Glass fiber-reinforced bi-component pultruded polyurethane material and application thereof in magnetic steel batten of direct-driven permanent magnetic synchronous wind turbine

A two-component polyurethane and polyurethane material technology, applied in wind power generation, magnetic circuits characterized by magnetic materials, etc., can solve the problems of different fixing effects of magnetic steel and easy falling off of magnetic steel, so as to achieve difficult delamination and peeling, Not easy to mechanical damage, not easy to be stained with oil

Pending Publication Date: 2017-11-24
南京经略复合材料有限公司
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to current, temperature, vibration and other reasons, the magnetic steel is easy to fall off. In the prior art, the bead is generally used to fix the magnetic steel, but the material of the bead produced and processed is different, and the fixing effect on the magnetic steel is also different.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber-reinforced bi-component pultruded polyurethane material and application thereof in magnetic steel batten of direct-driven permanent magnetic synchronous wind turbine
  • Glass fiber-reinforced bi-component pultruded polyurethane material and application thereof in magnetic steel batten of direct-driven permanent magnetic synchronous wind turbine
  • Glass fiber-reinforced bi-component pultruded polyurethane material and application thereof in magnetic steel batten of direct-driven permanent magnetic synchronous wind turbine

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be further described below in conjunction with the examples.

[0019] In the present invention, each component and source are respectively:

[0020] The two-component polyurethane resin is selected from: two-component polyurethane resin SK 97007, purchased from Huntsman Chemical R&D Center (Shanghai) Co., Ltd.; or two-component polyurethane resin CC6226 / 101C-A, purchased from BASF Polyurethane Specialty Products (China ) Ltd. The same type of domestic two-component polyurethane resin can also be used.

[0021] Two-component polyurethane resin special flame retardants are selected from: reactive flame retardant Flame Check X6667, additive flame retardant Flame Check 2725, additive flame retardant Flame Check 2750, all purchased from American Reves Corporation.

[0022] A batch of glass fiber-reinforced two-component polyurethane material was prepared, and the formula was as follows:

[0023]

[0024] Its preparation method includes the fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a glass fiber-reinforced bi-component pultruded polyurethane resin material which is at least prepared from the following components: alkali-free glass fiber yarn, glass fiber fabrics, bi-component polyurethane resin, a special flame retardant agent for bi-component polyurethane resin and color paste. The polyurethane material is rich in source of raw materials and low in preparation cost; a magnetic steel batten of a direct-driven permanent magnetic synchronous wind turbine prepared from the polyurethane material is flat and smooth in surface, free of bubbles and exposed fibers, unlikely to be contaminated by oil, uniform in surface color, and unlikely to have cracks, delaminate and produce mechanical scars.

Description

technical field [0001] The invention belongs to the field of power generation equipment, in particular to a glass fiber-reinforced two-component pultruded polyurethane material, and also relates to the application of the material to the magnetic steel layer of a direct-drive permanent magnet synchronous wind power generator. Background technique [0002] In nature, wind energy is a renewable, non-polluting, and clean energy with huge reserves, which has attracted widespread attention from all over the world. The development and utilization of wind energy, especially the vigorous development of wind power, has accelerated the research and development of wind turbines. In recent years, according to the official report of the Global Wind Energy Council, the installed capacity of wind turbines in various countries has continued to rise, and its proportion in the power grids of various countries is also increasing. Therefore, ensuring the safe and stable operation of wind turbin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08K13/04C08K7/14C08J5/04H02K1/02
CPCH02K1/02C08J5/043C08J5/047C08K7/14C08K13/04C08J2375/04C08K2201/014C08L2201/02C08L2203/20C08L75/04Y02E10/72
Inventor 王小平赵启林李飞钱易强曲全亮
Owner 南京经略复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap