Preparation method of sports carpet

A carpet and sports technology, which is applied in the field of sports carpet preparation, can solve the problems of easy corrosion, variability, and difficult dehumidification, and achieve the effect of meeting sports requirements, good elasticity, and not easy to pollute

Inactive Publication Date: 2017-11-21
江苏攸途健身器材有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the common carpets in the market are made of fiber floor materials. Generally, the surface of floor materials is smooth. If dirt enters the carpet, it cannot be cleaned.
Ordinary carpets are poor in elasticity, changeable, susceptible to corrosion, insects and difficult to dehumidify, so they cannot meet the requirements of sports venues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A preparation method of a sports carpet, the sports carpet is composed of the following components in parts by weight: 60 parts of styrene-butadiene rubber, 0.6 parts of stearic acid, 40 parts of N-220 black smoke powder, 40 parts of EPDM rubber powder, 6 parts of naphthenic oil part, 1 part of phenolic resin, 0.1 part of TMTD accelerator and 8 parts of water-absorbing agent; Wherein, described water-absorbing agent is the mixture of activated carbon and anhydrous calcium chloride, and the mass ratio of activated carbon and anhydrous calcium chloride is 1.9:1 ; The preparation method comprises the steps of:

[0014] (1) Mix styrene-butadiene rubber, stearic acid, N-220 black smoke powder, EPDM rubber powder and naphthenic oil evenly;

[0015] (2) Add the weighed phenolic resin, TMTD accelerator and water-absorbing agent to the mixture in step (1), stir for 3-5 minutes until uniform, put it into a mold, and heat it at 180-200°C. The time is 2min;

[0016] (3) After hea...

Embodiment 2

[0018] A preparation method of a sports carpet, the sports carpet is composed of the following components in parts by weight: 60 parts of styrene-butadiene rubber, 0.6 parts of stearic acid, 40 parts of N-220 black smoke powder, 40 parts of EPDM rubber powder, 6 parts of naphthenic oil part, 1 part of phenolic resin, 0.1 part of TMTD accelerator and 8 parts of water-absorbing agent; Wherein, described water-absorbing agent is the mixture of activated carbon and anhydrous calcium chloride, and the mass ratio of activated carbon and anhydrous calcium chloride is 2.3:1 ; The preparation method comprises the steps of:

[0019] (1) Mix styrene-butadiene rubber, stearic acid, N-220 black smoke powder, EPDM rubber powder and naphthenic oil evenly;

[0020] (2) Add the weighed phenolic resin, TMTD accelerator and water-absorbing agent to the mixture in step (1), stir for 3-5 minutes until uniform, put it into a mold, and heat it at 180-200°C. The time is 2min;

[0021] (3) After hea...

Embodiment 3

[0023] A preparation method of a sports carpet, the sports carpet is composed of the following components in parts by weight: 60 parts of styrene-butadiene rubber, 0.6 parts of stearic acid, 40 parts of N-220 black smoke powder, 40 parts of EPDM rubber powder, 6 parts of naphthenic oil part, 1 part of phenolic resin, 0.1 part of TMTD accelerator and 8 parts of water-absorbing agent; Wherein, described water-absorbing agent is the mixture of activated carbon and anhydrous calcium chloride, and the mass ratio of activated carbon and anhydrous calcium chloride is 2.1:1 ; The preparation method comprises the steps of:

[0024] (1) Mix styrene-butadiene rubber, stearic acid, N-220 black smoke powder, EPDM rubber powder and naphthenic oil evenly;

[0025] (2) Add the weighed phenolic resin, TMTD accelerator and water-absorbing agent to the mixture in step (1), stir for 3-5 minutes until uniform, put it into a mold, and heat it at 180-200°C. The time is 2min;

[0026] (3) After hea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a sports carpet, which is prepared from, by weight, 60-80 parts of butadiene styrene rubber, 0.6-0.8 part of stearic acid, 40-50 parts of N-220 chokedamp powder, 40-50 parts of EPDM rubber powder, 6-10 parts of naphthenic oil, 1-3 parts of phenolic resin, 0.1-0.3 part of TMTD accelerant, 8-10 parts of water absorbent, wherein the water absorbent is mixture of active carbon and anhydrous calcium chloride, and the mass ratio of the active carbon and anhydrous calcium chloride is 1.9-2.3: 1. The preparation method has the advantages that the sports carpet prepared by the formula is not easy to pollute, deform and wear, easy to remove humidity and good in heat insulation property; the sports carpet is suitable for treading by intensive crowd, and good in elasticity; therefore, the sports carpet can meet the sports requirement.

Description

technical field [0001] The invention belongs to the field of sporting goods, in particular to a preparation method of a sports carpet. Background technique [0002] The carpets that are ubiquitous in the market are made of fiber floor materials, and the surface of the general floor materials is smooth. If dirt enters the carpet, it cannot be cleaned. Ordinary carpets are poor in elasticity, changeable, susceptible to corrosion, insects and difficult to dehumidify, so they cannot meet the requirements of sports venues. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a sports carpet that is wear-resistant and easy to dehumidify. [0004] In order to solve the above-mentioned technical problems, the technical solution of the present invention is: a preparation method of a sports carpet. ~0.8 parts, N-220 black smoke powder 40~50 parts, EPDM rubber powder 40~50 parts, naphthenic oil 6~10 parts, phenolic resin 1~3 p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/06C08L23/16C08L91/00C08L61/06C08K5/09C08K3/04C08K3/16
CPCC08L9/06C08K2003/162C08L2205/035
Inventor 顾丽
Owner 江苏攸途健身器材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com