%, fatty acid ester 2%, masterbatch pigment 4%, the total weight is 100%.

[0054] A kind of preparation method of elastic rotating body of the present invention is carried out according to the following specific steps:

[0055] (1) Internal mixing: POE, EPDM rubber, anti-shrinkage agent, talcum powder, calcium carbonate, EVA, stearic acid, calcium stearate, zinc oxide, dicumyl peroxide DCP, azobis Add the formamide AC foaming agent, fatty acid ester, and masterbatch into the internal mixer for mixing and stirring, and then mix t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a production formula and a preparation method for an elastic rotator, which belong to the technical field of road transportation equipment. The formula comprises the following specific components: 10 to 20 percent of ethylene-octene copolymer (POE), 40 to 60 percent of EVA (ethylene-vinyl acetate copolymer), 10 to 20 percent of ethylene-propylene-diene monomer, 5 to 10 percent of anti-shrinking agent, 1 to 3 percent of filler, 0.6 to 1.6 percent of dispersed lubricant, 1 to 2 percent of zinc oxide, 0.7 to 1.2 percent of cross-linking agent, 1.5 to 2.5 percent of foaming agent, 1.5 to 2.5 percent of flowable agent and 2 to 4 percent of color masterbatch pigment, and the total weight is 100 percent. The POE, the ethylene-propylene-diene monomer and the EVA are mixed and refined, and are added with a variety of additives, so that the three types of materials keep respective properties and complement one another, the elasticity of the prepared elastic rotator is high, moreover, after foaming, the texture is dense, the weight is light, the good anti-aging property of the elastic rotator is ensured, the elastic rotator cannot be easily cracked when receiving impact force, and the service life of the elastic rotator is effectively prolonged.

Description

technical field [0001] The invention belongs to the technical field of road traffic equipment, and more specifically relates to a production formula and a preparation method of an elastic rotating body. Background technique [0002] With the rapid development of economy, automobiles are widely used as a convenient means of transportation. In my country, the speed limit of different roads is also different. For example, the general speed limit of urban roads is 40 kilometers per hour, the general speed of ordinary roads is 40-80 kilometers per hour, and the general speed limit of expressways is 60-120 kilometers per hour. Therefore, traffic accidents in urban areas are mostly rear-end collision accidents. On ordinary roads or expressways, traffic accidents occur frequently due to excessive speed of vehicles. On the guardrail, and these guardrails are made of concrete bricks or concrete blocks arranged at intervals and cross rails connecting adjacent blocks, or are composed of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/16C08K13/02C08K5/14C08K3/34C08K3/36C08K3/26C08J9/10B29B7/00B29C44/42B29C44/60
CPCB29B7/002B29C44/42B29C44/60C08J9/103C08J2203/04C08J2323/08C08J2423/08C08J2423/16C08K2003/265C08K2201/005C08L23/0853C08L2201/08C08L2203/14C08L2205/035C08L23/0815C08L23/16C08K13/02C08K5/14C08K3/34C08K3/26C08K3/36
Inventor 许运动
Owner 江苏恪铭智慧交通科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap